A kind of low molding temperature water-based polyurethane adhesive and preparation method thereof

A water-based polyurethane, molding temperature technology, applied in the direction of polyurea/polyurethane adhesives, adhesives, polymer adhesive additives, etc., can solve the problems of high energy consumption, high operating temperature, low operating temperature, etc. The effect of tackiness, improving bond strength and reducing loss

Active Publication Date: 2016-01-13
重庆中科力泰高分子材料有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] But at present, in the field of automotive interior adhesives, water-based polyurethane adhesives for automotive roofs have shortcomings such as high operating temperature and high energy consumption, which limit their application. At present, the market urgently needs a product with low operating temperature, high bonding strength, and zero VOC. To meet the development needs of the car roof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low molding temperature water-based polyurethane adhesive and preparation method thereof
  • A kind of low molding temperature water-based polyurethane adhesive and preparation method thereof
  • A kind of low molding temperature water-based polyurethane adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The aqueous polyurethane emulsion of low activation temperature mainly consists of the following components in parts by weight:

[0046] Polyol: phthalic anhydride polyester polyol (PD-56LV): 50 parts, polyoxypropylene glycol (GE-210): 25 parts;

[0047] Diisocyanate: toluene diisocyanate: 20 parts;

[0048] Small molecule alcohol chain extender: diethylene glycol: 1 part;

[0049] Catalyst: organotin dilaurate: 0.01 part;

[0050] Hydrophilic chain extender: sodium ethylenediamine sulfonate: 3.2 parts;

[0051] The preparation method is specifically:

[0052] Dehydrate the polyol in vacuum at 95°C-110°C, under the protection of dry inert gas, cool the dehydrated polyol to 60-70°C, add diisocyanate, react for 0.5-1 hour, add 0.5- Acetone 1.0 times the weight of the prepolymer, reduce the viscosity of the prepolymer, add a small molecule alcohol chain extender and catalyst, keep the temperature at 60-65°C for 2-4 hours, cool down to 45-55°C, add a hydrophilic chain e...

Embodiment 2-5

[0054] In Examples 2-5, the components and parts by weight of the water-based polyurethane emulsion with low activation temperature were added according to the data shown in Table 1, and the preparation method was the same as in Example 1.

[0055] The activation temperatures of the products prepared in Examples 1-5 were detected respectively, and the results are shown in Table 1.

[0056] Activation temperature test method: brush the glue on the medium density board, put it in a constant temperature oven at 60 ℃ and dry it for 2 minutes, take it out and let it air for 2 minutes at room temperature, then stick it with polyvinyl chloride film (PVC), press and stick it on a hot press Molding pressure setting: 0.2 MPa, molding time 30 seconds, molding temperature adjustable, polyvinyl chloride film (PVC) and MDF completely bonded to cause cohesive damage or material damage is regarded as activation, the molding temperature at this time is is the activation temperature.

[0057] ...

Embodiment 6

[0061] The low molding temperature water-based polyurethane adhesive mainly consists of the following components in parts by weight:

[0062] 50 parts of aqueous polyurethane emulsions of the low activation temperature prepared in embodiment 1;

[0063] Aqueous polyurethane dispersion: Bayer U54 (activation temperature at 53±5°C): 25 parts;

[0064] Vinyl acetate-ethylene copolymer emulsion: DA-102: 20 parts;

[0065] Acrylic emulsion: BASF AcronalA420S: 10 parts;

[0066] Tackifying resin: Eastman Tacolyn 3509: 1 part;

[0067] Flame retardant: trimethyl phosphate: 1 part;

[0068] Thickener: BYK420: 0.2 parts.

[0069] The preparation method is specifically:

[0070] At room temperature, stir the vinyl acetate-ethylene copolymer emulsion at a speed of 300-800 rpm, add triethanolamine pH regulator to adjust the pH of the vinyl acetate-ethylene copolymer emulsion to 7.8±1, add water-based polyurethane with low activation temperature Emulsion, polyurethane aqueous dispers...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low molding temperature water-based polyurethane adhesive and a preparation method thereof. The low molding temperature water-based polyurethane adhesive of the present invention is prepared based on a water-based polyurethane emulsion with a low activation temperature and combined with an aqueous polyurethane dispersion, EVA emulsion, and acrylic emulsion. The water-based polyurethane emulsion with a low activation temperature is mainly composed of polyol, Composed of diisocyanate, small molecule alcohol chain extender, catalyst and hydrophilic chain extender, its activation temperature is below 25°C, and the low molding temperature waterborne polyurethane adhesive prepared based on the low activation temperature waterborne polyurethane emulsion has an activation temperature of 30°C -60℃, high bonding strength, water-based emulsion, no organic solvent, 0VOC, green and environmental protection, can well meet the requirements of adhesives for car roofs. The low molding temperature water-based polyurethane adhesive of the present invention can also be used in conjunction with a certain amount of reinforcing agent, which effectively improves the bonding strength of the colloid in the later stage and ensures the heat resistance of the ceiling in the later stage of molding.

Description

technical field [0001] The invention belongs to the field of automobile interior decoration adhesives, and relates to a low-molding-temperature water-based polyurethane adhesive mainly used in automobile ceilings and a preparation method thereof. Background technique [0002] With the development of industry, the application market of adhesives is becoming more and more extensive, and the varieties are also increasing. Adhesives for automotive roofs mainly include two-component solvent-based polyurethane adhesives, two-component solvent-free polyurethane adhesives and hot-melt adhesives. Among them, two-component solvent-based polyurethane adhesives contain a large amount of organic solvents to pollute the environment, and VOC residues in the bonding parts; two-component solvent-free polyurethane adhesives do not contain organic solvents, are green and environmentally friendly, and have high bonding strength, but the viscosity of the colloid is large. Glue is applied by rol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J175/06C09J175/08C09J175/04C09J123/08C09J133/00C09J11/06C09J11/08C08G18/66C08G18/48C08G18/42C08G18/32
Inventor 李有刚冉忠祥徐林蒋乔波
Owner 重庆中科力泰高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More