Lithium ion battery positive current collector high in safety performance, preparing method thereof and lithium ion battery

A technology for positive current collectors and lithium-ion batteries, applied in the direction of electrode carriers/collectors, battery electrodes, secondary batteries, etc., can solve the problems of small short-circuit resistance, fire and explosion, thermal runaway, etc., to reduce current value and increase resistance , Improve the effect of cycle life

Inactive Publication Date: 2015-10-07
GUANGZHOU GREAT POWER ENERGY & TECH CO LTD
View PDF5 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The resistance of the positive electrode active material diaphragm in ordinary lithium-ion batteries is about 1-2Ω/cm 2 , while the positive electrode aluminum current collector, negative electrode copper current collector and negative electrode active material diaphragm resistance are extremely small. When the battery is subjected to mechanical damage such as severe extrusion, impact or piercing by sharp objects under abnormal conditions, it may cause a short c

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium ion battery positive current collector high in safety performance, preparing method thereof and lithium ion battery
  • Lithium ion battery positive current collector high in safety performance, preparing method thereof and lithium ion battery
  • Lithium ion battery positive current collector high in safety performance, preparing method thereof and lithium ion battery

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0038] Example 1

[0039] Using aluminum foil with a thickness of 25 μm as the base material, the aluminum foil was ultrasonically oscillated in ethanol for 15 minutes to remove the oil stains on the aluminum foil, and then placed in a 0.5 mol / L sodium hydroxide solution for 2 minutes to remove the naturally formed surface of the aluminum foil The oxide layer is then rinsed with distilled water for 15 seconds to obtain a pretreated aluminum foil. The pretreated aluminum foil is used as the anode and the graphite plate is used as the cathode. The voltage is 30 V and the current density is 20 mA / cm in a 0.5 mol / L sulfuric acid aqueous solution. 2 Oxidized for 25 minutes, then rinsed with distilled water for 15 seconds, and dried with hot air at 55 ℃ to obtain aluminum foil coated with a porous alumina resistance layer. The thickness of the porous alumina resistance layer is 75 nm and the blind surface is uniformly distributed. Pore ​​structure (such as figure 1 As shown), the pore...

Example Embodiment

[0045] Example 2

[0046] Using aluminum foil with a thickness of 35μm as the substrate, the aluminum foil is ultrasonically oscillated in acetone for 10 minutes to remove the oil stains on the aluminum foil substrate, and then placed in a 0.25 mol / L potassium hydroxide solution for 1 minute to remove the surface of the aluminum foil. The oxide layer is then rinsed with distilled water for 10 seconds to obtain a pretreated aluminum foil. The pretreated aluminum foil is used as the anode and the graphite plate is used as the cathode. In a mixed aqueous solution of 0.1 mol / L sulfuric acid, 0.05 mol / L phosphoric acid and 0.02 mol / L 2-hydroxypropionic acid, the voltage is 20 V and the current density is 15 mA / cm 2 , Oxidize for 20 minutes, then rinse with distilled water for 15 seconds, blow and dry with hot air at 55 ℃, so as to obtain an aluminum foil positive collector with a porous resistance layer.

[0047] The thickness of the porous alumina resistance layer is 43 nm, and the b...

Example Embodiment

[0050] Example 3

[0051] Using aluminum foil with a thickness of 20 μm as the substrate, the aluminum foil was ultrasonically oscillated in acetone for 10 minutes to remove the oil stains on the aluminum foil substrate, and then mixed with 0.1 mol / L sodium hydroxide and 0.05 mol / L sodium bicarbonate solution Let it stand for 1 minute to remove the oxide layer formed on the surface of the aluminum foil, and then rinse with distilled water for 10 seconds to obtain the pretreated aluminum foil. The pre-treated aluminum foil is used as the anode and the graphite plate is used as the cathode. In a mixed aqueous solution of 0.1 mol / L oxalic acid and 0.02 mol / L 2-hydroxypropionic acid, the voltage is 12 V and the current density is 15 mA / cm 2 , Oxidize for 20 minutes, then rinse with distilled water for 15 seconds, blow and dry with hot air at 55 ℃, so as to obtain an aluminum foil positive collector with a porous resistance layer.

[0052] The thickness of the porous alumina resistance...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Current densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a lithium ion battery positive current collector high in safety performance, a preparing method thereof and a lithium ion battery. The positive current collector comprises an aluminum layer and a porous anodic alumina resistive layer which covers the surface of the aluminum layer. The thickness of the porous anodic alumina resistive layer is 10-100 nm. The porous structure of the porous anodic alumina resistive layer is a blind hole structure. The diameter of blind holes is 0.01-5 microns. The porous anodic alumina resistive layer can effectively increase the resistance of the positive current collector so that the current value generated when a short circuit happens to the battery can be lowered, and accordingly the temperature is decreased when the short circuit happens to the battery and the dangers of firing and exploding caused by heat generated by the battery is avoided. In addition, the adhesive strength of the positive current collector and positive active substances can be improved through the blind hole structure of the positive current collector, so that the probability of falling of the positive active substances during charging and discharging is lowered, and accordingly the cycle life of the lithium ion battery is prolonged.

Description

technical field [0001] The invention relates to the technical field of lithium-ion batteries, and more specifically, relates to a high-safety lithium-ion battery cathode current collector, a preparation method thereof, and a lithium-ion battery. Background technique [0002] Lithium-ion batteries are widely used in various portable electronic products due to their advantages of environmental protection, large capacity, and high volumetric energy density. [0003] The interior of a lithium-ion battery is mainly composed of a positive electrode sheet, a negative electrode sheet, a separator, and an electrolyte. The positive electrode sheet includes a positive electrode collector (aluminum foil) and a positive electrode active material (lithium cobaltate, lithium manganate, etc.), and the negative electrode sheet includes a negative electrode collector ( copper foil) and negative active material (graphite, etc.). The resistance of the positive electrode active material diaphra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/64H01M4/66H01M4/80H01M10/0525
CPCH01M4/64H01M4/667H01M4/80H01M10/0525Y02E60/10
Inventor 杨伟薛建军崔燕胡新发邝子朋夏信德
Owner GUANGZHOU GREAT POWER ENERGY & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap