Modified calcium carbonate with oil-resistant and corrosion-resistant effect and preparation method thereof

An anti-corrosion and calcium carbonate technology, which is applied in the treatment of dyed high-molecular organic compounds, dyed low-molecular organic compounds, fibrous fillers, etc., can solve the problem of affecting the appearance, heat resistance and mechanical properties of materials, and the use of nano calcium carbonate temperature Small window, bubbles and other problems, to achieve the effect of strong binding force, low production cost, and increased dispersion performance

Active Publication Date: 2014-10-01
淮南市精兴生物科技股份有限公司
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the addition of dispersants and surface modifiers greatly reduces the temperature window of nano-calcium carbonate, because commonly used dispersants and coupling agents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified calcium carbonate with oil-resistant and corrosion-resistant effect and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] Specific implementation plan

[0013] The present invention will be described in detail below through specific examples.

[0014] A modified calcium carbonate with oil resistance and corrosion resistance, prepared from the following parts by weight (kg) of raw materials: calcium carbonate 85, hollow microbeads 3, white carbon black 2, coarse aggregate 2, coumarone 3, Fluorine rubber 5, nitrile rubber 4, accelerator Na-220.8, antioxidant DLTP1, polyurethane 5, sepiolite 2, silica 2, modified titanium dioxide 3;

[0015] The modified titanium dioxide is made of the following parts by weight (kg) of raw materials: nano titanium dioxide 50, magnesium hydroxide 2, ethyl cellulose 4, n-butyl acrylate 5, quartz powder 3, polyisobutylene 3, alkyd resin 3 , Terpineol 2, water 50; the preparation method is to first add n-butyl acrylate, nano titanium dioxide, magnesium hydroxide, ethyl cellulose, water and stir evenly to form a suspension, and dry it at 45-50 ℃ to water content 2-3%, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses modified calcium carbonate with an oil-resistant and corrosion-resistant effect. Modified calcium carbonate is characterized in that modified calcium carbonate is prepared from the following raw materials in parts by weight: 85-90 parts of calcium carbonate, 3-5 parts of hollow micro-bead, 2-2.5 parts of white carbon black, 2-3 parts of coarse aggregate, 3-5 parts of coumarone, 5-7 parts of fluororubber, 4-6 parts of butadiene-acrylonitrile rubber, 0.8-1.2 parts of promoter Na-22, 1-2 parts of antioxidant DLTP (dilauryl thiodipropionate), 5-7 parts of polyurethane, 2-4 parts of sepiolite, 2-3 parts of silicon deoxide and 3-4 parts of modified titanium dioxide. High-molecular fluororubber is added to coat the surface of modified calcium carbonate; modified calcium carbonate disclosed by the invention is reasonable in formula, oil-resistant and corrosion-resistant, is assisted by white carbon black so as to increase the oil resistance, is added with an antioxidant component and modified titanium dioxide so as to increase the dispersing performance, and has good flowability and relatively strong binding force; a filling material can be used as an auxiliary agent for plastics, rubber and paper-making; modified calcium carbonate is low in cost.

Description

technical field [0001] The invention relates to the field of industrial fillers, in particular to a modified calcium carbonate with oil-resistant and anti-corrosion effects and a preparation method thereof. Background technique [0002] Calcium carbonate is a very important functional inorganic filler, which is widely used in industrial fields such as plastics, rubber, coatings and papermaking. In the application field of calcium carbonate, most products belong to the category of polymers, such as plastics, rubber, adhesives, coatings, etc., and occupy an important market share. Modifiers play an important role in the performance and application of nano calcium carbonate. For example, the addition of dispersant can reduce the agglomeration of nanoparticles and improve the dispersion; the addition of surface modifier can improve the compatibility of nano-calcium carbonate in the polymer system. It can be seen that dispersants and surface modifiers are crucial for the applic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09C1/02C09C1/36C09C3/10C09C3/08C09C3/04
Inventor 朱蕊许小林
Owner 淮南市精兴生物科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka