Putty powder for wooden furniture

A technology for wood furniture and putty powder, applied in the direction of filling slurry, etc., can solve problems such as affecting people's health, high total organic volatile matter, environmental pollution, etc. strong effect

Inactive Publication Date: 2015-11-11
DRAGON FISH PAINT
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the traditional materials used to protect wooden furniture are generally wood lacquers. Wood lacquers are generally divided into solvent-based wood lacquers and water-based wood lacquers. Solvent-based wood lacquers are generally based on polyurethane and The total amount of volatile matter is high, causing pollution to the environment and affecting people's health, so the consumption is declining year by year, while water-based wood lacquers do not pollute the environment, and most of them mainly play a protective role. Defects cannot be filled

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The wood furniture putty powder uses the following raw materials:

[0019] The parts by weight of the raw materials are: 20 parts of heavy calcium carbonate, 50 parts of modified talcum powder, 5 parts of dihydrate silicon dioxide powder, 5 parts of nano-zinc oxide, 10 parts of japonica rice gel powder, 5 parts of paraffin, hydroxypropyl 1.0 part of methyl cellulose, 0.1 part of magnesium aluminum silicate, 0.5 part of pigment;

[0020] Its preparation method is: add modified talcum powder, heavy calcium carbonate, dihydrate silicon dioxide powder and nano-zinc oxide into the mixer, stir for 20 minutes and mix well, then add hydroxypropyl methylcellulose cellulose, silicon Magnesium aluminum phosphate, japonica rice gel powder, paraffin wax and pigments are put into the blender, and continue to stir for 10 minutes to make it fully mixed, and the product is ready;

[0021] Wherein, the fineness particle diameter of the modified talcum powder is 600 meshes; the particle ...

Embodiment 2

[0024] The wood furniture putty powder uses the following raw materials:

[0025] 40 parts of heavy calcium carbonate, 30 parts of modified talc powder, 10 parts of dihydrate silicon dioxide powder, 10 parts of nano-zinc oxide, 7 parts of japonica rice gel powder, 2 parts of paraffin wax, 0.8 parts of hydroxypropyl methylcellulose cellulose part, 0.7 part of magnesium aluminum silicate, and 1 part of pigment;

[0026] Its preparation method is identical with embodiment 1;

[0027] Wherein, the fineness particle diameter of the modified talcum powder is 800 meshes; the particle diameter range of the nano-zinc oxide is 40 nanometers, the specific surface area is 51.5 square meters per gram, and the viscosity of the hydroxypropyl methylcellulose is 51,000 mPa sec; the fineness particle diameter of the japonica rice gel powder is 800 mesh;

[0028] After testing, the wooden furniture putty powder prepared in this example was placed in an environment with a temperature of 40°C an...

Embodiment 3

[0030] The wood furniture putty powder uses the following raw materials:

[0031] 30 parts of heavy calcium carbonate, 40 parts of modified talc powder, 7 parts of dihydrate silicon dioxide powder, 7 parts of nano-zinc oxide, 8 parts of japonica rice gel powder, 3 parts of paraffin wax, 0.5 parts of hydroxypropyl methylcellulose cellulose 0.5 part, 0.5 part of magnesium aluminum silicate, 0.5 part of pigment;

[0032] Its preparation method is identical with embodiment 1;

[0033] Wherein, the fineness particle diameter of the modified talcum powder is 700 mesh; the particle diameter range of the nano-zinc oxide is 40 nanometers, the specific surface area is 51.5 square meters per gram, and the viscosity of the hydroxypropyl methylcellulose is 52,000 millipascal second; the fineness particle diameter of described japonica rice gel powder is 700 orders;

[0034] After testing, the wooden furniture putty powder prepared in this example was placed in an environment with a tempe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses putty powder for wooden furniture, and relates to the technical field of paint. The putty powder is prepared from the following components in parts by weight: 20-40 parts of ground calcium carbonate, 30-50 parts of modified talcum powder, 5-10 parts of silicon dioxide dihydrate powder, 5-10 parts of nano-zinc oxide, 5-10 parts of japonica rice gel powder, 2-5 parts of paraffin, 0.5-1.0 part of hydroxypropyl methyl cellulose, 0.1-0.7 part of magnesium aluminum silicate and 0.5-1 part of pigment. Compared with the prior art, the putty powder has the following advantages: silicon dioxide dihydrate powder is adopted, so that the filling power of the putty powder is greatly strengthened, the uneven surface of the wooden furniture is filled, and the brightness and exquisite property of wall surface are improved; japonica rice gel powder is added, so that the putty powder is strong in binding property, and peeling and checking phenomena of wooden surface are avoided after the wooden furniture is affected by water and damp.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a wooden furniture putty powder. Background technique [0002] At present, the traditional materials used to protect wooden furniture are generally wood lacquers. Wood lacquers are generally divided into solvent-based wood lacquers and water-based wood lacquers. Solvent-based wood lacquers are generally based on polyurethane and The total amount of volatile matter is high, causing pollution to the environment and affecting people's health, so the consumption is declining year by year, while water-based wood lacquers do not pollute the environment, and most of them mainly play a protective role. Defects cannot be filled. Contents of the invention [0003] The problem to be solved by the present invention is to provide a wooden furniture putty powder that can not only protect wooden furniture but also fill up the uneven surface on the wooden furniture. [0004] In order to sol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
Inventor 韦光南
Owner DRAGON FISH PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com