Water-based UV (ultraviolet) plastic screen printing ink and method for preparing same

A technology of plastic filaments and inks, applied in inks, household utensils, applications, etc., can solve the problems of flexibility and achieve the effect of reducing cross-linking density and glass transition temperature

Inactive Publication Date: 2013-03-13
东莞市佳烨化工科技有限公司
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The flexibility of current UV plastic screen printing inks is difficult to meet the requirements of PE and other plastic products, and the flexibility mainly depends on the composition of the formula: ①The lower the functionality, the better the flexibility, and the low-functionality monomer can reduce the crosslinking of the cured film Density, improve flexibility; ②Multiple acrylic monomers with longer flexible chain segments can provide suitable flexibility without affecting the curing rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] A water-based UV plastic screen printing ink is composed of the following raw materials in parts by weight: 35 parts of aliphatic polyurethane acrylate, 25 parts of UV curable acrylic emulsion, 15 parts of polyethylene glycol (400) diacrylate, 17 parts of (20) ethyl Oxidized trimethylolpropane triacrylate, 17 parts of yellow pigment powder, 0.5 parts of modified polysiloxane interpolymer solution, 2 parts of silicone leveling agent, 10 parts of absolute ethanol, 1 part of 2-methyl-1 -[4-(methylthio)phenyl]-2-(4-morpholinyl)-1-propanone, 0.5 parts of organic fluorine-modified acrylate polymer, 5 parts of water.

[0063] The preparation method of a kind of water-based UV plastic screen printing ink of the present embodiment comprises the following method steps: a, aliphatic urethane acrylate, UV curing acrylic emulsion, polyethylene glycol (400) diacrylate, (20) ethoxylated Add trimethylolpropane triacrylate into the batching tank by weight and stir evenly, and the stirri...

Embodiment 2

[0066] A water-based UV plastic screen printing ink is composed of the following raw materials in parts by weight: 40 parts of aliphatic urethane acrylate, 30 parts of UV curable acrylic emulsion, 20 parts of polyethylene glycol (400) diacrylate, 20 parts of (20) ethyl Oxidized trimethylolpropane triacrylate, 20 parts of yellow pigment powder, 1 part of modified polysiloxane interpolymer solution, 5 parts of silicone leveling agent, 15 parts of absolute ethanol, 3 parts of 2-methyl-1 -[4-(methylthio)phenyl]-2-(4-morpholinyl)-1-propanone, 2 parts of organic fluorine-modified acrylate polymer, 10 parts of water.

[0067] The preparation method of a kind of water-based UV plastic screen printing ink of the present embodiment comprises the following method steps: a, aliphatic urethane acrylate, UV curing acrylic emulsion, polyethylene glycol (400) diacrylate, (20) ethoxylated Add trimethylolpropane triacrylate into the batching tank by weight and stir evenly, and the stirring time...

Embodiment 3

[0070] A water-based UV plastic screen printing ink is composed of the following raw materials in parts by weight: 30 parts of aliphatic urethane acrylate, 21 parts of UV curable acrylic emulsion, 10 parts of polyethylene glycol (400) diacrylate, 15 parts of (20) ethyl Oxidized trimethylolpropane triacrylate, 18 parts of red pigment powder, 0.6 parts of modified polysiloxane interpolymer solution, 3 parts of silicone leveling agent, 9 parts of absolute ethanol, 2 parts of 2-methyl-1 -[4-(methylthio)phenyl]-2-(4-morpholinyl)-1-propanone, 1 part of organic fluorine-modified acrylate polymer, 8 parts of water.

[0071] The preparation method of a kind of water-based UV plastic screen printing ink of the present embodiment comprises the following method steps: a, aliphatic urethane acrylate, UV curing acrylic emulsion, polyethylene glycol (400) diacrylate, (20) ethoxylated Add trimethylolpropane triacrylate into the batching tank by weight and stir evenly, and the stirring time is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of the UV (ultraviolet) ink, and in particular relates to a water-based UV plastic screen printing ink and a method for preparing the same. The water-based UV plastic screen printing ink provided by the invention is composed of the following raw materials in parts by weight: 25-40 parts of aliphatic urethane acrylate, 20-30 parts of UV cured acrylic emulsion, 10-20 parts of polyethyleneglycol diacrylate, 10-20 parts of ethylated trimethylolpropane triacrylate, 15-20 parts of pigment powder, 0.5-1 part of organic silicon defoamer, 1-5 parts of organic silicon flatting agent, 5-15 parts of absolute ethyl alcohol, 1-3 parts of photoinitiator, 0.4-2 parts of adhesion promoter and 4-10 parts of water. The water-based UV plastic screen printing ink greatly improves the flexibility of an ink layer and improves the properties of products, and is good in printing adaptability.

Description

technical field [0001] The invention relates to the technical field of UV inks, in particular to a water-based UV plastic screen printing ink and a preparation method thereof. Background technique [0002] UV ink is a kind of chemical reaction ink, which is the specific application of UV photocuring technology in the field of ink. UV ink is composed of resin with unsaturated functional groups, reactive diluent and initiator, pigment and auxiliary agent. It is printed on the base After being placed on the material, when irradiated by ultraviolet light, the initiator cracks to generate active free radicals or cations, which cause the polymerization of unsaturated functional groups to complete the drying process. As a new type of environmentally friendly ink, UV ink has the advantages of energy saving, no solvent emission, no pollution to the environment, high production efficiency, excellent printing performance, and low equipment investment. In the commercial supply market, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/10C09D11/101C09D11/107
Inventor 尹文科
Owner 东莞市佳烨化工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap