Manufacturing method of high-bulk coating printing paper

A technology of coated printing paper and its manufacturing method, which is applied in the field of papermaking, and achieves the effect of strong three-dimensional effect, broad market prospect, and full and bright colors of printed patterns

Active Publication Date: 2013-01-16
MCC PAPER YINHE
View PDF6 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, high-bulk printing papers on the market are mainly uncoated light offset papers, and domestic paper companies have not yet developed high-bulk coated printing papers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The components of the paint are by weight: 70 parts of heavy calcium carbonate, 20 parts of china clay, 10 parts of hollow plastic pigment (polystyrene / acrylate spherical particles); 12 parts of carboxylated styrene-butadiene latex; 5 parts of coated starch; PVA (polyvinyl alcohol) 1 part; CMC (sodium carboxymethyl cellulose) 1 part; water repellent (ammonium zirconium carbonate) 0.6 parts; lubricant (calcium stearate) 1.5 parts; defoamer (polyether modified Silicone oil type) 0.03 parts.

[0024] (1) Bleached kraft softwood pulp after beating (beating degree 42°SR, wet weight 7.3g), hardwood bleached chemical thermomechanical pulp (beating degree 36°SR, wet weight 1.3g), poplar alkali Permanent hydrogen peroxide mechanical pulp (beating degree 46°SR, wet weight 1.2g) and the three kinds of pulp are prepared according to the ratio of 25:35:40;

[0025] (2) Afterwards, 0.8% cationic starch, 0.3% PAE, 0.1% PEI and 16% light calcium carbonate filler are added sequentially...

Embodiment 2

[0033]The components of the paint are by weight: 60 parts of heavy calcium carbonate, 30 parts of china clay, 10 parts of hollow plastic pigment (polystyrene / acrylate spherical particles); 10 parts of carboxylated styrene-butadiene latex; 6 parts of coated starch; PVA (polyvinyl alcohol) 1.5 parts; CMC (sodium carboxymethyl cellulose) 1.2 parts; water repellent (ammonium zirconium carbonate) 0.7 parts; lubricant (calcium stearate) 1.6 parts; defoamer (polyether modified Silicone oil type) 0.02 parts.

[0034] (1) Bleached kraft softwood pulp after beating (beating degree 45°SR, wet weight 7.0g), hardwood bleached chemical thermomechanical pulp (beating degree 36°SR, wet weight 1.3g), poplar alkali The three pulps of permanent hydrogen peroxide mechanical pulp (beating degree 48°SR, wet weight 1.2g) were prepared according to the ratio of 20:35:45.

[0035] (2) Afterwards, 0.8% cationic starch, 0.3% PAE, 0.1% PEI and 18% light calcium carbonate filler are sequentially added to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
surface roughnessaaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing method of high-bulk coating printing paper. In the method, high proportion chemical pulp is adopted for coating body paper, light calcium carbonate is used as filler, and high bulk is achieved. A door roller coating machine is used for coating the body paper, and the coating paint adopts plastic paint with a given proportion and a hollow structure, so that the bulk of the coat and the formed paper brightness can be effectively improved. Meanwhile, a soft calender is used for pre-calendering and polishing the coated body paper, so that the fineness of the paper surface is greatly improved while the thickness of the original paper is maintained. The bulk of the high-bulk coating printing paper manufactured through the method is 1.3 to 1.5 cm<3> / g and is far better than that of the ordinary copper paper and light coating paper; and meanwhile, the surface of the paper is smooth and fine, so that printed patterns are full and rich in color, image dots are clear and strong in three-dimensional impression, and the paper is applicable to top-grade color printing.

Description

technical field [0001] The invention relates to a method for manufacturing high-bulk coated printing paper, which belongs to the technical field of papermaking. Background technique [0002] In recent years, the demand for high bulk printing papers has been increasing. The light weight of high-bulk paper not only maintains the thickness and opacity of the original paper, but also can use low-weight high-bulk paper of the same thickness to replace high-weight ordinary double-adhesive paper during printing, which is not only convenient for readers, but also can reduce paper pulp consumption, saving energy and reducing environmental pollution load. [0003] At present, high-bulk printing papers on the market are mainly uncoated light offset papers, and domestic paper companies have not yet developed high-bulk coated printing papers. In order to fill this gap in the market, and from the perspective of saving resources and protecting the environment, China Metallurgical Paper Y...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H23/56D21H19/38D21H19/40D21H19/42D21H19/54D21H19/58D21H19/60D21H19/52D21H21/06D21H21/12
Inventor 李树俭冯桂平田中粟张晗褚衍峰黄少斌曾金枝耿金亮王松
Owner MCC PAPER YINHE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap