Two-component castor oil polyurethane waterproof paint

A technology of polyurethane waterproofing and castor oil, applied in polyurea/polyurethane coatings, coatings, etc., can solve the problem of affecting the adhesion of the film to the substrate, the difficulty of isocyanate moisture absorption and curing, and the poor appearance of the film, etc. Problems, to achieve the effect of improving and adjusting the coating performance, improving the appearance state, and good decorative effect

Inactive Publication Date: 2012-04-18
湖北蓝盾之星科技有限公司 +1
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After the surface is cured, the diffusion of water to the interior of the coating film is hindered, making it difficult to absorb moisture and cure the remaining isocyanate in the coating film, and the system takes a long time to dry.
In addition, because the bubbles produced by moisture absorption and curing inside the coating film are not easy to discharge, the apparent state of the film coating is not good, and it also affects the adhesion of the film coating to the substrate.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Two-component castor oil polyurethane waterproof paint
  • Two-component castor oil polyurethane waterproof paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] White exposed waterproof coating: the specific ratio is: component A: castor oil 20.0%, 2,4-toluene diisocyanate 38.07%, xylene 8.6%, azobisisobutyronitrile 0.2%; component B: two Glycol 8.0.%, titanium dioxide 15.5%, talcum powder 2.0%, ultramarine 0.05%, coupling agent YB-201A (the titanate coupling agent of Changzhou Yabang Yayu Auxiliary Co., Ltd. can be used) 0.08%, Formic acid methacrylate 7.0%, antioxidant 1010 0.1%, UV-292 0.1%, hydroquinone 0.1%, stannous octoate 0.1%, triethylenediamine 0.1%. Mix component A and component B, add an appropriate amount of diluent, stir evenly, let stand for 30 minutes, cast on the glass template and spray on the steel plate at room temperature, keep the temperature at 30°C for 7 days. The surface drying time of the coating on the glass formwork is 2 hours, and the surface drying time of the coating on the steel plate is 2 hours; the glossiness of the coating on the steel plate is 60.3, and the hardness is 3H; the coating film on...

Embodiment 2

[0019]White exposed waterproof coating: the specific ratio is: component A: castor oil 30.07%, 2,4-toluene diisocyanate 20.0%, xylene 8.6%, azobisisobutyronitrile 0.2%; component B: two Glycol 8.0.%, titanium dioxide 15.5%, talcum powder 2.0%, ultramarine 0.05%, coupling agent YB-201A (the titanate coupling agent of Changzhou Yabang Yayu Auxiliary Co., Ltd. can be used) 0.08%, Formic acid methacrylate 7.0%, antioxidant 1010 0.1%, UV-292 0.1%, hydroquinone 0.1%, stannous octoate 0.1%, triethylenediamine 0.1%. Mix component A and component B, add an appropriate amount of diluent, stir evenly, let stand for 30 minutes, cast on the glass template and spray on the steel plate at room temperature, keep the temperature at 30°C for 7 days. The surface drying time of the coating on the glass formwork is 3 hours, and the surface drying time of the coating on the steel plate is 2 hours; the glossiness of the coating on the steel plate is 60.4, and the hardness is 3H; the coating film on ...

Embodiment 3

[0021] White exposed waterproof coating: the specific ratio is: component A: castor oil 27.0%, 2,4-toluene diisocyanate 14.85%, xylene 4.2%, ethyl acetate 2.1%, azobisisobutyronitrile 0.3% ; Component B: 8.5% diethylene glycol, 16.5% titanium dioxide, 3.0% talcum powder, 0.15% ultramarine blue, coupling agent YB-201A (the titanate coupling of Changzhou Yabang Yayu Auxiliary Co., Ltd. agent) 0.5%, methacrylic acid formic acid 21.8%, antioxidant 1010 0.2%, UV-292 0.3%, hydroquinone 0.2%, stannous octoate 0.2%, triethylenediamine 0.2%. Mix component A and component B, add an appropriate amount of diluent, stir evenly, let stand for 30 minutes, cast on the glass template and spray on the steel plate at room temperature, keep the temperature at 30°C for 7 days. The surface drying time of the coating on the glass formwork is 2 hours, and the surface drying time of the coating on the steel plate is 1.5 hours; the glossiness of the coating on the steel plate is 72.8, and the hardness ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

A two-component castor oil polyurethane waterproof paint is obtained by interpenetrating a polyurethane prepolymer (component A) and a colorant (component B) under the actions of an initiator and a catalyst. The component A is obtained by reacting castor oil and 2,4-toluene diisocynate in an organic solvent with a dissolved initiator. The preparation method of the component B comprises the following steps of: mixing a blending agent and a solid pigment (or solid filler) with a coupling agent, grinding, and then adding an allyl monomer, a catalyst, a polymerization inhibitor and a light stabilizer in turn to stir evenly. The two-component castor oil polyurethane waterproof paint has excellent waterproof performance, good appearance, rich colors, good decorative effect, adjustable curing time, adjustable flexibility and hardness and convenience in operations.

Description

technical field [0001] The invention relates to a polyurethane waterproof coating, in particular to a two-component castor oil polyurethane waterproof coating. Background technique [0002] Polyurethane (PU-Polyurethane) is the abbreviation of polyurethane, which is a kind of polymer. It is a polymer made of raw materials such as polyisocyanate and polyether polyol or polyester polyol or small molecule polyol, polyamine or water and other chain extenders or crosslinking agents. By changing the type and composition of raw materials, the shape and performance of the product can be greatly changed, and the final product can be obtained from soft to hard. Compared with other polymer coatings, polyurethane has many advantages, such as good mechanical properties of materials, wide range of performance adjustment, and good molding process performance. PU is one of the six most developed synthetic coatings in the world. In terms of its breadth of application, it has become the fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/14C09D7/12
Inventor 谭晓明胡远强徐闫郑鑫鲁小龙张盛付争兵
Owner 湖北蓝盾之星科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com