Environment-friendly anticorrosive coating and preparation method thereof

An anti-corrosion coating and environment-friendly technology, applied in anti-corrosion coatings, rosin coatings, chemical instruments and methods, etc., can solve the problems of color difference, low efficiency, uneven mixing, etc., and achieve the effect of uniform material, excellent performance and improved efficiency

Active Publication Date: 2014-12-03
ZHANGZHOU XIN ZHAN WANG CHEM IND
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In addition, the existing coatings need to use a variety of raw materials in the preparation process. In the past, various raw materials were poured into a large tank for stirring, and the components were gradually mixed with the stirring, but this method of stirring and mixing There are still uneven mixing and low efficiency, so that there is color difference after the product leaves the factory

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly anticorrosive coating and preparation method thereof
  • Environment-friendly anticorrosive coating and preparation method thereof
  • Environment-friendly anticorrosive coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] The coating formula is: it is obtained by mixing the paint component and the curing agent component in a weight ratio of 100:20;

[0048] Described paint composition comprises following composition and content:

[0049] Acrylic resin 55wt%, tea stalk powder 10wt%, organic amine black 12wt%, rosin 3wt%, butyl ester 15wt%, nonylphenol polyoxyethylene ether 5wt%, butyl ester was separated according to the mass ratio of 8:2. Add 80wt%, plus the remaining 20wt% to adjust the viscosity;

[0050] Described curing agent component comprises following composition and content:

[0051] Aliphatic isocyanate curing agent 69wt%, butyl ester 30wt%, trimethyl orthoformate 1wt%;

[0052] Tea stems are used as raw materials, dried at 90°C until the moisture content is 1%-3%, crushed, and passed through a 300-mesh sieve to obtain tea stem powder.

[0053] The preparation steps of paint components include:

[0054] 1) First add 80wt% butyl ester into the reactor and heat to 40°C;

[005...

Embodiment 2

[0065] The formula composition of the coating is: it is obtained by mixing the paint component and the curing agent component in a weight ratio of 100:30;

[0066] Described paint composition comprises following composition and content:

[0067] Acrylic resin 70wt%, tea stalk powder 5wt%, organic quipeptide ketone 10wt%, rosin 3wt%, cyclohexanone 10wt%, fatty alcohol polyoxyethylene ether 2wt%, cyclohexanone was separated according to the mass ratio of 8:2, and prepared Add 80wt% first, then add the remaining 20wt% to adjust the viscosity;

[0068] Described curing agent component comprises following composition and content:

[0069] Modified cycloaliphatic amine curing agent 60wt%, cyclohexanone 39wt%, trimethyl orthoacetate 1wt%;

[0070] Tea stems are used as raw materials, dried at 120°C until the water content is 1%-3%, crushed, and passed through a 500-mesh sieve to obtain tea stem powder.

[0071] The preparation method is:

[0072] The preparation steps of paint co...

Embodiment 3

[0084] The formula of the coating is: it is obtained by mixing the paint component and the curing agent component in a weight ratio of 100:25;

[0085] Described paint composition comprises following composition and content:

[0086] Acrylic resin 55wt%, tea stalk powder 15wt%, organic bispyrrole and organic perylene millet (3:1 mixture) 15wt%, rosin 3wt%, ethylene glycol butyl ether 10wt%, fatty acid polyoxyethylene ester 2wt%;

[0087] Described curing agent component comprises following composition and content:

[0088] Aliphatic isocyanate curing agent 65wt%, ethylene glycol butyl ether 34.95wt%, 2,2-dimethoxypropane 0.05wt%.

[0089] Tea stems are used as raw materials, dried at 100°C until the water content is 1%-3%, crushed, and passed through a 400-mesh sieve to obtain tea stem powder.

[0090] The preparation method is:

[0091] The preparation steps of paint components include:

[0092] 1) First add 80wt% ethylene glycol butyl ether into the reaction kettle and h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of preparation of coatings and particularly relates to an environment-friendly anticorrosive coating and a preparation method thereof. The coating is prepared by mixing an oil paint component and a curing agent component in a weight ratio of 100 to (20-30). The oil paint component is prepared from the following components in percentage by weight: 55-70wt% of acrylic resin, 5-15wt% of tea stem powder, 10-15wt% of organic pigments, 3-5wt% of rosin, 10-15wt% of solvent and 2-5wt% of surfactant. The curing agent component is prepared from the following components in percentage by weight: 60-69wt% of curing agent, 30-39wt% of solvent and 0.05-1wt% of dehydrating agent, wherein the dehydrating agent is one or two of butyl ester, cyclohexanone and butyl cellosolve. The added tea stem powder can react with harmful gases such as formaldehyde and dimethylbenzene to form non-volatile harmless macromolecular chain substances, so as to effectively eliminate harmful gases in the atmosphere, so that the prepared coating is relatively environmentally friendly and pollution-free. Due to the design of a stepwise feeding device, the raw materials are fully and uniformly mixed, thereby improving the performance of the coating. Due to adoption of a discharging spill-proof hopper, the packaging process is simple, convenient and efficient.

Description

technical field [0001] The invention belongs to the field of paint preparation, and in particular relates to an environment-friendly anticorrosion paint and a preparation method thereof. Background technique [0002] Acrylic resin coating is a type of synthetic resin coating with the most comprehensive performance and the strongest versatility. Compared with other polymer resin coatings, acrylic resin coating has many outstanding advantages, such as its excellent light resistance, weather resistance, and corrosion resistance. , has better resistance to acid, alkali, salt, grease, detergent and other chemicals staining and corrosion performance. Acrylic resin coatings are divided into two types: thermosetting and thermoplastic. Most thermosetting products are synthesized at high temperature, which will produce a large amount of toxic organic gases, which is not in line with the slogan of "low carbon and environmental protection" advocated by the international community, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D193/04C09D7/12C09D5/08B01F13/10
Inventor 张信露谢平展张秋虹
Owner ZHANGZHOU XIN ZHAN WANG CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap