Preparation method of water-based paint from kaolin filler

A technology of water-based paint and kaolin, applied in the direction of coating, etc., can solve the problems of poor decoration and easy cracking, and achieve the effects of overcoming easy cracking, improving early water resistance, and improving film-forming performance

Active Publication Date: 2014-01-08
广东科进应用技术研究有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to overcome the defects of the prior art, and to provide a preparation method for preparing water-based paint by using kaolin filler. The Si-O-Si polymer network structure that can be formed during the process can greatly improve the early water resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1

[0020] The preparation method of ultrafine high-activity kaolin for coating described in Example 1, the preparation steps are:

[0021] A preparation method for preparing water-based paint using kaolin filler includes the following steps:

[0022] (1) Take 800g of kaolin rock ore from the coal mine, crush it with a crusher to form crushed stone ore with a diameter of 20mm, and then remove iron oxide and magnesium oxide minerals from the crushed stone ore through a magnetic separation device to obtain 200 mesh kaolin raw material;

[0023] (2) Dissolve 200g of hexanediol in 500ml of deionized water and stir for 1 hour to form a hexanediol solution; add 500g of 200 mesh kaolin powder to the hexanediol solution, add 50g of dispersant anionic polyfunctional polymerization Alcohol amine salt solution, sodium carboxymethyl cellulose, sodium hexametaphosphate, and then stirred at 80 ℃ for 2.5h, rotating speed 500r / min, uniformly dispersed to obtain a mixed solution; the mi...

Example Embodiment

[0028] Example 2

[0029] The preparation method of the water-based paint prepared by using kaolin filler in the second embodiment includes the following steps:

[0030] (1) Take 800g of kaolin rock ore from the coal mine, crush it with a crusher to form crushed stone ore with a diameter of 20mm, and then remove iron oxide and magnesium oxide minerals from the crushed stone ore through a magnetic separation device to obtain 200 mesh kaolin raw material;

[0031] (2) Dissolve 200g of hexanediol in 500ml of deionized water and stir for 1.5h to form a hexanediol solution; add 500g of 200 mesh kaolin powder to the hexanediol solution, and add 50g of dispersant anionic polyfunctional The mixture of polymer alcohol amine salt solution and sodium carboxymethyl cellulose is then stirred and reacted at 60 ℃ for 1 hour, rotating speed 450r / min, and uniformly dispersed to obtain a mixed solution; after stirring, the mixed solution is separated by centrifugal sedimentation to obtain kaolin fine ...

Example Embodiment

[0036] Example 3

[0037] The method for preparing water-based paint using kaolin filler in Example 3 includes the following steps:

[0038] (1) Take 800g of kaolin rock ore from the coal mine, crush it with a crusher to form crushed stone ore with a diameter of 20mm, and then remove iron oxide and magnesium oxide minerals from the crushed stone ore through a magnetic separation device to obtain 200 mesh kaolin raw material;

[0039] (2) Dissolve 200g of hexanediol in 500ml of deionized water and stir for 1 hour to form a hexanediol solution; add 500g of 200 mesh kaolin powder to the hexanediol solution, add 50g of sodium hexametaphosphate, and then Stir the reaction at 90 ℃ for 3 hours, rotate speed 750r / min, and disperse uniformly to obtain a mixed liquid; after the mixing is finished, the kaolin fine material is obtained by centrifugal sedimentation and separation;

[0040] (3) Measure 100ml of ethyl orthosilicate with 300ml of absolute ethanol and 50ml of hydrochloric acid with a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of water-based paint from kaolin filler. The preparation method is characterized in that alkali metal silicate and small-particle-size silica sol are compounded into an Si-O-Si polymer mesh structure during the film forming process, early water resistance of paint film is improved greatly, and final hardness, scratch resistance and stain resistance in the paint film are improved greatly; organic polymer emulsion is added, film forming property of the paint can be improved, and the defects in the traditional two-component water-based paint such as proneness to cracking, poor decorativeness and poor storage stability are overcome. The paint made by the preparation method has the functions such as environment protection, toxicity resisting, heat insulating, high wash resistance, wear resistance, yellowing resistance, aging resistance, stain resistance, good breathability and acoustic insulation.

Description

technical field [0001] The invention relates to a method for preparing water-based paint by using kaolin filler, in particular to a method for preparing water-based paint capable of improving the functions of the water-based paint such as weather resistance and salt spray resistance. Background technique [0002] For a long time, oil-based paint has occupied an important market in China, and its harmfulness has also been paid attention to in recent years. The solvents used in solvent-based coatings contain harmful substances such as benzene, toluene, and xylene, which seriously damage human health. It is understood that at present, countries are gradually restricting the use of solvent-based coatings (paints), and China is joining the ranks. Water-based coatings have created excellent development space for water-based coatings due to their environmental protection, external climate, consumption habits and other factors. In addition, consumers are increasingly paying more at...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D7/12C09D1/00
Inventor 尹荔松黄韶葵
Owner 广东科进应用技术研究有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap