Method for surface modification of calcium sulfate crystal whisker

A calcium sulfate whisker and surface modification technology, applied in chemical instruments and methods, calcium/strontium/barium sulfate, crystal growth, etc., to reduce production costs and achieve zero emissions

Active Publication Date: 2015-04-22
KUNMING UNIV OF SCI & TECH
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of this invention is to provide a kind of method of surface modification calcium sulfate whisker, the technical problem solved is to overcome existing calcium sulfate whisker and modification process insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The concrete steps of present embodiment surface modification calcium sulfate whisker comprise as follows:

[0029] (1) Dry the calcium sulfate whiskers under hot air at 110°C for 2 hours, and then stand at room temperature for 8 minutes to obtain dry calcium sulfate whiskers; the average diameter of calcium sulfate whiskers is 0.5 μm, the average length is 30 μm, and the average major diameter than 20, where CaSO 4 Content ≥ 99.99wt%.

[0030] (2) Mix calcium sulfate whiskers, polyquaternary ammonium salts, octadecylamine and absolute ethanol at a mass ratio of 100:2:3:1200, and use ammonia water to adjust the pH of the reaction system to 6; the quality of ammonia in ammonia water The score is 25%.

[0031] (3) Heat the reaction system to 80°C, shake at a constant temperature for 6 minutes under the condition of a shaking rate of 300r / min, then filter, and return the filtrate to the reactor for use to obtain a filter residue;

[0032] (4) Dry the filter residue obta...

Embodiment 2

[0034] The concrete steps of present embodiment surface modification calcium sulfate whisker comprise as follows:

[0035] (1) Dry the calcium sulfate whiskers under hot air at 90°C for 3 hours, and then let them stand at room temperature for 5 minutes to obtain dry calcium sulfate whiskers; the average diameter of calcium sulfate whiskers is 3 μm, the average length is 150 μm, and the average aspect ratio 100, where CaSO 4 Content ≥ 99.99wt%.

[0036] (2) Mix calcium sulfate whiskers, polyquaternary ammonium salts, octadecylamine and absolute ethanol at a mass ratio of 100:3:5:1000, and use ammonia water to adjust the pH of the reaction system to 9; the quality of ammonia in ammonia water The score is 26%.

[0037] (3) Heat the reaction system to 70°C, shake at a constant temperature for 7 minutes at a shaking rate of 300r / min, then filter, and return the filtrate to the reactor for use to obtain a filter residue;

[0038] (4) Dry the filter residue obtained in step (3) wi...

Embodiment 3

[0040] The concrete steps of present embodiment surface modification calcium sulfate whisker comprise as follows:

[0041] (1) Dry calcium sulfate whiskers under hot air at 100°C for 4 hours, and then stand at room temperature for 10 minutes to obtain dry calcium sulfate whiskers; the average diameter of calcium sulfate whiskers is 6 μm, the average length is 300 μm, and the average aspect ratio 200, of which CaSO 4 Content ≥ 99.99wt%.

[0042](2) Mix calcium sulfate whiskers, polyquaternary ammonium salt, octadecylamine and absolute ethanol at a mass ratio of 100: 4: 6: 1500, and use ammonia water to adjust the pH of the reaction system to 7; the quality of ammonia in ammonia water The score is 28%.

[0043] (3) Heat the reaction system to 90°C, shake at a constant temperature for 8 minutes at a shaking rate of 300r / min, then filter, and return the filtrate to the reactor for use to obtain a filter residue;

[0044] (4) Dry the filter residue obtained in step (3) with hot ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for jointly modifying a calcium sulfate crystal whisker by utilizing quaternary ammonium salt and octadecylamine and belongs to the technical field of material utilization. The method comprises the following steps of: firstly drying the calcium sulfate crystal whisker; then, mixing the calcium sulfate crystal whisker, poly quaternary ammonium salt, octadecylamine and absolute ethyl alcohol according to a certain proportion, adjusting the pH of the liquid to 6-9 and filtering; and drying filter residues to obtain the modified product calcium sulfate crystal whisker. The method is carried out under the non-high-temperature condition of the absolute ethyl alcohol and can better protect the structure of the calcium sulfate crystal whisker, maintains the length-diameter ratio of the calcium sulfate crystal whisker, and is good in the modification effect and high in activation index; and the calcium sulfate crystal whisker is used as a material enhancing element to be added into polycaprolactone so as to obviously enhance the mechanical property of polycaprolactone. By using the method, the production cost is reduced, and zero discharge of pollutants is realized. The method disclosed by the invention belongs to a green and clean chemical process.

Description

Technical field: [0001] The present invention involves a method of combining calcium sulfate in the use of polyamine salt and eighteen amine, which is the technical field of material utilization. Background technique: [0002] Calcium sulfate is a fibrous crystal made of dissolving, heavy crystallization or water heat.It can be used as a material enhancement group. Compared with glass fiber, calcium sulfate must be smaller, high -temperature resistant, good tough, high strength, stronger affinity with rubber and plastic, is a green environmental protection with excellent performance.Materials can be widely used in rubber, plastic, adhesives, friction materials, as well as industries and fields such as cement slowing and environmental engineering. [0003] However, due to the characteristics of large surface area, high surface can be high, and large contact interface, calcium sulfate crystals must be easily reunited between crystal beard during the preparation and application, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C30B29/22C30B29/62C30B33/00C08K7/08C08K9/04C01F11/46
Inventor 马林转王华陈迁卿山崔琼芳祝星
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com