Metal antirust paint containing modified pure acrylic emulsion, and its preparation method

A pure acrylic emulsion, metal anti-rust technology, applied in anti-corrosion coatings, coatings, polyester coatings and other directions, can solve the problems of easy cracking or peeling of paint films, endangering health, and increasing construction costs, achieving low cost, The effect of good adhesion, increased corrosion resistance and heat resistance

Inactive Publication Date: 2013-03-20
TONGLING MINGCHENG FOUNDRY
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In recent years, epoxy zinc-rich paint is the most commonly used industrial anti-rust paint to protect metal. Due to the relatively high density of metal zinc powder, in order not to To settle or slow down the settling speed of zinc powder, it is necessary to add a certain amount of anti-settling agent to the paint; the viscosity of the paint will also increase when the anti-settling agent is added. When selecting polyamide resin, it is necessary to choose as small a Molecular weight resin (E44); in order to meet the brushability during construction, a large amount of solvent should be added to the paint. During construction, the solvent seriously endangers the health of workers, and the solvent volatilizes into the air during the drying process to pollute the environment. The construction cost is increased; the brittleness of the paint film after the curing of the small molecular weight resin is large, and the thermal expansion and contraction of the metal is large, and the paint film is easy to crack or fall off when the temperature changes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0014] Example: The metal antirust paint containing modified pure acrylic emulsion, the parts by weight of its raw materials are: ABS resin 28, phenolic resin 20, titanium dioxide 20, silicon acrylic emulsion 10, dodecylamine 1.5, diethanolamine 2.2, polyethylene glycol Acid lactone 18, Tween 80 0.7, 2-n-octyl-4-isothiazolin-3-one 0.4, polydimethylsiloxane 0.3, 2,6-di-tert-butyl-α-dimethylamine Base p-phenol 0.2, modified nano-carbon 1.3, modified pure acrylic emulsion 2, chitosan 0.3, citric acid 0.6, 3-aminopropyltrimethoxysilane 0.8 and hydroxymethyl cellulose 1.2.

[0015] The preparation method of the metal antirust paint containing modified pure acrylic emulsion, comprises the following steps:

[0016] (1) Mix and stir ABS resin, phenolic resin, silicon-acrylic emulsion, titanium dioxide, modified nano-carbon, modified pure acrylic emulsion and chitosan according to the weight of the raw materials, disperse at high speed and grind to a fineness below 35um ;

[0017] (...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a metal antirust paint containing a modified pure acrylic emulsion, and its preparation method. The metal antirust paint comprises the following raw materials, by weight, 25-30 parts of an ABS resin, 17-23 parts of a phenolic resin, 18-22 parts of titanium dioxide, 9-11 parts of a silicone-acrylic emulsion, 1.3-1.8 parts of dodecylamine, 1.5-3.0 parts of diethanolamine, 15-20 parts of polycaprolactone, 0.4-1.0 part of Tween-80, 0.3-0.5 parts of 2-n-octyl-4-isothiazoline-3-one, 0.2-0.4 parts of polydimethylsiloxane, 0.1-0.3 parts of 2,6-di-t-butyl-alpha-dimethylamino-p-phenol, 1.2-1.5 parts of modified nanometer carbon, 1-3 parts of the modified pure acrylic emulsion, 0.2-0.4 parts of chitosan, 0.4-0.8 parts of citric acid, 0.5-1.0 part of 3-aminopropyltrimethoxysilane, and 1.0-1.5 parts of carboxymethyl cellulose. The film of the metal antirust paint has the advantages of good adhesion, fast drying, heat resistance, environmental protection and no pollution, and the modified pure acrylic emulsion and the modified nanometer carbon which are added to the raw materials improve the excellent performances of high-polymer materials in the raw materials and simultaneously increase the corrosion resistance and the heat resistance of the metal antirust paint, and the preparation method has the advantages of simplicity, low cost and suitableness for large-scale production.

Description

technical field [0001] The invention relates to a metal antirust paint containing modified pure acrylic emulsion and a preparation method thereof, belonging to the technical field of antirust materials. Background technique [0002] In recent years, epoxy zinc-rich paint is the most used industrial anti-rust paint to protect metal. Due to the relatively high density of metal zinc powder, in order to prevent the zinc powder from settling or slow down the settling speed of the zinc powder, it is necessary to add A certain amount of anti-settling agent; the viscosity of the paint will also increase when the anti-settling agent is added. When selecting polyamide resin, it is necessary to choose a resin with a small molecular weight (E44) as much as possible; in order to meet the brushability during construction , to add a large amount of solvent to the paint, the solvent seriously endangers the health of workers during construction, the solvent volatilizes into the air during t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D7/12C09D155/02C09D161/06C09D167/04C09D133/04C09D5/08
Inventor 肖颖张蔓青
Owner TONGLING MINGCHENG FOUNDRY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products