Nano titanium dioxide special for flue gas denitrifying catalyst and preparation method thereof
A denitrification catalyst and nano-titanium dioxide technology, which is applied in the direction of chemical instruments and methods, separation methods, and dispersed particle separation, can solve the problems of polluting the environment, being highly toxic, and not easy to store, so as to increase the specific surface area and enhance surface acidity , The effect of simple process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] The metatitanic acid prepared by the sulfuric acid method is washed with deionized water to remove impurities, so that the iron ion, alkali metal ion and various heavy metal ions in the metatitanic acid are less than 100ppm. Weigh 350kgTiO 2 Metatitanic acid slurry, add deionized water, configure TiO 2 20% metatitanic acid slurry. The slurry is transported to the mixer, add an appropriate amount of ammonia water to adjust the pH value of the slurry to 7, then add 45kg of ammonium carbonate, after fully stirring, add 33kg of ammonium sulfate, after stirring for 1 hour, transport to the membrane filter press after pressure filtration (solid content About 55%, the content of pore-forming agent after press filtration is about TiO 2 4.3% of the mass percentage) to the rotary kiln, dry and roast from 70°C to 610°C at a heating rate of 30°C / hour to obtain nano-titanium dioxide special for denitrification catalyst, its SO 4 2- The content is 2.4%, the rest is TiO 2 , the a...
Embodiment 2
[0027] Ammonium carbonate is not added, and the pH value of the slurry is not adjusted, and other conditions are consistent with Example 1, so that the special nano-titanium dioxide for denitration catalyst is obtained, and its SO 4 2- The content is 2.4%, the rest is TiO 2 , the average crystal particle size is 25nm, and the BET specific surface area is 73M 2 / g.
Embodiment 3
[0029] Change the heating rate in Example 1 to 20° C. / hour, change the maximum calcination temperature to 500° C., and other conditions are consistent with Example 1 to obtain nano-titanium dioxide special for denitrification catalyst. 4 2- The content is 2.4%, the rest is TiO 2 , the average crystal particle size is 17nm, and the BET specific surface area is 98M 2 / g.
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com