Acid and alkali resistance ceramic tile and production method thereof

A ceramic brick, acid and alkali resistance technology, applied in the field of ceramic materials, can solve the problems of poor acid and alkali corrosion resistance, unable to meet market demand, short service life, etc., achieve good temperature resistance, improve chemical stability and acid and alkali resistance Corrosive, long service life effect

Inactive Publication Date: 2015-08-26
安徽省亚欧陶瓷有限责任公司
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ceramic tiles currently on the market have the disadvantages of poor acid a...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] A ceramic tile resistant to acid and alkali corrosion, made of the following weight (kg) raw materials: barite 35, garnet 30, yuhua stone 24, composite clay 14, lithium fluoride 5, micro-silica powder 20, ceramic polishing slag 16 , Zirconium silicon residue 12, gum arabic powder 6, calcium formate 3, coconut acid monoethanolamide 2.5, diethylene glycol 2, sodium polystyrene sulfonate 2.5;

[0019] The preparation method of the composite clay is as follows:

[0020] a. Weigh knives clay, iron bauxite and purple sand mud according to the mass ratio of 5:3:1, mix them evenly, crush them, pass through a 150-mesh sieve, add water and stir to make a slurry with a concentration of 50%, and then add the equivalent weight of the slurry 7% diethanol monoisopropanolamine, 4.5% sodium diisooctyl succinate sulfonate, 3% dodecyl dimethyl betaine, heated in a water bath to 55 ℃, 3500r / min high-speed grinding for 18 minutes, Filter by suction, dry, and set aside;

[0021] b. Weigh 4:2:1 ac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an acid and alkali resistance ceramic tile and a production method thereof. The ceramic tile comprises, by weight, 27 parts to 43 parts of barite, 24 parts to 36 parts of garnet, 17 parts to 29 parts of river stones, 12 parts to 16 parts of compound clay, 4 parts to 7 parts of lithium fluoride, 15 parts to 25 parts of silica fume, 14 parts to 18 parts of ceramic polishing residues, 10 parts to 15 parts of zirconium-containing silica residues, 4 parts to 8 parts of gum acacia powder, 2 parts to 4 parts of calcium formate, 2 parts to 3 parts of coconut oil monoethanolamine, 1.5 parts to 2.5 parts of diethylene glycol, and 2 parts to 3 parts of sodium polystyrene sulfonate. Waste such as ceramic polishing residues and zirconium-containing silica residues are added to the produced ceramic tile, resources can be saved, production cost is reduced, the chemical stability and the acid and alkali resistance of the ceramic tile can be improved, and the ceramic tile can especially tolerate the environment with strong acid or strong base. The ceramic tile is high in strength, good in wear resistance and temperature tolerance, resistant to ageing, long in service life and wide in application range.

Description

Technical field [0001] The invention relates to a ceramic tile resistant to acid and alkali corrosion and a preparation method thereof, belonging to the field of ceramic materials. Background technique [0002] Ceramic bricks are refractory metal oxides and semi-metal oxides, formed by grinding, mixing, pressing, glazing, sintering, etc., a kind of acid and alkali resistant porcelain or stone building or decorative materials , Its raw materials are mostly mixed with clay, quartz sand and other inorganic non-metallic materials. In recent years, with the rapid development of my country's building ceramic industry, people have higher and higher performance requirements for ceramic tiles. The current ceramic tiles on the market have the disadvantage of poor acid and alkali corrosion resistance, short service life, and cannot meet market demand. Summary of the invention [0003] The purpose of the present invention is to provide a ceramic tile resistant to acid and alkali corrosion a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/01C04B35/622B09B3/00
Inventor 徐安辉孔德泽郑辉
Owner 安徽省亚欧陶瓷有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap