Nickel base porcelain glaze for sintered metal drum and production method thereof

A technology of enamel and gold barrel, applied in the chemical industry, can solve the problems of incompatible expansion coefficient, cold explosion, poor porcelain surface, etc., and achieve the effect of small surface tension, large firing range and good wetting performance

Inactive Publication Date: 2014-09-10
GUIZHOU XINGREN COUNTY RONGKAI HARDWARE ENAMEL PROD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing burnt gold barrels made of enamel formula for forming an underglaze layer on the base metal have poor bonding and adhesion with the metal body, and are not compatible with the expansion coefficient of the metal body, resulting in the porcelain surface after firing. Poor, numbness, scorching spots, and cold bursts often occur, which seriously affect the quality and service life of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A method for producing nickel-bottomed enamel for burning gold barrels, comprising the following steps:

[0019] (1) 21 kg of feldspar, 25 kg of quartz, 28 kg of borax, 8.5 kg of sodium carbonate, 7.5 kg of sodium nitrate, 6.7 kg of fluorite, 1.8 kg of manganese oxide, and 1.5 kg of nickel oxide. or flaky borosilicate glass to obtain nickel-bottomed enamel blocks;

[0020] (2) Based on 100 kg of nickel-bottomed enamel blocks, add 5% quartz, 0.3% borax, 0.3% sodium nitrite, 0.2% sodium carbonate, 0.4% antimony oxide, 0.02% magnesium sulfate, and 6.5% Xuyong porcelain clay ( SiO2 40.00%, Al2O3 36.05%), 48.00% water, 115.00% high alumina balls, mix evenly, and ball mill to form enamel glaze. ;

[0021] When in use, carry out conventional glaze preparation according to the thickness of the steel plate (such as the thickness of the steel plate, the water can be appropriately reduced), so that the glaze can be evenly coated on the entire barrel layer, and then high-temperat...

Embodiment 2

[0024] A method for producing nickel-bottomed enamel for burning gold barrels, comprising the following steps:

[0025] (1) 20 kg of feldspar, 23 kg of quartz, 32 kg of borax, 8 kg of sodium carbonate, 7 kg of sodium nitrate, 6.5 kg of fluorite, 1.5 kg of manganese oxide, and 2 kg of nickel oxide. or flaky borosilicate glass to obtain nickel-bottomed enamel blocks;

[0026] (2) Based on 100 kg of nickel-bottomed enamel blocks, add 5% quartz, 0.3% borax, 0.3% sodium nitrite, 0.2% sodium carbonate, 0.4% antimony oxide, 0.02% magnesium sulfate, and 6.5% Xuyong porcelain clay ( SiO2 40.00%, Al2O3 36.05%), 48.00% water, 115.00% high alumina balls, mix evenly, and ball mill to form enamel glaze. ;

[0027] When in use, carry out conventional glaze preparation according to the thickness of the steel plate (such as the thickness of the steel plate, the water can be appropriately reduced), so that the glaze can be evenly coated on the entire barrel layer, and then high-temperature ca...

Embodiment 3

[0030] A method for producing nickel-bottomed enamel for burning gold barrels, comprising the following steps:

[0031] (1) 22 kg of feldspar, 27 kg of quartz, 24 kg of borax, 9 kg of sodium carbonate, 8 kg of sodium nitrate, 7 kg of fluorite, 2 kg of manganese oxide, and 1 kg of nickel oxide. or flaky borosilicate glass to obtain nickel-bottomed enamel blocks;

[0032] (2) Based on 100 kg of nickel-bottomed enamel blocks, add 5% quartz, 0.3% borax, 0.3% sodium nitrite, 0.2% sodium carbonate, 0.4% antimony oxide, 0.02% magnesium sulfate, and 6.5% Xuyong porcelain clay ( SiO2 40.00%, Al2O3 36.05%), 48.00% water, 115.00% high alumina balls, mix evenly, and ball mill to form enamel glaze. ;

[0033] When in use, carry out conventional glaze preparation according to the thickness of the steel plate (such as the thickness of the steel plate, the water can be appropriately reduced), so that the glaze can be evenly coated on the entire barrel layer, and then high-temperature calcin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses nickel base porcelain glaze for a sintered metal drum and a production method thereof. The nickel base porcelain glaze is prepared from the following raw materials in parts by weight: 20-22 parts of feldspar, 23-27 parts of quartz, 24-32 parts of borax, 8-9 parts of sodium carbonate, 7-8 parts of sodium nitrate, 6.5-7 parts of fluorite, 1.5-2 parts of manganese oxide and 1-2 parts of nickel oxide. The production method comprises the following steps: melting the raw materials at a high temperature according to the formula, and then, rapidly cooling to form granular or flake-like borosilicate glass so as to obtain a nickel base porcelain glaze block; weighted by 100kg of nickel base porcelain glaze block, adding 5% of quartz, 0.3% of borax, 0.3% of sodium nitrite, 0.2% of sodium carbonate, 0.4% of antimony oxide, 0.02% of magnesium sulfate, 6.5% of Xu Yong clay, 48.00% of water and 115.00% of high-aluminum stone balls, uniformly mixing, and carrying out ball milling to obtain the porcelain glaze with the fineness of 80 meshes of a screen. After being sintered, the nickel base porcelain glaze is relatively good in porcelain surface and free of cold explosion.

Description

technical field [0001] The invention belongs to the technical field of chemical industry, and specifically relates to an enamel used for forming an underglaze layer on a base metal, and also relates to a production method of the enamel. Background technique [0002] Burning gold barrel is a kind of enamel barrel with holes in the barrel wall used for offering sacrifices and burning paper money and other sacrificial supplies. The existing production process is divided into blank making and glaze making (including melting glaze blocks and grinding them into glaze powder or glaze pulp), enamelling, firing, flower decoration and other processes. The base glaze is first applied to the pre-stamped or cast metal blank, and the top glaze is applied after firing (once or several times). The bottom glaze is a transitional layer combined with the metal blank. The top glaze is applied on the bottom glaze to cover the bottom color and give the product a smooth and beautiful surface and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/06
Inventor 艾德飞
Owner GUIZHOU XINGREN COUNTY RONGKAI HARDWARE ENAMEL PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com