Whitening agent for ceramic blank body and preparation method thereof
A technology of ceramic body and whitening agent, applied in the field of materials, can solve the problems of not being suitable for daily use ceramics, threats to users' health, and high price, so as to improve whitening effect and antibacterial effect, improve mechanical properties, and improve mechanical properties. performance effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0009] Example 1
[0010] A whitening agent for a ceramic body, comprising the following raw materials by weight: 35 parts of titanium dioxide, 60 parts of aluminum hydroxide, 5 parts of kaolin, 12.5 parts of active silicon powder, 2 parts of zinc nitrate, 3 parts of barium carbonate, talcum powder 2 parts, 4 parts of aluminum oxide, 7 parts of disodium edetate, 9 parts of sodium hexametaphosphate, 2 parts of nickel oxide, 4 parts of lithium borohydride, and 1 part of magnesite.
[0011] The specific preparation method includes the following steps:
[0012] S100: 5 parts of kaolin, 3 parts of barium carbonate, 1 part of magnesite, 60 parts of aluminum hydroxide, 12.5 parts of active silicon powder, 2 parts of talc, and 4 parts of aluminum oxide, add 90 parts of water and grind to a particle size The diameter is 0.5 microns to 1.5 microns to obtain slurry;
[0013] S200: Mix the slurry evenly in the stirring vessel, and after drying, enter the kiln to sinter low-temperature r...
Example Embodiment
[0017] Example 2
[0018] A whitening agent for a ceramic body, comprising the following raw materials by weight: 38 parts of titanium dioxide, 65 parts of aluminum hydroxide, 7 parts of kaolin, 14 parts of active silicon powder, 3 parts of zinc nitrate, 3.5 parts of barium carbonate, talcum powder 3 parts, 6 parts of aluminum oxide, 7.5 parts of disodium EDTA, 9.5 parts of sodium hexametaphosphate, 5 parts of nickel oxide, 5 parts of lithium borohydride, and 4 parts of magnesite.
[0019] The specific preparation method includes the following steps:
[0020] S100: 7 parts of kaolin, 3.5 parts of barium carbonate, 4 parts of magnesite, 65 parts of aluminum hydroxide, 14 parts of active silica powder, 3 parts of talc, and 6 parts of aluminum oxide, add 100 parts of water and grind to a particle size The diameter is 0.5 micron-1.5 micron to obtain slurry;
[0021] S200: Mix the slurry evenly in the stirring vessel, and after drying, enter the kiln to sinter low-temperature raw...
Example Embodiment
[0025] Example 3
[0026] A whitening agent for a ceramic body, comprising the following raw materials by weight: 40 parts of titanium dioxide, 70 parts of aluminum hydroxide, 8 parts of kaolin, 15.5 parts of active silicon micropowder, 4 parts of zinc nitrate, 4 parts of barium carbonate, talcum powder 4 parts, 9 parts of aluminum oxide, 8 parts of disodium edetate, 10 parts of sodium hexametaphosphate, 7 parts of nickel oxide, 7 parts of lithium borohydride, and 6 parts of magnesite.
[0027] The specific preparation method includes the following steps:
[0028] S100: 8 parts of kaolin, 4 parts of barium carbonate, 6 parts of magnesite, 70 parts of aluminum hydroxide, 15.5 parts of active silicon powder, 4 parts of talc, and 9 parts of aluminum oxide, add 110 parts of water and grind to a particle size The diameter is 0.5 micron-1.5 micron to obtain slurry;
[0029] S200: Mix the slurry evenly in the stirring vessel, and after drying, enter the kiln to sinter low-temperatu...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap