Compression molding fibre-reinforced straw plastic combined cabinet slab and preparation method thereof

A fiber-reinforced, molding technology, applied in the field of molding fiber-reinforced straw-plastic composite cabinet board and its preparation, can solve the problems of low mechanical strength, high production cost, poor waterproof performance, etc., achieve high productivity and reduce production costs The effect of high energy consumption and nail holding force

Inactive Publication Date: 2011-08-17
绍兴一普塑业有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the fireproof board series with a large market share is made of particleboard as the core material and hot-pressed with melamine-impregnated paper veneer. This type of material has the following defects: environmental safety of formaldehyde release, poor waterproof performance, low mechanical strength, High production costs and high prices, etc., the industry urgently needs to rely on independent innovation to develop new green materials with high performance, low cost, long life and environmental safety

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] In this example, the modified crop straw fiber is firstly prepared by mass parts: 0.9 part of crop straw fiber; 0.05 part of anhydrous sodium silicate; 0.001 part of surfactant; 0.005 part of methyl silicone oil at 120 ° C. Blend in a high speed blender for 15 minutes. Wherein the crop straw is rice straw, and the surfactant is sodium dodecylbenzenesulfonic acid.

[0034] Then carry out the preparation of fiber-reinforced straw-plastic composite cabinet panels by molding method, firstly prepare modified talc powder: use 0.05 part of methyl silicone oil and 0.95 part of 800 mesh talc powder at 100 ° C for 30 minutes at high speed to mix the modified talc powder made.

[0035] The chemical auxiliary agent adopts titanate coupling agent and polyethylene wax; the mass ratio of titanate coupling agent and polyethylene wax is 1:1-1:2.

[0036] Polyolefin thermoplastic resin is polyethylene thermoplastic resin recycled material.

[0037] The parts by mass: 0.4 part of modif...

Embodiment 2

[0039] In this example, the modified crop straw fiber is firstly prepared by mass parts: 0.95 part of crop straw fiber; 0.1 part of anhydrous sodium silicate; 0.005 part of surfactant; 0.01 part of methyl silicone oil at 140 ° C Blend in a high speed blender for 60 minutes. The crop straw is wheat straw, and the surfactant is sodium dodecylbenzenesulfonic acid.

[0040] Then carry out the preparation of fiber-reinforced straw-plastic composite cabinet panels by molding method, firstly prepare modified talc powder: use 0.01 part of methyl silicone oil and 0.99 part of 800 mesh talc powder at 150 ° C for 60 minutes at high speed to mix the modified talc powder made.

[0041] The chemical auxiliary agent adopts titanate coupling agent and polyethylene wax; the mass ratio of titanate coupling agent and polyethylene wax is 1:1-1:2.

[0042] Polyolefin thermoplastic resin is polypropylene thermoplastic resin recycled material.

[0043] The mass parts are: 0.6 parts of modified cr...

Embodiment 3

[0045] In this example, the modified crop straw fiber is firstly prepared by mass parts: 0.92 part of crop straw fiber; 0.08 part of anhydrous sodium silicate; 0.003 part of surfactant; 0.007 part of methyl silicone oil at 130 ° C. Blend in a high speed blender for 45 minutes to make. The crop stalks are cotton stalks, and the surfactant is sodium dodecylbenzenesulfonic acid.

[0046] Then carry out the preparation of fiber-reinforced straw-plastic composite cabinet panels by molding method, firstly prepare modified talc powder: use 0.07 part of methyl silicone oil and 0.97 part of 800 mesh talc powder for modified talc powder at 130 ° C for 45 minutes at high speed and mix. made.

[0047] The chemical auxiliary agent adopts titanate coupling agent and polyethylene wax; the mass ratio of titanate coupling agent and polyethylene wax is 1:1-1:2.

[0048] Polyolefin thermoplastic resin is a new material of polyvinyl chloride.

[0049]The parts by mass: 0.2 part of modified cro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a compression molding fibre-reinforced straw plastic combined cabinet slab which is prepared from the following raw materials according to parts by weight: 0.2-0.6 part of modified crop straw fibre or straw fibre wood powder thereof, 0.1-0.2 part of PET or nylon waste silk, 0.05-0.2 part of melamine, 0.05-0.2 part of modified talcum powder, 0.01-0.05 part of chemical assistant and 0.3-0.6 part of polyolefin thermoplastic resin. The invention also discloses a preparation method thereof. The cabinet slab of the invention is formaldehyde-free environment-protection material and has wood texture and handling characteristics, and the machinery mechanics strength thereof exceeds that of good-quality solid-wood slabs; and in addition, the cabinet slab does not adsorb water and has the functions of low coefficient of thermal expansion, moisture prevention, mildew prevention, aging prevention, combustion prevention, reuse and the like and is an ideal cabinet slab wood replacing material.

Description

technical field [0001] The invention relates to a molded fiber reinforced straw-plastic composite cabinet board and a preparation method thereof. Background technique [0002] Cabinet boards are a huge market in the home improvement industry, and the safety and economic applicability of flat board materials for family cabinets are also issues involving the livelihood of thousands of households. At present, the boards used to make cabinets in my country include fire-resistant boards, paint boards, PVC molded blister board, acrylic board, moisture-proof particle board, etc. Except for solid wood boards, most of the boards are made of density board (fiberboard) or particle board as the core material and then veneered or surface coated. For example, the fireproof board series with a large market share is made of particleboard as the core material and hot-pressed with melamine-impregnated paper veneer. This type of material has the following defects: environmental safety of forma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L23/12C08L27/06C08L97/02C08L67/02C08L77/00C08K13/06C08K9/06C08K3/34C08K5/3492B29C43/02B29C43/58B29B7/72
Inventor 谢德芳桂先伦李黎明张占荣史月华
Owner 绍兴一普塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap