Environmental-friendly termite-resistant cable sheath insulating material and method for preparing same

A technology of cable sheathing and insulating materials, applied in the direction of insulated conductors, insulated cables, rubber insulators, etc., can solve compatibility, low temperature resistance, compression set resistance, heat aging performance reduction, low tear resistance, water resistance low shrinkage, excellent physical properties, and good compactness

Inactive Publication Date: 2013-03-27
安徽文峰电子科技集团有限公司
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the increase of chlorine content, the compatibility of plasticizer, low temperature resistance, compression set resistance, thermal aging performance, etc. decrease, and the water resistance is poor. When the temperature is relatively low, the material itself is relatively hard, low in elasticity and brittle. Large, low tear resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmental-friendly termite-resistant cable sheath insulating material and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An environmentally friendly and termite-proof cable sheath insulation material, which is composed of the following raw materials in parts by weight (kg):

[0018] Neoprene CR121 97, chlorinated polyethylene 21, semi-reinforced carbon black N774 22, magnesium oxide 3, glass powder 5, barite powder 35, antioxidant MB 2, N-(β-aminoethyl)-γ- Aminopropyltrimethoxysilane 2, propylene glycol adipate polyester 1.4, dioctyl maleate 5, accelerator DM 2, lead dibasic phosphite 0.8, hydrotalcite 1, 4,4'-oxobis Benzenesulfonyl hydrazide 3, antioxidant DSTP4, glass powder 4, zinc oxide 0.8, modified calcium carbonate 3, antimony trioxide 6, ethylene thiourea 5, modified bentonite 1;

[0019] The preparation method of the modified calcium carbonate is as follows: mix quicklime and boiled water at a mass ratio of 1:10, digest for 5 hours, filter and remove slag through a 180 μm resonance sieve, and then further remove slag through a hydrocyclone to obtain Ca(OH) 2 Suspension, in Ca(O...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environmentally-friendly termite-resistant cable sheath insulating material and a preparation method thereof. The material is prepared from the following raw materials in parts by weight: 90-97 parts of chloroprene rubber (CR) 121, 15-21 parts of chlorinated polyethylene, 15-22 parts of semi-reinforcing purpose furnace black N774, 2-3 parts of magnesium oxide, 2-5 parts of glass powder, 30-35 parts of barite powder, 1-2 of anti-aging agent MB, 1-2 of N-(beta-aminoethyl)-gamma-3-aminopropyltrimethoxysilane, 0.9-1.4 of poly(1, 2-propylene glycol adipate, 5-77 parts of dioctyl maleate, 1-2 parts of accelerator DM, 0.8-1 part of dibasic lead phosphite, 12-18.4 parts of hydrotalcite, 1-3 parts of 4, 4'-oxybis(benzenesulfonyl hydrazide), 2-4 parts of antioxidant DSTP, 4-6 parts of glass powder, 0.8-1 part of zinc oxide, 2-3 parts of modified calcium carbonate, 5-6 parts of antimony oxide, 3-5 parts of ethylene thiourea and 0.8-1 part of modified bentonite. The produced environmentally-friendly termite-resistant cable sheath insulating material has excellent physical performance, stable dimensions and low shrinkage factor, and the tensile strength, tear resistance and elastic force performance of a product are all greatly improved.

Description

technical field [0001] The invention mainly relates to a rubber sheath material and a preparation method thereof, in particular to an environment-friendly termite-proof cable sheath insulation material and a preparation method thereof. Background technique [0002] At present, the main materials commonly used in China as cable sheaths are neoprene, chlorosulfonated polyethylene rubber, etc., and the structural components of each material are different and their properties are also different. Chlorinated polyethylene compound is a kind of saturated chlorine-containing rubber, which partially retains the properties of polyethylene, and its elasticity and thermal stability decrease, and the substance becomes a semi-rigid material and loses its elasticity. With the increase of chlorine content, the compatibility of plasticizer, low temperature resistance, compression set resistance, thermal aging performance, etc. decrease, and the water resistance is poor. When the temperature ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L11/00C08L23/28C08K13/06C08K9/02C08K9/04C08K3/34C08K3/26C08K3/30C08K3/22C08K5/11H01B3/28H01B3/44H01B7/17
Inventor 徐文利
Owner 安徽文峰电子科技集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com