ZIF-8 material-based hydrogenation catalyst and synthetic method thereof

A technology of ZIF-8 and hydrogenation catalyst, which is applied in the direction of chemical instruments and methods, organic compound/hydride/coordination complex catalyst, physical/chemical process catalyst, etc., to achieve regular shape, simple and efficient synthesis method, metal The effect of high content

Inactive Publication Date: 2015-07-15
BEIJING FORESTRY UNIVERSITY
View PDF10 Cites 42 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the hydrogenation catalyst and its synthesis me

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ZIF-8 material-based hydrogenation catalyst and synthetic method thereof
  • ZIF-8 material-based hydrogenation catalyst and synthetic method thereof
  • ZIF-8 material-based hydrogenation catalyst and synthetic method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of hydrogenation catalyst based on ZIF-8 material of the present invention and synthetic method thereof, specifically comprise the following steps:

[0026] Step 1: Zinc nitrate and 2-methylimidazole are dissolved in methanol, wherein the mass concentration of zinc nitrate is 5%, and the mass concentration of 2-methylimidazole is 5%, the surfactant is dissolved in the above solution, and the configuration A solution with a mass concentration of 2.5% was formed; after stirring and reacting at 20°C for 2 hours, it was allowed to stand for 12 hours to form a white turbid solution.

[0027] Step 2: Centrifuge the turbid solution obtained in Step 1 at a speed of 6000 rpm for 5 minutes; wash the precipitate obtained by centrifugation with methanol for 5 times, then dry the precipitate in an oven for 3 hours at a temperature of 150°C, the ZIF-8 carrier was obtained.

[0028] Step 3: Dissolve the transition metal salt in water and impregnate it on the ZIF-8 carrier desc...

Embodiment 2

[0034] A kind of hydrogenation catalyst based on ZIF-8 material of the present invention and synthetic method thereof, specifically comprise the following steps:

[0035] Step 1: Zinc nitrate and 2-methylimidazole are dissolved in methanol, wherein the mass concentration of zinc nitrate is 8%, and the mass concentration of 2-methylimidazole is 4%, the surfactant is dissolved in the above solution, and the configuration A solution with a mass concentration of 4% was formed; the reaction was stirred at 60°C for 4 hours and then allowed to stand for 18 hours to form a white turbid solution.

[0036] Step 2: Centrifuge the turbid solution obtained in Step 1 at a speed of 5000 rpm for 10 minutes; wash the precipitate obtained by centrifugation with methanol for 3 times, then dry the precipitate in an oven for 1 hour at a temperature of 200°C, the ZIF-8 carrier was obtained.

[0037] Step 3: Dissolve the transition metal salt in water and impregnate it on the ZIF-8 carrier described ...

Embodiment 3

[0043] A kind of hydrogenation catalyst based on ZIF-8 material of the present invention and synthetic method thereof, specifically comprise the following steps:

[0044] Step 1: Zinc nitrate and 2-methylimidazole are dissolved in methanol, wherein the mass concentration of zinc nitrate is 3%, and the mass concentration of 2-methylimidazole is 7%, the surfactant is dissolved in the above solution, and the configuration A solution with a mass concentration of 1% was formed; the reaction was stirred at 30°C for 3 hours and then left to stand for 15 hours to form a white turbid solution.

[0045] Step 2: Centrifuge the turbid solution obtained in Step 1 at a speed of 4000 rpm for 15 minutes; wash the precipitate obtained by centrifugation with methanol 4 times, then dry the precipitate in an oven for 5 hours at a temperature of 100°C, the ZIF-8 carrier was obtained.

[0046] Step 3: Dissolve the transition metal salt in water and impregnate it on the ZIF-8 carrier described in s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to a ZIF-8 material-based hydrogenation catalyst and a synthetic method thereof. The synthetic method particularly comprises the following steps: (1) dissolving zinc nitrate, 2-methylimidazole and a surface active agent with methanol, carrying out stirring reaction for 1-6h at 20-60 DEG C, and standing for 10-18h to obtain a turbid solution; (2) carrying out centrifugal treatment on the turbid solution, placing sediments in a drying oven to be dried to obtain a ZIF-8 carrier after washing with methanol; and (3) dissolving transition metal salt with water, dipping the ZIF-8 carrier into the dissolved transition metal salt, and roasting in a muffle furnace to obtain the ZIF-8 material based hydrogenation catalyst. The hydrogenation catalyst can be used for preparing biodiesel; the biodiesel preparation method comprises the steps of placing the ZIF-8 material based hydrogenation catalyst into a fixed bed reactor to be reduced, and introducing vegetable oil into the reactor for hydrocracking reaction at 300-400 DEG C under the conditions that the hydrogen partial pressure is 2-4MPa, the air speed is 0.9-3.6h<-1> so as to obtain the biodiesel finally. The catalytic efficiency of the synthesized ZIF-8 material based hydrogenation catalyst is improved by dozens of times compared with the catalytic efficiency of a traditional aluminum oxide catalyst.

Description

technical field [0001] The invention relates to a hydrogenation catalyst based on a ZIF-8 material and a synthesis method thereof, belonging to the technical field of catalyst synthesis. Background technique [0002] Zeolitic imidazolate frameworks (Zeolitic Imidazolate Frameworks, ZIFs) materials are a class of metal-organic framework materials that have been studied more in recent years. imidazole, benzimidazole) are connected to form a tetrahedral coordination polymer with a zeolite-like structure. ZIF-8 is the most representative one among ZIFs materials, with high specific surface area, good chemical stability and thermal stability. [0003] As for the synthesis method of ZIF-8, hydrothermal synthesis method and solvent evaporation method are mostly used. For example, in the patent CN103230777A, the inventor injected DMF into the polytetrafluoroethylene lining, added zinc nitrate and 2-methylimidazole to fully dissolve, and then put it into the reactor to carry out th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J31/34C10G3/00
CPCY02P30/20
Inventor 刘静雷建都何静王璐莹邓立红陈盼饶昕李蓉初锦霞陈向丽
Owner BEIJING FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap