Catalytic Luminescent Sensitive Material for Rapid Determination of Formaldehyde and Carbon Monoxide

A carbon monoxide, rapid measurement technology, applied in the field of sensing, can solve the problems of long time-consuming and difficult on-site implementation

Inactive Publication Date: 2017-08-15
BEIJING UNION UNIVERSITY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since these methods require pre-enrichment and sample preparation to complete the determination by analytical instruments, they are time-consuming and difficult to implement on-site

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Add natural flake graphite into concentrated sulfuric acid at a temperature of 0°C under continuous stirring, keep the temperature and stir for 2 hours, then add sodium phosphate equal to the weight of natural flake graphite, and then add solid permanganate 2.2 times the weight of natural flake graphite Potassium, continue to maintain the temperature and stir for 3 hours, raise the temperature to 44°C and continue to stir for 1 hour, add an appropriate amount of hydrogen peroxide with a mass fraction of 5%, raise the temperature to 85°C, keep the temperature and stir for 1 hour, suction filter and wash the filtrate until neutral, Obtain graphene oxide;

[0013] Co-dissolve palladium dichloride, cerium acetate pentahydrate and nickel chloride hexahydrate in an aqueous hydrochloric acid solution with a mass fraction of 10% at a temperature of 35°C, ultrasonically vibrate until clarified, and add appropriate amount of citric acid and sodium citrate under high-speed stirring...

Embodiment 2

[0017] Add natural flake graphite into concentrated sulfuric acid at a temperature of 1°C under continuous stirring, keep the temperature and stir for 2 hours, then add sodium phosphate equal to the weight of natural flake graphite, and then add solid permanganate 2.2 times the weight of natural flake graphite Potassium, continue to maintain the temperature and stir for 3 hours, raise the temperature to 42°C and continue to stir for 2 hours, add an appropriate amount of hydrogen peroxide with a mass fraction of 6%, raise the temperature to 88°C, keep the temperature and stir for 1 hour, suction filter and wash the filtrate until neutral, Obtain graphene oxide;

[0018] Co-dissolve palladium dichloride, cerium oxalate decahydrate, cerium nitrate hexahydrate and nickel bromide trihydrate in an aqueous hydrochloric acid solution with a mass fraction of 8% at a temperature of 31°C, ultrasonically vibrate until clear, and add an appropriate amount of lemon under high-speed stirring ...

Embodiment 3

[0022] Add natural flake graphite to concentrated sulfuric acid at a temperature of 2°C under continuous stirring, keep the temperature and stir for 1.5 hours, then add sodium phosphate equal to the weight of natural flake graphite, and then add solid permanganate 2.2 times the weight of natural flake graphite Potassium, continue to maintain the temperature and stir for 2 hours, raise the temperature to 40°C and continue to stir for 1.5 hours, add an appropriate amount of hydrogen peroxide with a mass fraction of 7%, raise the temperature to 70°C, keep the temperature and stir for 1 hour, suction filter and wash the filtrate until neutral, Obtain graphene oxide;

[0023] Palladium dichloride, ammonium cerium nitrate, cerium sulfate octahydrate and nickel sulfate hexahydrate were co-dissolved in aqueous hydrochloric acid solution with a mass fraction of 6% at a temperature of 33°C, vibrated ultrasonically until clarified, and added appropriate amount of citric acid and Sodium c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

A catalytic and luminescent sensitive material for the rapid determination of formaldehyde and carbon monoxide, which is composed of Pd and CeO supported on graphene 2 and NiO nanocomposite powder material. The preparation method is to add natural flake graphite into concentrated sulfuric acid, after stirring, add sodium phosphate and potassium permanganate, heat up and add hydrogen peroxide, then heat up, stir, suction filter, and wash with water to obtain graphene oxide; palladium dichloride , cerium salt and nickel salt are co-dissolved in hydrochloric acid aqueous solution, add citric acid and sodium citrate, then add graphene oxide, add hydrazine hydrate after stirring, stir, stand still, age, filter, dry, grind, roast to obtain Graphene supported Pd, CeO 2 Composite powder material composed of NiO. The gas sensor for detecting formaldehyde and carbon monoxide made of the sensitive material provided by the invention can quickly and accurately measure trace formaldehyde and carbon monoxide in the air without being interfered by common coexistent substances.

Description

technical field [0001] The invention relates to a catalytic luminescence sensitive material for rapid determination of formaldehyde and carbon monoxide, especially graphene-supported CeO doped with palladium atoms 2 The composite sensitive material composed of NiO and NiO belongs to the field of sensing technology. Background technique [0002] Formaldehyde is a colorless and volatile chemical raw material. It is widely used as an adhesive raw material, disinfectant, preservative and finishing agent in products such as compressed boards, coatings, paints, cosmetics and packaging materials. are continuously released into the air. People have different reactions to various concentrations of formaldehyde in the air: when the concentration of formaldehyde in the air reaches 0.08mg / m 3 Children will have mild asthma when it reaches 0.1mg / m 3 There is a sense of peculiar smell when it reaches 0.6mg / m 3 It can cause throat discomfort or pain when it reaches 1mg / m 3 Sometimes i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N21/76
Inventor 周考文范慧珍张洁
Owner BEIJING UNION UNIVERSITY