Method for preparing thermal barrier coating

Abstract

The invention discloses a method for preparing a thermal barrier coating. According to the method disclosed by the invention, a deposition matrix is bombarded by ion beams while a deposition coating is evaporated by electron beams, the steam energy of the electron beams is about 0.1-1 electron volts, and the energy is not enough to well migrate atoms in the process of depositing the coating; and the energy of the ion beams can reach thousands of electron volts, and the energy is enough to interfere growth of columnar crystals to increase crystal boundaries and crystal sub-boundaries and enlarge or increase microscopic holes so as to reduce phonon and photon scattering mean free path and reduce the thermal conductivity of the thermal barrier coating. The energy of vaporous clouds can be increased through activation ionization effects of ions; and compared with the conventional EB-PVD (Electron Beam Physical Vapour Deposition), the method can ensure that same performances can be achieved at low deposition temperature; furthermore, forms, structures and stresses of the columnar crystals can be also adjusted and controlled through ion assisted deposition, and thus, the service life ofthe thermal barrier coating can be prolonged.

Description

technical field [0001] The invention relates to a method for preparing a thermal barrier coating, which belongs to the technical field of surface treatment of metal materials. The thermal barrier coating with low thermal conductivity and long life can be prepared by using the method, and the invention is applicable to the fields of coating preparation and surface modification, including the preparation of metal and ceramic coatings. Background technique [0002] The currently widely used aero-engine thermal barrier coating system is mainly composed of yttria partially stabilized zirconia (YSZ) ceramic coating and MCrAlY (where M stands for Ni, Co or NiCo) metal bonding layer, which plays a role of thermal insulation What is YSZ ceramic coating. The structure and performance of YSZ coating are closely related to the preparation method and process parameters. The preparation methods are mainly plasma spraying and electron beam physical vapor deposition (EB-PVD). Both methods ...

AI Technical Summary

Problems solved by technology

However, the layered structure of plasma spraying is parallel to the surface of the substrate, so that there are many transverse interfaces in the ceramic layer. The coating with this structure is not enough to resist the thermal stress generated by the thermal cycle in the high temperature working environment, which will cause the coating to peel off prematurely.

However, the coating prepared by EB-PVD can obtain a columnar crystal structure perpendicular to the surface of the substrate, which has a high stress tolerance, significantly improves the thermal stress resistance of the coating, and has a service life much longer than that of plasma sprayed thermal barrier coatings. layer, but the thermal barrier coating prepared by EB-PVD has higher thermal conductivity, and the thermal insulation effect is not as good as that of plasma sprayed thermal barrier coating

Although the composition of YSZ prepared by these two methods is the same, the performance is very different due to the different structure, so the structure is very important to the performance of YSZ coating

Images