Anti-cavitation and abrasion-resistant paint for water pump impellers and preparation method of paint

A wear-resistant coating, water pump impeller technology, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problems of easy agglomeration of nanoparticles and affect the uniform dispersion of epoxy resin, and achieve good leveling and chemical resistance. Good product performance, smooth surface effect

Inactive Publication Date: 2015-09-09
CHANGSHA UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A key problem in the toughening of inorganic nanoparticles is that the nanopartic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] Embodiment 1 Water pump impeller anti-cavitation wear-resistant coating (with primer)

[0059] top coat

[0060] Tetrafluoroethylene-vinyl ether polymer 80kg

[0061] HDI trimer (curing agent) 12kg

[0062] Fluorosilicone coupling agent: 5kg

[0063] Silane coupling agent 2kg

[0064] Silicon carbide 35kg

[0065] Fumed silica 5.33kg

[0066] Nano chromium oxide 2kg

[0067] Nano Zirconia 0.67kg

[0068] Leveling agent BYK-310 (auxiliary) 0.2kg

[0069] Defoamer BYK-A530 (auxiliary) 0.2kg

[0070] Dispersant BYK-163 (auxiliary) 0.2kg

[0071] Anti-sedimentation agent BYK-431 (auxiliary) 0.2kg

[0072] Butyl acetate: MIBK=6:1 (solvent) 65kg

[0073] Dibutyltin dilaurate (catalyst) 0.1kg

[0074] Primer

[0075] E-44 (epoxy resin) 100kg

[0076] Modified amine: polyamide=2:5 (curing agent) 70kg

[0077] KH550 (coupling agent) 1kg

[0078] BK-886 (bentonite) 20kg

[0079] Acetone 60kg

[0080] The preparation method of the coating of embodiment 1 is:...

Embodiment 2

[0089] Embodiment 2 Water pump impeller anti-cavitation wear-resistant coating (with primer)

[0090] Topcoat:

[0091] Tetrafluoroethylene-vinyl ether polymer 200kg

[0092] HDI trimer (curing agent) 35kg

[0093]Fluorosilicone coupling agent: 25kg

[0094] Silane coupling agent 10kg

[0095] Silicon carbide 110

[0096] Fumed silica 16.67kg

[0097] Nano chromium oxide 5.21kg

[0098] Nano Zirconia 2.10kg

[0099] Leveling agent BYK-310 (auxiliary) 0.6kg

[0100] Defoamer BYK-A530 (auxiliary) 0.6kg

[0101] Dispersant BYK-163 (auxiliary) 0.6kg

[0102] Anti-sedimentation agent BYK-431 (auxiliary) 0.6kg

[0103] Butyl acetate: MIBK=6:1 (solvent) 180kg

[0104] Dibutyltin dilaurate (catalyst) 0.5kg

[0105] Primer:

[0106] E-44 (epoxy resin) 250kg

[0107] Modified amine: polyamide=2:5 (curing agent) 100kg

[0108] KH550 (coupling agent) 2kg

[0109] BK-886 (bentonite) 40kg

[0110] Acetone 150kg.

[0111] The preparation method of the coating of embodimen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses anti-cavitation and abrasion-resistant paint for water pump impellers and a preparation method of the paint. The paint comprises the following components in percentage by weight: 35-70% of a tetrafluoroethylene-vinyl ether polymer, 5.5-12% of a curing agent, 2-10% of a silane coupling agent and a fluoroalkyl silane coupling agent, 15-30% of silicon carbide, 1-10% of nano-composite particles, 0.03-3% of additives, 20-40% of methyl isobutyl ketone and butyl acetate, and 0.001-1% of a drying agent, wherein the nano-composite particles are a mixture of chromium sesquioxide, zirconia and gas-phase silicon dioxide; the additives comprise a leveling agent, an antifoaming agent, a dispersing agent and an anti-settling agent. The paint adopts a special paint formula; a coating prepared by utilizing the paint has a flat and smooth surface, and the adhesive force, the film coating rigidity, the waterproof performance, the salt-fog resistance performance and the abrasion resistance performance of the prepared coating reach 0 degree, 9 H, 3000 h, 2500 h and 5 times of 20 carbon steel respectively.

Description

technical field [0001] The invention belongs to the paint industry, in particular to a water pump impeller anti-cavitation wear-resistant paint. Background technique [0002] As a common power machine, water pumps are widely used in electric power, hydraulic and other fields. The stability and working life of water pumps largely depend on the reliability of their blades. The impeller has been subjected to the impact of high-speed airflow and liquid droplets for a long time. Under the joint action of cavitation and fatigue, the entire impeller will be scrapped to a certain extent and needs to be replaced in time. There are two main types of water pump anti-cavitation wear surface protection technology: the use of metal surface protection and coating protection. [0003] The most commonly used metal surface protection layer is electrode surfacing and wire spraying. The surfacing welding method using stainless steel electrodes can ensure a high bonding strength between the we...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D127/18C09D5/08C09D7/12C09D163/00
Inventor 朱志平代陈林银朝晖柳森
Owner CHANGSHA UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap