Single-component waterproof coating material and method of preparing the same

A waterproof coating, single-component technology, applied in antifouling/underwater coatings, coatings, paints containing biocides, etc., can solve problems such as convulsions, damage, respiratory system irritation, etc., and achieve the effect of simple and convenient construction technology

Inactive Publication Date: 2009-01-14
SHENZHEN OCEAN POWER INDUSTRIAL CO LTD +3
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, solvent-based coatings and reactive coatings will emit volatile organic compounds (VOCs) into the atmosphere during production and construction to cause pollution. VOCs can stimulate and damage the central nervous system, hematopoietic organs, and respiratory system of the human body. Cause convulsions, coma and even death, therefore, VOC is extremely harmful to human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) The composition and dosage of one-component waterproof coating are as follows:

[0029] No. Component Weight (%) Remarks

[0030] 1 Emulsion CM-101 30 Union Carbide Corporation

[0031] 2 Dispersant Hydropalat 150 0.8 Cognis

[0032] 3 Wetting agent Hyonic PE-100 0.1 Cognis

[0033] 4 Defoamer FoamStar EF-331 0.2 Cognis

[0034] 5 Propylene Glycol 2 Technical Grade

[0035] 6 Titanium Dioxide R-215 18 Nuclear Industry 404 Factory

[0036] 7 Kaolin 1250 mesh 16

[0037] 8 wollastonite 600 mesh 6

[0038] 9 FoamStar EF-331 0.2 Cognis

[0039] 10 Preservative Alex F-251 0.2 Cognis

[0040] 11 Coalescing aid EFC-100 1 Cognis company

[0041] 12 CM-101 20 United Carbide Corporation

[0042] 13 Thickener DSX 3800 0.6 Cognis

[0043] 14 water 4.9

[0044] (2) Paint sample performance:

[0045] Viscosity: 120KU;

[0046] Surface dry time: 25 minutes.

[0047] (3) Preparation process:

[0048] Weigh the components of serial number 1-5, mix and stir;

[0049]...

Embodiment 2

[0053] (1) The composition and dosage of one-component waterproof coating are as follows:

[0054] No. Component Weight (%) Remarks

[0055] 1 Emulsion S-400 30 BASF

[0056] 2 Dispersant Hydropalat 150 0.8 Cognis

[0057] 3 Wetting agent Hyonic PE-100 0.1 Cognis

[0058] 4 Defoamer FoamStar EF-331 0.2 Cognis

[0059] 5 Propylene Glycol 2 Technical Grade

[0060] 6 Titanium Dioxide R-215 18 Nuclear Industry 404 Factory

[0061] 7 Kaolin 1250 mesh 16

[0062] 8 wollastonite 600 mesh 6

[0063] 9 FoamStar EF-331 0.2 Cognis

[0064] 10 Preservative Alex F-251 0.2 Cognis

[0065] 11 Coalescing aid EFC-100 1 Cognis company

[0066] 12 S-400 20 BASF Corporation

[0067] 13 Thickener DSX 3075 0.6 Cognis

[0068] 14 water 4.9

[0069] (2) Paint sample performance:

[0070] Viscosity: 115KU;

[0071] Surface dry time: 25 minutes.

[0072] (3) Preparation process:

[0073] Weigh the components of serial number 1-5, mix and stir;

[0074] Add components 6-8 under stirring ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
surface tensionaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses single component waterproof coating and the preparation method. 50 percent to 80 percent of emulsion, latent solvent, dispersing agent and wetting agent are mixed with 40 percent to 60 percent of anti-foaming agent and are stirred at the rotating speed of 300 rpm to 700 rpm, pigment and filler are added during the stirring process, then the dispersing operation is performed at the rotating speed of 2000 rpm to 4000 rpm, slurry with the fineness lesser 50 um is obtained, and the residual anti-foaming agent is added. After the anti-foaming operation is performed, anticorrosion agent, film forming auxiliary agent, residual emulsion, thickening agent and water are added and evenly stirred at the rotational speed of 300rpm to 700 rpm, and the single component waterproof coating is obtained. The method has the advantages that the construction technology of the coating is simple and convenient, the film-forming process is finished mainly depending on the volatilization of the water and the interfusion of the latex particles, no VOC is discharged, no organic solvent is effused, the single component waterproof coating has no environmental pollution and combustion, the construction is safe, and the coating is an environmental protective-type single component waterproof coating.

Description

technical field [0001] The invention relates to a waterproof coating, in particular to an environment-friendly single-component waterproof coating without VOC emission. [0002] The invention also relates to a preparation method of the waterproof paint. Background technique [0003] Leakage in buildings will not only damage the interior decoration and equipment of the project, but also damage the structure of the project in severe cases, making it lose its function, causing scrap and even endangering people's lives. Adopting waterproof technology to prevent water seepage and water leakage of buildings is a kind of waterproof method that has just begun to be used in the late 1950s. The waterproof coating is a viscous liquid at room temperature, and can form a seamless waterproof coating film after coating and curing. It is especially suitable for construction on detailed structures such as facades, internal and external corners, and narrow places. It has both bonding and wat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/16C09D7/12
Inventor 张艳何唯平
Owner SHENZHEN OCEAN POWER INDUSTRIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com