Punched nickel-plated steel strip and its manufacturing method
A manufacturing method and technology of nickel-plated steel, applied in the direction of alkaline battery electrodes, etc., can solve the problems of difficult control of burr length, difficult mold design, difficult control of burr, etc., and achieve easy control of process flow and parameters, adhesion and conductivity. The effect of improving the properties and electrochemical performance, and increasing the effective specific surface area
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022] Example 1: The ordinary perforated steel strip is electroplated in a mixed solution containing 1.5 mol / l nickel sulfate, 0.1 mol / l nickel chloride, and 0.65 mol / l boric acid for 1.5 minutes, the pH value of the plating solution is 4.5, and the temperature is 50°C , The cathode plating density is 3A / dm 2 , The pre-nickel-plated steel strip is obtained, and the deposition thickness of the pre-nickel layer is 0.5-1 micron. Put this pre-plated nickel steel strip into the second nickel plating bath for electroplating. The composition and process conditions of the plating solution are as follows: nickel sulfate 1mol / l, nickel chloride 0.15mol / l, boric acid 0.65mol / l, and additives 20ml / l, the nickel powder with a diameter of 1 micron floats evenly in the solution under stirring and the added amount is 5g / L, electroplating 1min, the pH value of the plating solution is 4.5, the temperature is 50℃, and the cathode current density is 3A / dm 2 The resulting coating is a matt composite...
Example Embodiment
[0023] Example 2: The composition of the nickel electroplating solution for pre-plating nickel on ordinary perforated steel strips is nickel sulfate 1.5mol / l, nickel chloride 0.1mol / l, 0.65mol / l boric acid, additive 20ml / l mixed solution, plating time 2.5min , The pH value of the plating solution is 4.8, the temperature is 52℃, and the cathode plating density is 3A / dm 2 , The deposition thickness of the pre-plated nickel layer is 2 to 3 microns. The composition and process conditions of the composite nickel electroplating solution are: nickel sulfate 1.5mol / l, nickel chloride 0.12mol / l, boric acid 0.65mol / l, additive 4ml / l, and carbonyl nickel powder with a diameter of 3 microns floats uniformly under stirring. In the solution and the adding amount is 100g / L, the electroplating is 4min, the pH of the plating solution is 4.8, the temperature is 50℃, and the cathodic plating density is 3A / dm 2 , The deposition thickness of the composite electroplating nickel layer is 4.5~5 microns. ...
Example Embodiment
[0024] Example 3: The composition of the nickel electroplating solution for pre-plating nickel on ordinary perforated steel strip is nickel sulfate 1.5 mol / l, nickel chloride 0.1 mol / l, 0.65 mol / l boric acid, plating time 1 min, plating solution pH value 4.8, temperature It is 52℃, the cathode plating density is 3A / dm 2, The deposition thickness of the pre-plated nickel layer is 0.5-0.9 microns. The composition and process conditions of the composite nickel electroplating solution are: nickel sulfate 1.5mol / l, nickel chloride 0.12mol / l, boric acid 0.65mol / l, additive 4ml / l, 5 micron diameter cobalt trioxide powder uniformly under stirring The ground floats in the solution and the adding amount is 150g / L, the plating is 8min, the pH value of the plating solution is 4.8, the temperature is 50℃, and the cathode plating density is 3A / dm 2 The deposition thickness of the composite electroplating nickel layer is 7~8 microns. The resulting coating is a matt nickel coating. From the scann...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Deposition thickness | aaaaa | aaaaa |
Deposition thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap