Stereoscopic colorful auto-bonded macromolecular waterproof roll

A polymer waterproof and color technology, applied in layered products, building components, asphalt layered products, etc., can solve the problems of hard material of polymer waterproof rolls, hidden safety hazards caused by waterproof safety, single construction method, etc. The effect of saving labor cost and equipment cost, preventing water leakage and water channeling, and meeting environmental requirements

Active Publication Date: 2015-02-25
LIAONING DAYU WATERPROOF TECH DEV
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional modified asphalt waterproofing membranes are complicated to construct and require the use of open flames for hot-melt bonding, which produces smoke and exhaust gas, pollutes the environment, and is prone to safety accidents; it cannot be completely bonded to the base layer, and water seepage and channeling often occur phenomenon; in addition, its construction speed is slow, and it is greatly affected by weather changes, base surface flatness and moisture content, and it is easy to delay the construction period
[0004] The traditional polymer waterproof roll has a hard texture, poor construction smoothness, and due to complex equipment, poor passability during the welding process, and high difficulty in waterproof node construction, it is only suitable for large-scale simple waterproof projects.
The traditional polymer waterproof membrane is constructed by wet method, and its construction method is single, and cement slurry is used as the bonding medium for the overlapping edges between materials. At the same time, if it is affected by rainfall during the construction process, the rainwater will dilute the unset cement mortar at the edge of the lap, resulting in failure of the lap joint and complete bonding with the base layer cannot be achieved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A three-dimensional color self-adhesive polymer waterproof membrane, which sequentially includes a film layer, a self-adhesive layer, a carcass layer, a self-adhesive layer and a mineral particle layer, and the carcass layer is made of the following raw materials in parts by weight: 100 parts of polyvinyl chloride resin, 20 parts of polyethylene terephthalate-1,4-cyclohexane dimethanol ester, 15 parts of organic fiber, 4 parts of ABS high-glue powder; Described self-adhesive layer consists of the following Raw materials in parts by weight: 100 parts of modified asphalt, 35 parts of naphthenic oil, 15 parts of styrene-butadiene rubber, 30 parts of styrene-based thermoplastic elastomer, 25 parts of talcum powder, 1.5 parts of antioxidant, and 4 parts of ultraviolet absorber.

[0040] The PE material film of the coating layer, the mineral particle layer is composed of granite and calcite, with a particle size of 0.5-0.8 mm, which can be selected according to different color...

Embodiment 2

[0053] A three-dimensional color self-adhesive polymer waterproof membrane, which sequentially includes a film layer, a self-adhesive layer, a carcass layer, a self-adhesive layer and a mineral particle layer, and the carcass layer is made of the following raw materials in parts by weight: 100 parts of polyvinyl chloride resin, 15 parts of polyethylene terephthalate-1,4-cyclohexane dimethanol ester, 10 parts of organic fiber, 3 parts of ABS high-glue powder; Described self-adhesive layer consists of the following Raw materials in parts by weight: 100 parts of modified asphalt, 30 parts of naphthenic oil, 10 parts of styrene-butadiene rubber, 25 parts of styrene-based thermoplastic elastomer, 20 parts of talcum powder, 1 part of antioxidant, and 3 parts of ultraviolet absorber.

[0054] The coating layer is made of PE material, and the mineral particle layer is granite with a particle size of 0.5-0.8 mm, which can be selected according to the needs of three-dimensional effect; t...

Embodiment 3

[0058] A three-dimensional color self-adhesive polymer waterproof membrane, which sequentially includes a film layer, a self-adhesive layer, a carcass layer, a self-adhesive layer and a colored mineral particle layer, and the carcass layer is made of the following raw materials in parts by weight 100 parts of polyvinyl chloride resin, 25 parts of polyethylene terephthalate-1,4-cyclohexanedimethanol ester, 20 parts of organic fiber, 5 parts of ABS high-glue powder; the self-adhesive layer is composed of Made from the following raw materials in parts by weight: 100 parts of modified asphalt, 40 parts of naphthenic oil, 20 parts of styrene-butadiene rubber, 35 parts of styrene-based thermoplastic elastomer, 30 parts of talcum powder, 2 parts of antioxidant, 5 parts of ultraviolet absorber .

[0059] The coating layer is a PE material film, and the colored mineral particle layer is a mixture of dolomite and calcite, with a particle size of 0.5-0.8mm, which can be selected accordin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a stereoscopic colorful auto-bonded macromolecular waterproof roll. The stereoscopic colorful auto-bonded macromolecular waterproof roll sequentially comprises a membrane layer, a first auto-bonded layer, a core layer, a second auto-bonded layer and a colorful mineral grain layer. The core layer is prepared by 100 parts of polyvinyl chloride resin, 15-25 parts of polyethylene terephthalate-1, 4-cyclohexane dimethanol ester, 10-20 parts of organic fibers and 3-5 parts of ABS high-adhesive powder by weight. Each auto-bonded layer is prepared by 100 parts of modified asphalt, 30-40 parts of naphthenic oil, 10-20 parts of butadiene styrene rubber, 25-35 parts of styrene thermoplastic elastomers, 20-30 parts of talcum powder, 1-2 parts of antioxidant and 3-5 parts of ultraviolet light absorber by weight.

Description

technical field [0001] The invention belongs to the technical field of building waterproofing, and in particular relates to a three-dimensional color self-adhesive polymer waterproofing coiled material. Background technique [0002] Waterproof membrane is mainly used in building walls, roofs, tunnels, roads, landfills, etc., to resist external rainwater and groundwater leakage, a flexible building material product that can be rolled into rolls, as an engineering basis The leak-free connection with the building is the first barrier for the waterproofing of the entire project and plays a vital role in the entire project. The main products are asphalt waterproof membrane and polymer waterproof membrane. [0003] Traditional modified asphalt waterproofing membranes are complicated to construct and require the use of open flames for hot-melt bonding, which produces smoke and exhaust gas, pollutes the environment, and is prone to safety accidents; it cannot be completely bonded t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/14B32B27/40B32B11/04B32B11/12B32B27/30B32B27/36
CPCB32B11/046B32B11/12B32B27/14B32B27/322B32B27/36B32B2260/021B32B2270/00B32B2305/30B32B2307/404B32B2307/73B32B2327/06B32B2367/00B32B2419/06
Inventor 郑宪明王真平王颖
Owner LIAONING DAYU WATERPROOF TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products