High-abrasion resistant ultraviolet light solidifying fingerprint resistant coating
An ultraviolet light, high wear-resistant technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problem that the performance of the coating film cannot meet the wear resistance requirements of portable electronic products, and achieve easy mass production and excellent wear resistance Performance and hardness, the effect of simple preparation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0024] Example 1:
[0025] The following components: high-functionality urethane acrylate (six-functionality M-80 of Dejing Co., Ltd.) 20%; bifunctional urethane acrylate (M-60 of Dejing Co., Ltd.) 15%; acrylate mono Body (methyl acrylate) 10%; high-functionality acrylate (trimethylolpropane triacrylate) 15%; fluorine-containing acrylate (heptafluorooctyl acrylate) 15%; nano inorganic powder filler 5% (particles) Silicon dioxide with a diameter of 10-50nm); photoinitiator (benzophenone) 2%; additives (leveling agent BYK-3060.5%, defoaming agent BYK-0660.2%, wetting agent BYK-1640.3%) 1 %; solvent (5% ethyl acetate, 5% butyl acetate, 7% 4-methyl-2-pentanone) 17%. Add it to the stirred tank and mix evenly to form paint. The above percentages are weight ratios.
[0026] Spray the above coatings on the ABS substrate and test the coating film performance after UV curing. The ultraviolet curing method and the coating film performance testing method are all well-known technologies in ...
Example Embodiment
[0034] Example 2:
[0035] The following components: high-functionality urethane acrylate (Nine-functionality M-81 from Dejing Co., Ltd.) 15%; bifunctional urethane acrylate (M-70 from Dejing Co., Ltd.) 25%; acrylate mono Body (butyl acrylate) 8%; high-functionality acrylate (trimethylolpropane trimethacrylate) 5%; fluorine-containing acrylate (heptafluorooctyl acrylate) 25%; nano inorganic powder filler (particles) Titanium dioxide with diameter 20~60nm) 5%; photoinitiator (DEAP) 2%; additives (leveling agent BYK UV35000.5%, defoamer BYK-0660.2%, wetting agent BYK-1610.3%) 1%; Solvent (3% ethylene glycol monomethyl ether, 5% acetone, 6% 4-methyl 2-pentanone) 14%. Add it to the stirred tank and mix evenly to form paint. The above percentages are weight ratios.
[0036] Spray the above coatings on the ABS substrate and test the coating film performance after UV curing.
[0037] Film performance:
[0038] 1. No blistering, peeling or obvious discoloration in appearance;
[0039] 2. T...
Example Embodiment
[0044] Example 3:
[0045] The following components: high-functionality polyurethane acrylate (SM-6318 of Jiangsu Sanmu Group Co., Ltd.) 25%; bifunctional polyurethane acrylate (SM-6201 of Jiangsu Sanmu Group Co., Ltd.) 15%; acrylate monomer ( Isobornyl acrylate) 5%; high-functionality acrylate (pentaerythritol tetraacrylate) 8%; fluorine-containing acrylate (tridecafluorooctyl methacrylate) 20%; nano-inorganic powder filler (particle size 20~ 30 nano calcium carbonate) 8%; photoinitiator (α-hydroxycyclohexyl benzophenone) 5%; additives (leveling agent BYK 3580.8%, defoaming agent BYK-0660.2%, wetting agent EFKA-4800 0.3% , Holead Ultramarine HG 0.5%) 1.8%; solvent (4% propylene glycol ethyl ether acetate, 5% xylene, 3.2% butanol) 12.2%. Add it to the stirred tank and mix evenly to form paint. The above percentages are weight ratios.
[0046] Spray the above coatings on the ABS substrate and test the coating film performance after UV curing.
[0047] Film performance:
[0048] 1. ...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap