Preparation method for soft porous synthetic paper
A synthetic paper, soft technology, applied in the field of soft synthetic paper preparation, can solve the problems of hard hand feeling, high production energy consumption, slow ink penetration, etc., to improve penetration and absorption speed, reduce production costs, fast ink penetration Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0021] Example 1:
[0022] Weigh 2.2 kilograms of isophorone diisocyanate, 160 kilograms of polycaprolactone diol (molecular weight 8000), and 100 kilograms of dimethylformamide into the reactor, react at 80°C for 3 hours, and then add 1 3.8 kg of 3'-propylene glycol and 13.3 kg of isophorone diisocyanate were reacted at 80°C for 2 hours to obtain a viscous polyurethane solution; the prepared polyurethane solution was cooled to 25°C, and 318.4 kg of dimethyl was added Base formamide is formulated into a solution with a polyurethane solid mass content of 30%, then 147 kg of light calcium carbonate is added, and stirred for 1 hour to obtain a mixed solution; 80% of the total obtained mixed solution is coated on release paper, And sent to the oven for drying (the oven temperature is 70 ℃), after the film on the release paper is completely dried, the substrate for synthetic paper production is obtained; the remaining mixed solution is coated on the synthetic paper with a certain thic...
Example Embodiment
[0024] Example 2:
[0025] Weigh 2.6 kilograms of 4,4-dicyclohexylmethane diisocyanate, 400 kilograms of polybutylene adipate glycol (molecular weight 20,000), and 300 kilograms of dimethylacetamide into the reactor at 80°C After reacting for 3 hours, 5.9 kg of 1,6'-hexanediol and 15.7 kg of 4,4-dicyclohexylmethane diisocyanate were added. The reaction was continued at 80°C for 2 hours to obtain a viscous polyurethane solution; then the prepared The polyurethane solution was cooled to 20°C, and 689.8 kg of dimethylacetamide was added to prepare a solution with a polyurethane solid content of 30%, then 787.8 kg of heavy calcium carbonate was added, and stirred for 1 hour to obtain a mixed solution; 70% of the total mixed solution is coated on release paper and sent to an oven for drying (the oven temperature is 110°C). After the film on the release paper is completely dried, the base for synthetic paper production is obtained. Finally, the remaining mixed solution is coated on th...
Example Embodiment
[0027] Example 3:
[0028] Weigh 2.6 kilograms of 4,4-dicyclohexylmethane diisocyanate, 300 kilograms of polyethylene adipate diol (molecular weight 15000), and 200 kilograms of dimethylacetamide into the reactor at 80°C After reacting for 3 hours, add 4.5 kg of 1,4'-butanediol and 13.3 kg of isophorone diisocyanate and continue to react at 80°C for 2 hours to obtain a viscous polyurethane solution; then, the prepared polyurethane solution is cooled to 22℃, and 547.6 kg of dimethylformamide was added to prepare a solution with a polyurethane solid content of 30%, and 480.6 kg of colloidal calcium carbonate was added, and stirred for 1 hour to obtain a mixed solution; then the total amount of the obtained mixed solution 80% of the release paper is coated on the release paper and sent to the oven for drying (the oven temperature is 90℃). After the film on the release paper is completely dried, the base material for synthetic paper production is obtained; The remaining mixed soluti...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap