Polishing fluid for machining ultra-smooth bearing steel surface and its application

A technology of polishing liquid and bearing steel, applied in the field of materials, to achieve the effect of reducing defects, low number of defects, and high removal rate

Active Publication Date: 2016-04-20
TSINGHUA UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current technical means are difficult to achieve ultra-smooth bearing steel surface with nano-scale surface roughness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polishing fluid for machining ultra-smooth bearing steel surface and its application
  • Polishing fluid for machining ultra-smooth bearing steel surface and its application
  • Polishing fluid for machining ultra-smooth bearing steel surface and its application

Examples

Experimental program
Comparison scheme
Effect test

experiment example 1

[0045] Polishing liquid formula: 4wt% colloidal silicon dioxide, 0.75wt% glycine, and water as the balance, using nitric acid and potassium hydroxide to adjust the pH value to 2.0-10.0;

[0046] Polishing step: During chemical mechanical polishing, such as figure 1 As shown, the polishing liquid is continuously added to the polishing pad at a certain flow rate, and the sample on the polishing head is in contact with the polishing pad under the applied pressure, and the polishing pad and the sample rotate in the same direction to continuously replenish the polishing liquid to the contact area. The surface material is planarized and removed under the synergistic action of the chemical reaction of the polishing fluid and mechanical grinding, thereby achieving local and global planarization. It is worth noting that the above usage method is based on the traditional polishing machine. For a special polishing machine system, the execution method can be adjusted reasonably according ...

experiment example 2

[0053] Polishing liquid formula: 4wt% colloidal silicon dioxide, 1.05wt% serine or 0.75wt% glycine or 0.9wt% oxalic acid, the balance is water, and the pH value is adjusted to 4.0 with nitric acid and potassium hydroxide;

[0054] Polishing steps: the same as in Experimental Example 1, and the test results are shown in Table 3.

[0055] Table 3 test results

[0056]

[0057] It can be seen that after adding the metal complexing agent, the removal rate of bearing steel material is significantly increased, but the surface quality is deteriorated. By comparison, it was found that after adding aminoacetic acid, the material removal rate of bearing steel increased greatly, and the surface roughness increased the least. Therefore, aminoacetic acid is preferred as the metal complexing agent.

experiment example 3

[0059] Polishing liquid formula: 4wt% colloidal silicon dioxide, 0-1wt% hydrogen peroxide, 0.75wt% glycine, the balance is water, and adjust the pH value to 4.0 with nitric acid and potassium hydroxide;

[0060] Polishing steps: the same as in Experimental Example 1, and the test results are shown in Table 4.

[0061] Table 4 test results

[0062]

[0063] It can be seen that as the mass fraction of hydrogen peroxide increases, the static corrosion rate of bearing steel gradually decreases, the material removal rate first increases sharply and then decreases gradually, and the surface quality gradually improves, indicating that hydrogen peroxide has an important influence on the polishing performance of bearing steel.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
surface roughnessaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polishing solution for processing an ultra-smooth bearing steel surface and application thereof. The polishing solution comprises 0.01-40 wt% of grinding particle, 0-10 wt% of oxidizer, 0.1-10 wt% of metal complexing agent, 0-5 wt% of metal corrosion inhibitor and the balance of water. The grinding particle is selected from at least one of monocrystal diamond, polycrystalline diamond, aluminum oxide, zirconium dioxide, titanium dioxide, cerium oxide, fumed silica and colloidal silicon dioxide; the oxidizer is selected from at least one of periodate, iodate, perchlorate, persulfate and hydrogen peroxide; the metal complexing agent is selected from at least one of ammonia, amino acid and organic acid; and the metal corrosion inhibitor is selected from at least one of nitrogen-containing heterocycle derivatives, sulfur-containing heterocycle derivatives and heterocycle derivatives simultaneously containing nitrogen and sulfur. The bearing steel obtained by using the polishing solution has the functional characteristics of low surface roughness and low number of defects, and thus, can be used in precise devices.

Description

technical field [0001] The invention belongs to the technical field of materials, in particular, the invention relates to a polishing liquid for processing super-smooth bearing steel surfaces and an application thereof. Background technique [0002] Since bearing steel (such as GCr15 bearing steel) has excellent mechanical properties and is relatively easy to produce, it is widely used in the field of machinery manufacturing. The surface quality of bearing steels has a crucial influence on the functional properties of engineering components, such as coefficient of friction and wear resistance. In recent years, there has been an increasing demand from the industry for precision devices using bearing steel as a raw material. In order to achieve satisfactory device functional characteristics, bearing steels are required to have low surface roughness and low number of defects. However, the current technical means are difficult to achieve ultra-smooth bearing steel surface with...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23F3/04C09G1/02
CPCC23F3/04
Inventor 江亮雒建斌何永勇
Owner TSINGHUA UNIV