Urea-formaldehyde resin-chloroprene rubber adhesive and preparation method thereof

A chloroprene rubber and urea-formaldehyde resin technology, applied in the directions of adhesives, adhesive additives, polymer adhesive additives, etc., can solve the problems of poor storage stability, poor water resistance, poor heat resistance, etc., and achieves the use effect and The effect of convenience, good environmental protection and excellent heat resistance

Active Publication Date: 2013-06-26
安徽徽邦漆业有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The structure of chloroprene rubber is relatively regular, and there are chlorine atoms with high polarity, so it has high crystallinity. It has good bonding performance and high cohesive strength at room temperature, and is very suitable as an adhesive. The characteristics of neoprene adhesive are: large initial adhesion, high bonding strength, good durability, flexible adhesive layer, good elasticity, impact and vibration resistance, good oil resistance, water resistance, alkali resistance, acid resistance and solvent resistance. , has good adhesion to a variety of materials, easy to use, low price, but poor heat resistance, poor water resistance, poor storage stability
In order to overcome the disadvantages of traditional chloroprene adhesives such as poor heat resistance, poor water resistance, poor storage stability, and high toxicity, a new type of urea-aldehyde resin was produced by improving the formula and adding other raw materials such as urea-aldehyde resin. - Neoprene adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Urea-formaldehyde resin-chloroprene rubber adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0014] A urea-formaldehyde resin-chloroprene rubber adhesive, made of the following raw materials in parts by weight: 105 parts of styrene, 120 parts of ethyl acetate, 25 parts of neoprene CR121, 18 parts of xylene, 4,4'- 1.6 parts of diphenylmethane diisocyanate, 10 parts of polyisobutylene, 2.5 parts of 3-aminopropyltrimethoxysilane, 2 parts of polytetrahydrofuran ether glycol, 18 parts of urea aldehyde resin, 1.8 parts of ferrocene, butyl rubber CBK139 6 parts, 3 parts of epoxy butyl oleate, 4 parts of n-butyl methacrylate, 0.6 parts of sulfur, 1.5 parts of calcium stearate, 1.2 parts of zinc oxide, 1.6 parts of isooctyl tin dimethyldithioglycolate, 12 parts of nano-clay, 24 parts of nano-silica, 1.5 parts of titanate coupling agent TMC-TTS, 2 parts of dicumyl peroxide, 0.8 parts of accelerator CBS, 0.15 parts of accelerator Na-22, anti-aging agent ODA 1.5 parts, anti-aging agent RD 1.5 parts, crosslinking agent TAIC 1.6 parts, modified starch 3 parts.

[0015] Whe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a urea-formaldehyde resin-chloroprene rubber adhesive. The adhesive comprises the following raw materials in parts by weight: 100-120 parts of styrene, 100-150 parts of ethyl acetate, 20-25 parts of chloroprene rubber CR121, 15-20 parts of dimethyl benzene, 1-2 parts of 4, 4'-diphenylmethane diisocyanate, 8-12 parts of polyisobutylene, 2-3 parts of 3-aminopropyltrimethoxysilane, 2-3 parts of polyoxytertramethylene glycol, 15-20 of urea-formaldehyde resin, 1-2 of ferrocene, 5-10 parts of butyl rubber CBK139, 2-4 parts of epoxy n-butyl Oleate and the like. The adhesive has the advantages of excellent heat resistance, water resistance, high adhesive strength, moisture proofness, good storage stability, good environment friendliness, good use effect, convenience and wide application scope; and the adhesive is suitable for adhering artificial leather, synthetic leather, plastics, nylon and organic glass and shoemaking industry.

Description

technical field [0001] The invention relates to a urea-formaldehyde resin-chloroprene rubber adhesive and a preparation method thereof, belonging to the technical field of chemical industry. Background technique [0002] Neoprene is a synthetic rubber compound that is produced in large quantities to make adhesives for a wide range of applications. The structure of chloroprene rubber is relatively regular, and there are chlorine atoms with high polarity, so it has high crystallinity. It has good bonding performance and high cohesive strength at room temperature, and is very suitable as an adhesive. The characteristics of neoprene adhesive are: large initial adhesion, high bonding strength, good durability, flexible adhesive layer, good elasticity, impact and vibration resistance, good oil resistance, water resistance, alkali resistance, acid resistance and solvent resistance. , has good adhesion to a variety of materials, easy to use, and low price, but poor heat resistance,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/06C09J4/02C09J11/04C09J11/06C09J11/08C08B30/18
Inventor 徐冉阳
Owner 安徽徽邦漆业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products