Dispersible papermaking lubricant and preparation method thereof
A dispersive and lubricant technology, applied in papermaking, textiles and papermaking, fiber raw material processing, etc., can solve the problems of poor storage stability, easy layering, long storage time, etc., to achieve improved storage stability and a wide range of solid content , The effect of simple preparation process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] Add 74 grams of calcium hydroxide and 1000 grams of water to a four-necked flask with a thermometer. The temperature is increased to 80°C, and 284 grams of stearic acid in a molten state are added. The addition time is 0.5 hours. After reacting for 1 hour, the product is cooled out. The material is dewatered in the SB / SS three-foot upper discharge centrifuge (the same below) to obtain calcium stearate with a solid content of 60% by weight. 505 grams of calcium stearate is dispersed in 2.47 grams of water, and added 2.22 grams of sodium lauryl sulfate, 1.48 grams of emulsifier MOA-3 (Jiangsu Haian Petrochemical Plant) (fatty alcohol polyoxyethane condensate, n=3), after dispersion, grind in a grinder to obtain A dispersible lubricant with a solid content of 60% by weight.
[0022] The obtained product has an average particle size of 0.05μm and a viscosity of 800cps. Viscosity test uses NDJ-1 rotary viscometer 2# rotor; particle size test uses JL-1155 laser particle size di...
Embodiment 2
[0024] Add 58 grams of magnesium hydroxide and 1000 grams of water into a four-necked flask with a thermometer, and add 100 grams of molten lauric acid to the temperature of 70°C. The addition time is 2 hours, the reaction is 3.5 hours, and the product is cooled and discharged. Dehydrate to obtain magnesium laurate with a solid content of 50% by weight. Disperse 213.4 g of magnesium laurate with 338.7 g of water. Add 2.9 g of polyethylene glycol stearate and triethylhexyl phosphate (Jiande City). Xinde Chemical Co., Ltd.) 1.74 g, uniformly dispersed, and then ground to obtain a dispersible lubricant with a solid content of 20%. The obtained product has an average particle size of 0.5μm and a viscosity of 250cps.
Embodiment 3
[0026] Add 171.3 g of barium hydroxide and 1000 g of water into a four-necked flask with a thermometer. The temperature is increased to 100 ℃, and 452 g of triaconic acid in molten state is added. It is dehydrated to obtain barium triaconate with a solid content of 85%. 567.4 g of barium triaconate is dispersed in 37.26 g of water, and 0.34 g of sorbitan polyoxyethylene stearate monoester, hydroxypropyl methyl 6.85 grams of cellulose, uniformly dispersed and ground to obtain a dispersible lubricant with a solid content of 80%. The product has an average particle size of 0.1μm and a viscosity of 530cps.
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com