Novel immobilized 8-hydroxyquinoline type chelate adsorption material and preparation method thereof

A hydroxyquinoline type, chelating adsorption technology, applied in chemical instruments and methods, adsorption water/sewage treatment, other chemical processes, etc., can solve the problems of low bonding amount of 8-hydroxyquinoline and small adsorption capacity, etc. Achieve the effects of high coordination complexing ability, simple preparation process and easy preparation process

Inactive Publication Date: 2012-11-14
ZHONGBEI UNIV
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Purpose of the present invention: In order to solve the existing chelating adsorption materials, the bonding amount of 8-hydroxyquinoline on the substrate surface is low, and the adsorption capacity is small, providing a stable performance, good rigidity, and a variety of heavy metal adsorption...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel immobilized 8-hydroxyquinoline type chelate adsorption material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Example 1: In a four-necked flask, add 1.0 g of amino-containing silane coupling agent-modified silica gel particles, 5 mL of hydroxyethyl methacrylate and 100 mL of DMF and H 2 Mixed solvent of O (V:V=1:1), blow nitrogen for 30min, heat up to 30°C, add 0.0537g of ammonium persulfate aqueous solution to the reaction system, react at constant temperature for 12h, filter with suction, and extract the filter cake with methanol Dry at 70°C for 24 hours to obtain silica gel particles PHEMA / SiO grafted with polyhydroxyethyl methacrylate 2 . The graft rate of poly(hydroxyethyl methacrylate) is 41.3%.

[0020] In the four-neck flask, add 0.5g grafted particle PHEMA / SiO 2 , 1.82g 5-chloromethyl-8-hydroxyquinoline CHQ and 20mL dimethyl sulfoxide, heated to 90°C, and added 1.5gNa 2 CO 3 , N 2 Under the atmosphere, react at constant temperature for 6 hours, filter, wash with water, wash with absolute ethanol, and dry to obtain the functional composite particle HQ-PHEMA / SiO wit...

Embodiment 2

[0021] Example 2: In a four-necked flask, add 1.0 g of amino-containing silane coupling agent-modified silica gel particles, 4.5 mL of hydroxyethyl methacrylate and 100 mL of DMF and H 2 Mixed solvent of O (V:V=1:1), blow nitrogen for 30min, heat up to 25°C, add 0.0483g of ammonium persulfate aqueous solution to the reaction system, react at constant temperature for 14h, filter with suction, and extract the filter cake with methanol Dry at 70°C for 24 hours to obtain silica gel particles PHEMA / SiO grafted with polyhydroxyethyl methacrylate 2 . The graft rate of poly(hydroxyethyl methacrylate) is 35.6%.

[0022] In the four-neck flask, add 0.5g grafted particle PHEMA / SiO 2 , 1.82g 5-chloromethyl-8-hydroxyquinoline CHQ and 20mL nitrobenzene, heated to 80°C, and added 1.4g NaHCO 3 , N 2 Under the atmosphere, react at constant temperature for 7 hours, filter, wash with water, wash with absolute ethanol, and dry to obtain the functional composite particle HQ-PHEMA / SiO with 8-hy...

Embodiment 3

[0023] Example 3: In a four-necked flask, add 1.0 g of amino-containing silane coupling agent-modified silica gel particles, 5.5 mL of hydroxyethyl methacrylate and 90 mL of DMF and H 2Mixed solvent of O (V:V=1:1), blow nitrogen for 30min, heat up to 35°C, add 0.0591g of ammonium persulfate aqueous solution to the reaction system, react at constant temperature for 12h, filter with suction, and extract the filter cake with methanol Dry at 70°C for 24 hours to obtain silica gel particles PHEMA / SiO grafted with polyhydroxyethyl methacrylate 2 . The graft rate of poly(hydroxyethyl methacrylate) is 39.8%.

[0024] In the four-neck flask, add 0.5g grafted particle PHEMA / SiO 2 , 1.82g 5-chloromethyl-8-hydroxyquinoline CHQ and 20mL N,N-dimethylformamide, heated to 100°C, and added 1.5g NaHCO 3 , N 2 Under the atmosphere, react at constant temperature for 5 hours, filter, wash with water, wash with absolute ethanol, and dry to obtain the functional composite particle HQ-PHEMA / SiO w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Saturated adsorption capacityaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of chelate resin materials, and particularly relates to a novel immobilized 8-hydroxyquinoline type chelate adsorption material and a preparation method thereof. 0.95-1.85mmol/g of ligand 8-hydroxyquinoline is bonded to the surface of a silica gel micro-particle modified by hydroxyethyl methacrylate (HEMA). The preparation method includes the steps: grafting the hydroxyethyl methacrylate on the surface of the silica gel micro-particle modified by amino containing silane coupling agents; and fixing the ligand 8-hydroxyquinoline on the surface of the silica gel micro-particle modified by polymer. The material is large in 8-hydroxyquinoline bonding quantity, simple in synthesis process, moderate in condition, short in time, easy to control and fine in mechanical property, is repeatedly used, has a high coordinated complexing capacity for metal ions, can enrich and recycle various precious metal ions, particularly has excellent adsorption and selection performances for heavy metals such as copper, nickel and lead, and can be used for purifying industrial wastewater.

Description

technical field [0001] The invention belongs to the technical field of chelating adsorption materials, and in particular relates to a novel immobilized 8-hydroxyquinoline type chelating adsorption material and a preparation method thereof. Background technique [0002] Chelating adsorption materials (including chelating resins) are solid (particle) materials that have chelating functional groups for metal ions bonded to the surface of a solid substrate. There are many types of chelating functional groups, such as 8-hydroxyquinoline type, iminoacetic acid type, Schiff base type, salicylic acid type, and amidoxime type. Among these types of chelating groups, 8-hydroxyquinoline is a strong chelating ligand, and Goswami A and Wang Z et al. found that it interacts with Fe 3+ Ions and Ga 3+ The coordination constants of the ions are as high as 10 38 with 10 49 [Goswami A, Singh A K, Venkataramani B. Talanta, 2003, 60: 1141; Wang Z, J Miao, F S C Lee, Wang X R. Chinese Journa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/26B01J20/30C02F1/28C02F1/62
Inventor 高保娇李延斌王蕊欣房晓琳喻龙
Owner ZHONGBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap