Capacitor coating with deep drawing resistant performance and high temperature yellowing resistance and preparation thereof

A deep-drawing performance and capacitor technology, applied in polyester coatings, coatings, etc., can solve problems such as insufficient balance of comprehensive performance

Active Publication Date: 2011-01-19
清远慧谷新材料技术有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the shortcomings of current capacitor coatings that are not sufficiently balanced in temperature resistance, deep drawing resistance, and pressure resistance, the purpose of the present invention is to provide a coating with deep drawing resistance, good elongation of the paint film, and no yellowing at high temperatures. Capacitor coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Recipe (1)

[0043] Bisphenolic Acid 11.2g

[0044] Acetic anhydride 25ml

[0045] Pyridine 0.12ml

[0046] Recipe (2)

[0047] Bisphenol Acetate A 21.7g

[0048] Bisphenol Acid 3.5g

[0049] Recipe (3)

[0050] Hyperbranched Polyester Resin B 25.7

[0051] SK chemicals ES-710 10.5g

[0052]Bayer Desmodur BL3475SN 5.2g

[0053] king industry K-FLEX A307 3.7g

[0054] PE slip wax 0.1g

[0055] Epoxy phosphate Lubrizol 2061 0.4g

[0056] Dibutyltin dilaurate 0.2g

[0057] Defoamer BYK354 0.1g

[0058] Leveling agent EFKA-3777 0.2g

[0059] Propylene Glycol Methyl Ether Acetate 20g

[0060] Solvesso100 solvent 32.9g

[0061] The preparation steps of hyperbranched polyester resin are as follows:

[0062] 1. Under the condition of nitrogen protection, in the reaction bottle equipped with electromagnetic stirring, thermometer and condenser tube, add each substance in formula (1) in turn, stir and mix evenly. After the bisphenolic acid is completely dissolve...

Embodiment 2

[0068] Recipe (1)

[0069] Bisphenolic Acid 15.2g

[0070] Acetic anhydride 20ml

[0071] Pyridine 0.12ml

[0072] Recipe (2)

[0073] Bisphenol Acetate A 33.6g

[0074] Bisphenolic Acid 4.0g

[0075] Recipe (3)

[0076] Hyperbranched polyester resin B 32.0g

[0077] Italkid 300 7.5g

[0078] Bayer Desmodur BL3475SN 4.2g

[0079] king industry K-FLEX A307 4.2g

[0080] MF-5 PTFE Slip Wax 0.1g

[0081] Epoxy phosphate Lubrizol 2061 0.3g

[0082] Dibutyltin diacetate 0.2g

[0083] Defoamer BYK088 0.1g

[0084] Leveling agent EFKA-3777 0.2g

[0085] Propylene glycol methyl ether acetate 25g

[0086] Solvesso100 solvent 26.2g

[0087] The preparation steps of hyperbranched polyester resin are as follows:

[0088] 1. Under the condition of nitrogen protection, in the reaction bottle equipped with electromagnetic stirring, thermometer and condenser tube, add each substance in formula (1) in turn, stir and mix evenly. After the bisphenolic acid is completely dissol...

Embodiment 3

[0094] Recipe (1)

[0095] Bisphenolic acid 20.7g

[0096] Acetic anhydride 40ml

[0097] Pyridine 0.27ml

[0098] Recipe (2)

[0099] Bisphenol Acetate A 38.6g

[0100] Bisphenolic Acid 8.5g

[0101] Recipe (3)

[0102] Hyperbranched polyester resin B 36.4g

[0103] Dynapol L-912 8.0g

[0104] Bayer Desmodur BL3175SN 5.8g

[0105] king industry K-FLEX A307 4.2g

[0106] LP1040F PE Slip Wax 0.1g

[0107] Epoxy phosphate HA2802 0.3g

[0108] Dibutyltin oxide 0.2g

[0109] Defoamer BYK354 0.1g

[0110] Leveling agent Naybo 62 0.2g

[0111] Propylene glycol methyl ether acetate 20.0g

[0112] Solvesso 100 Solvent 24.7g

[0113] The preparation steps of the capacitor coating with deep drawing performance and high temperature non-yellowing are the same as in Example 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a non-yellowing capacitor coating at a high temperature having deep drawing resistance performance and a preparation method thereof. The capacitor coating in the invention is prepared from the materials according to the following parts by weight: 20 to 50 parts of hyperbranched polyester resin, 1 to 7 parts of saturated polyester resin, 3 to 12 parts of isocyanate, 0 to 0.5 parts of adhesion promoter, 0 to 0.15 parts of slipping wax, 0 to 0.3 parts of organic tin catalyst, 2.0 to 6.0 parts of resin modifier, 0.07 to 1.0 parts of defoamer, 0.15 to 0.20 parts of flattingagent, and 30 to 62 parts of solvents. The hyperbranched polyester resin, saturated polyester resin and isocyanate are put into a container so as to prepare a mixture after high-speed dispersing; therest of the materials are then put into the mixture so as to mix homogeneously by medium-speed dispersing, thereby obtaining the non-yellowing capacitor coating at a high temperature having deep drawing resistance performance. The capacitor in the invention has the characteristics of deep drawing resistance, good percentage elongation of coating film and no yellowing at a high temperature.

Description

technical field [0001] The invention belongs to the technical field of capacitor coatings, and in particular relates to a capacitor coating with deep drawing resistance and high temperature non-yellowing and a preparation method thereof. Background technique [0002] Electronic components are used in different environments, so they have sufficient resistance to humidity, heat, mildew, salt spray, etc. Moisture has a particularly pronounced effect on components. Therefore, most electronic components require coating encapsulation. This is a protective measure for insulation and moisture resistance, and it can also prevent mechanical abrasion and beautify the appearance. The requirements for coating materials mainly have advantages in terms of dielectric properties, temperature resistance, mechanical strength, anti-aging, and moisture resistance. [0003] The production of electronic capacitors generally adopts the vacuum impregnation process to coat the coating after the al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/00
Inventor 冯志德唐靖熊华山兰家勇
Owner 清远慧谷新材料技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com