Multiple crosslinking ultraviolet light solidifying water polyurethane dispersoid and its preparation method and application
A water-based polyurethane and multiple cross-linking technology, applied in polyurea/polyurethane coatings, coatings, etc., can solve product safety and health and long-term adverse effects on performance, active diluents increase coating film shrinkage, environmental and human harmful organic Solve problems such as volatile matter, achieve the effect of mature and stable production process, good molecular structure, and increase hardness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0051] The multi-crosslinking UV-curable waterborne polyurethane wood coating was prepared according to the following steps.
[0052] Prepare raw materials: Prepare materials according to the formula in Table 1.
[0053] Table 1
[0054] type
raw material
Dosage (% by weight)
Water-based poly
Urethane
bulk
Toluene diisocyanate
30.0
Polyether N210
35.9
1,4-Butanediol
5.0
Trimethylolpropane
1.0
Glycerin
0.5
N-Methylalcohol
5.0
Acetone
35.0
[0055] Epoxy resin E-51
3.4
2,2-Dimethylolpropionic acid
7.0
Hydroxyethyl methacrylate
11.6
Triethylamine
5.0
Ethylenediamine
0.6
water
150.0
paint
Irgacure369
5.5
W461
4
TEGO-245
0.5
TEGO-800
1
1,2-propanediol
12
...
Embodiment 2
[0065] Raw materials were prepared according to the ratio in Table 2 below, and then the same steps as in Example 1 were used to prepare multiple cross-linked UV-curable water-based polyurethane wood coatings.
[0066] Table 2
[0067] type
raw material
Dosage (% by weight)
Water-based poly
Urethane
bulk
Toluene diisocyanate
30.3
Polyether N220
35.6
1,4-Butanediol
5.2
pentaerythritol
1.3
N-Methylalcohol
10.0
Acetone
35.0
Epoxy resin E-20
3.4
2,2-Dimethylolpropionic acid
7.0
Hydroxyethyl Acrylate
11.5
Triethylamine
5.0
[0068] Ethylenediamine
0.7
water
230.0
paint
Irgacure651
10
BYK333
2
TEGO500
2
TEGO-815
1.5
ethanol
9
Rheo WT-201
2
RM-895
2 ...
Embodiment 3
[0078] Raw materials were prepared according to the ratio in Table 3 below, and then the multiple cross-linked UV-curable waterborne polyurethane wood coating was prepared according to the same steps as in Example 1.
[0079] table 3
[0080] type
raw material
Dosage (% by weight)
Water-based poly
Urethane
bulk
Toluene diisocyanate
29.3
Polyether N230
36.6
1,4-Butanediol
5.0
Glycerin
1.5
N-Methylalcohol
15.0
acetone
25.0
Epoxy resin E-44
3.4
2,2-Dimethylolpropionic acid
7.0
Hydroxypropyl Methacrylate
11.4
Triethylamine
5.0
Ethylenediamine
0.8
water
200.0
paint
Darocur907
14
W461
1
W-518
1
0506
2
ethylene glycol
6
[0081] DSX3256
...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap