Preparation method of silicon-nitrogen-boron continuous ceramic fibers

A ceramic fiber, silicon nitrogen boron technology, applied in the chemical characteristics of fibers, chemical post-processing of rayon, rayon of inorganic raw materials, etc., can solve the problems of high cost, complex process equipment environment requirements, etc., to achieve low equipment requirements, manufacturing The effect of low cost and easy process control

Active Publication Date: 2014-07-30
NAT UNIV OF DEFENSE TECH
View PDF10 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in these methods, since the polyborosilazane precursor itself contains a large amount of B-N and Si-N chemical bonds, it is extremely sen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of silicon-nitrogen-boron continuous ceramic fibers
  • Preparation method of silicon-nitrogen-boron continuous ceramic fibers
  • Preparation method of silicon-nitrogen-boron continuous ceramic fibers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] This embodiment includes the following steps:

[0038] (1) Nitriding decarburization: place the obtained infusible PCS fiber in a high-temperature atmosphere furnace, vacuumize and introduce nitrogen into it and repeat it three times. ℃, keep warm for 1h;

[0039] (2) Boronation treatment: evacuate to a furnace pressure of 30Pa, and then introduce a mixture of boron trichloride gas and nitrogen gas, in which BCl is added. 3 The gas volume concentration is 10%, the mixed gas flow rate is 30L / min, and after 3h, the pressure in the furnace is evacuated to 30Pa, then ammonia gas is introduced at 2L / min to quench the excess B-Cl bond, and the reaction is carried out for 1h;

[0040] (3) High temperature sintering: Stop feeding ammonia gas, feed nitrogen gas at a flow rate of 20L / min, continue to heat up to 1300°C at a heating rate of 100°C / hour, and keep heat for 2 hours to obtain silicon-nitrogen-boron continuous ceramic fibers. ​​

[0041] The diameter of the silicon nit...

Embodiment 2

[0043] This embodiment includes the following steps:

[0044] (1) Nitriding decarburization: place the obtained infusible PCS fiber in a high-temperature atmosphere furnace, and after vacuuming, introduce nitrogen and repeat three times, in a mixed gas atmosphere of ammonia and nitrogen, press 100 ℃ / The temperature was raised to 900 °C at a rate of 1 hour, and the nitriding decarburization was carried out, and the temperature was kept for 1 h;

[0045] In the mixture of ammonia and nitrogen, the ammonia volume concentration is 50%;

[0046] (2) Boronation treatment: vacuum until the pressure in the furnace is 28 Pa , and then pass into the mixture of boron trichloride and nitrogen, in the mixture, BCl 3 The gas volume concentration is 25%, the mixed gas flow is 20L / min, after 0.5h, vacuum again The pressure in the furnace is 30Pa , and then pass ammonia gas at 2L / min to quench the excess B-Cl bond, and react for 2h;

[0047] (3) High temperature sintering: stop feeding...

Embodiment 3

[0050] This embodiment includes the following steps:

[0051] (1) Nitriding decarburization: place the obtained infusible PCS fiber in a high-temperature atmosphere furnace, and after vacuuming, feeding nitrogen and repeating it three times, in a mixed atmosphere of ammonia and nitrogen, the temperature is 150℃ / hour. The rate of heating to 800 ℃, nitriding decarburization, holding for 2h;

[0052] In the mixture of ammonia and nitrogen, the ammonia volume concentration is 70%;

[0053] (2) Boronation treatment: vacuuming to The furnace pressure is 28Pa , and then pass into the mixture of boron trichloride and nitrogen, in the mixture, BCl 3 The gas volume concentration is 60%, the flow rate is 10L / min, and the vacuum is evacuated after 1h to furnace pressure 28Pa , then pass high-purity ammonia gas at 5L / min to quench the excess B-Cl bond, and react for 1h;

[0054] (3) High temperature sintering: stop feeding ammonia gas, feed nitrogen gas at a flow rate of 25L / min,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Diameteraaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of silicon-nitrogen-boron continuous ceramic fibers. The method comprises the following steps: (1) nitriding and removing carbon; (2) carrying out boronizing; and (3) firing at high temperature to obtain the silicon-nitrogen-boron continuous ceramic fibers. According to the preparation method, boron is added in silicon nitride fibers to prepare silicon-nitrogen-boron fibers, compared with existing silicon-nitrogen-boron fibers, the preparation method provided by the invention adopts a simple process and is low in manufacturing cost. The preparation method can be implemented by production equipment of silicon nitride fibers and is easy to industrialize.

Description

technical field [0001] The invention belongs to the field of high-performance ceramic materials, and in particular relates to a preparation method of silicon nitrogen boron continuous ceramic fiber. Background technique [0002] Silicon nitride fiber is a high-temperature structural material with excellent performance. It has excellent properties such as high strength, high toughness, high thermal conductivity, high insulation, abrasion resistance, thermal shock resistance, oxidation resistance, low thermal expansion coefficient, and low density. It is mainly used in the preparation of metal matrix and ceramic matrix composite reinforcement materials and heat-resistant functional composite materials. It is one of the ideal materials for aerospace and automotive engine high temperature resistant components. The preparation methods of silicon nitride fibers mainly include: silicon nitride ceramic precursor method and polycarbosilane fiber nitriding method. [0003] The silico...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F9/08D01F11/00C04B35/58C04B35/622
Inventor 邵长伟王军王浩王小宙谢征芳简科
Owner NAT UNIV OF DEFENSE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap