Fibre structure of carbon nano tube/nano oxide nano composite material and preparation method and use thereof

A technology of nanocomposite materials and composite fiber, which is applied in the fields of botanical equipment and methods, heat exchange materials, chemical instruments and methods, etc., which can solve the problems of difficult application, difficulty in fixing and separating nanoparticles, and easy aggregation of nanoparticles sexual issues

Inactive Publication Date: 2008-03-12
INST OF CHEM CHINESE ACAD OF SCI
View PDF1 Cites 76 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the large-scale application of carbon nanotube/nano-oxide hybrid materials still has great obstacles to overcome: firstly, these extremely small nanoparticles are very easy to agglomerate and it is difficult to show their superiority, so how to disperse these nanoparticles well is a very important problem; in addition, d

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fibre structure of carbon nano tube/nano oxide nano composite material and preparation method and use thereof
  • Fibre structure of carbon nano tube/nano oxide nano composite material and preparation method and use thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056]15 parts by weight of carbon nanotubes (diameter 10-20nm, length 1-10μm) are dispersed in 100 parts by weight of ethanol by ultrasound, then 100 parts by weight of n-butyl titanate are added, and after mixing, 150 parts by weight of nano oxides are added to form As auxiliary agent acetic acid, after magnetically stirring for 0.5 h, the dispersion was mixed with 100 parts by weight of ethanol solution in which 30 parts by weight of polyvinylpyrrolidone was dissolved, and mixed uniformly after magnetically stirring for 1 hour to obtain a dispersion. Then the dispersion is contained in the liquid storage tank of the metering pump, and the resulting fiber (polyvinylpyrrolidone / carbon nanotube / titanium dioxide precursor) is collected at a sample injection rate of 1mL / h under the condition of an electric field strength of 1kV / cm on a grounded aluminum foil collector plate. Then, the polyvinylpyrrolidone is removed by calcining at 300-800° C. for 1 h, and finally a carbon nanot...

Embodiment 2

[0058] 10 parts by weight of fluorinated single-walled carbon nanotubes (diameter 1-2nm, length 0.5-5μm) are dispersed in 100 parts by weight of water by ultrasound, then 50 parts by weight of isopropyl titanate are added, and 10 parts by weight of nanometer Hydrochloric acid as an auxiliary agent for oxide formation, after magnetic stirring for 1 hour, the dispersion was mixed with 100 parts by weight of ethanol solution in which 30 parts by weight of polyvinyl acetate was dissolved, and after magnetic stirring for 1 hour, the mixture was uniformly mixed to obtain a dispersion. Then the dispersion is contained in the liquid storage tank of the metering pump, with a sample injection speed of 1mL / h, under the condition of an electric field strength of 3kV / cm, the obtained fiber (polyvinyl acetate / carbon nanotube / titanium dioxide precursor) Collect on a grounded aluminum foil collection plate. Then, polyvinyl acetate / carbon nanotubes / titanium dioxide hybrid nanofibers were obtai...

Embodiment 3

[0060] 10 parts by weight of a mixture of single-walled carbon nanotubes and multi-walled carbon nanotubes (1 to 20 nm in diameter and 1 to 15 μm in length) are dispersed in 100 parts by weight of ethanol by ultrasonic waves, then 50 parts by weight of zirconium acetate are added, and stirred under magnetic conditions for 0.5 h Finally, the dispersion was mixed with 100 parts by weight of ethanol solution in which 20 parts by weight of polyvinyl alcohol was dissolved, stirred magnetically for 10 hours, and mixed uniformly to obtain a dispersion. Then the dispersion is contained in the liquid storage tank of the metering pump, with the sample injection speed of 5mL / h, under the condition of electric field strength 2kV / cm, the fiber (polyvinyl alcohol / carbon nanotube / zirconia) that obtains is collected in Ground the aluminum foil collection plate. Then, polyvinyl alcohol was removed by calcination at 600° C. for 1 h, and finally a carbon nanotube / zirconia hybrid nanofiber membra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a fiber structure of nanometer composite material of carbon nanometer pipe/nanometer oxide or polymer/carbon nanometer pipe/nanometer oxide. Disperse the front drive body of the carbon nanometer pipe and nanometer oxide into a polymer solution, so as to obtain a dispersion liquid; then, perform electric filature to obtain a polymer/carbon nanometer pipe/nanometer oxide with a front drive body of nanometer fiber structure. The front drive body of the nanometer oxide can be converted into a nanometer oxide with such methods as hydrothermal process, high-temperature process or microwave process and etc. The polymer can be kept or eliminated through such methods as high-temperature process or solvent fractionating and etc, in order to obtain the nanometer fiber of carbon nanometer pipe/nanometer oxide. The fiber composed of the composite material fiber structure, or films made of the fiber can be utilized in the fields of sewage process, air purification, solar energy battery and antibiotic material and etc.

Description

technical field [0001] The invention belongs to the nanocomposite field of carbon nanotube / nano oxide, in particular to carbon nanotube / nano oxide, or the fiber structure of the nanocomposite material of polymer / carbon nanotube / nano oxide, and by this fiber The film (non-woven fabric) constituted, and the preparation method and application of the fiber structure of the nanocomposite material. Background technique [0002] Carbon Nanotubes, also known as carbon nanotubes, carbon nanotubes, carbon nanotubes, fuller tubes, carbon nanotubes, carbon nanotubes, carbon nanotubes, carbon nanotubes or bucky tubes, etc. , is a quasi-one-dimensional material with a special structure. Carbon nanotubes can be divided into single-walled carbon nanotubes (SWNT) and multi-walled carbon nanotubes (MWNT) according to the number of graphite-like layers constituting the tube wall. The production methods of carbon nanotubes are divided into arc discharge, laser ablation, and chemical vapor dep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F1/10D01F6/92D01F6/90D01F6/46D01F6/44D01F6/52D01F6/54C01B31/02D04H13/00C02F1/00C09K3/16C09K5/00A61L9/00H01L31/00B01D69/00A01N25/00
CPCY02A20/212Y02W10/37
Inventor 阳明书胡广君张世民孟祥福封喜彦丁艳芬张军华胡晓
Owner INST OF CHEM CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap