Paint composition for solar cell back plate and preparation method thereof

A technology of solar cells and compositions, applied in the directions of coatings, circuits, photovoltaic power generation, etc., can solve problems such as cracking, and achieve the effects of simple production process, easy industrial production, easy transportation and storage

Inactive Publication Date: 2015-03-11
WUXI SUNOCEAN
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Water vapor will attack the underlying PET film through the base resin in the coating and the small cracks in the coating, so that the PET will be degraded and cracked quickly, and this type of backsheet will crack severely during strong humidity and heat aging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A coating composition for a solar battery back sheet of the present embodiment is prepared from the following raw materials in parts by weight: 80 parts of perfluorooctyl ether, 10 parts of methyl methacrylate, 4 parts of Coumaron resin, isopropanol 5 parts of titanium, 13 parts of colloidal silicon dioxide, 5 parts of acrylonitrile, 3 parts of dibutyltin dilaurate, 7 parts of oleic acid, 3 parts of leveling agent, 3 parts of cobalt naphthenate liquid, 2 parts of zirconia, 4 parts of polyvinyl formal, 2 parts of acrylic acid.

[0019] The alkenoic acid is acrylic acid.

[0020] The said leveling agent is propylene glycol methyl ether acetate.

[0021] A coating composition for a solar battery back sheet of the present embodiment comprises the following steps: mixing perfluorooctyl ether, methyl methacrylate, coomalon resin, colloidal silicon dioxide, dibutyl Mix tin laurate and cobalt naphthenate solution, stir and heat to 80-85°C and maintain for 1 hour; then add tit...

Embodiment 2

[0023] A coating composition for a solar battery back sheet of the present embodiment is prepared from the following raw materials in parts by weight: 85 parts of perfluorooctyl ether, 14 parts of methyl methacrylate, 8 parts of Coumaron resin, isopropanol 9 parts of titanium, 17 parts of colloidal silicon dioxide, 9 parts of acrylonitrile, 6 parts of dibutyltin dilaurate, 11 parts of enoic acid, 6 parts of leveling agent, 8 parts of cobalt naphthenate, 5 parts of zirconia, 8 parts of polyvinyl formal, 4 parts of acrylic acid.

[0024] The alkenoic acid is methacrylic acid.

[0025] The said leveling agent is propylene glycol methyl ether acetate.

[0026] A coating composition for a solar battery back sheet of the present embodiment comprises the following steps: mixing perfluorooctyl ether, methyl methacrylate, coomalon resin, colloidal silicon dioxide, dibutyl Mix tin laurate and cobalt naphthenate solution, stir and heat to 80-85°C and maintain for 1 hour; then add titan...

Embodiment 3

[0028] A coating composition for a solar battery back sheet of the present embodiment is prepared from the following raw materials in parts by weight: 82 parts of perfluorooctyl ether, 12 parts of methyl methacrylate, 5 parts of Coumaron resin, isopropanol 6 parts of titanium, 14 parts of colloidal silicon dioxide, 6 parts of acrylonitrile, 4 parts of dibutyltin dilaurate, 8 parts of alkene acid, 4 parts of leveling agent, 4 parts of cobalt naphthenate liquid, 3 parts of zirconia, 5 parts of polyvinyl formal, 3 parts of acrylic acid.

[0029] The enoic acid is undecylenic acid.

[0030] The said leveling agent is propylene glycol methyl ether acetate.

[0031] A coating composition for a solar battery back sheet of the present embodiment comprises the following steps: mixing perfluorooctyl ether, methyl methacrylate, coomalon resin, colloidal silicon dioxide, dibutyl Mix tin laurate and cobalt naphthenate solution, stir and heat to 80-85°C and maintain for 1 hour; then add t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a paint composition for a solar cell back plate and a preparation method thereof. The paint is prepared from the following raw materials in parts by weight: 80-85 parts of perfluorooctyl ether, 10-14 parts of methyl methacrylate, 4-8 parts of coumatone resin, 5-9 parts of titanium propoxide, 13-17 parts of colloid silicon dioxide, 5-9 parts of acrylonitrile, 3-6 parts of dibutyltin dilaurate, 7-11 parts of an olefin acid, 3-6 parts of a levelling agent, 3-8 parts of cobalt naphthenate liquid, 2-5 parts of zirconium oxide, 4-8 parts of poly(vinyl formal), and 2-4 parts of acrylic acid. The paint has good weatherability and steam obstruction property, and also has relatively good wear resistance and adhesive force. The production technology is simple, the production cost is low, and the paint is easy to transport and store, is easy for industrialized production and has market application value.

Description

technical field [0001] The invention relates to a coating composition for a solar battery back plate and a preparation method thereof. Background technique [0002] With the gradual reduction of non-renewable resources and various pollution problems caused by the production and use of mineral resources, countries are using policy and legal means to gradually increase the development and utilization of renewable energy and clean energy, and strive to improve Its share of total energy use. Among these clean and renewable energy sources, solar energy is one of the most important energy sources. Solar photovoltaic power generation is increasingly becoming a part of our lives. The national 12th Five-Year Plan sets the total installed capacity at 15GW in 2015, which indicates that part of our daily electricity consumption will quietly become from solar energy generation. For the photovoltaic power generation industry, it is necessary to reduce costs while continuously improving...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/12C09D7/12C08F220/14C08F220/22C08F220/06C08F220/64H01L31/049
CPCY02E10/50C09D133/12C08F220/14C08F220/06C08F220/44C08F220/64C08L45/02C08L29/14C08K13/02C08K2003/2244C08K5/098C08K3/36
Inventor 黄新东刘天人
Owner WUXI SUNOCEAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products