Bright warm-keeping lightness type fibers and preparation method thereof

A light and bright technology, applied in fiber processing, filament/thread forming, chemical post-treatment of synthetic polymer artificial filament, etc., can solve the problems of increased difficulty in quality control, prone to static electricity and hair, loops, etc., to achieve Lightweight, soft touch, and increased air permeability

Active Publication Date: 2015-11-18
JIANGSU HENGKE ADVANCED MATERIALS CO LTD
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Because bright special-shaped yarn does not contain TiO2 particles and has an irregular cross-section, it is prone to static electricity and hair and loops, and the difficulty of quality control is greatly increased.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bright warm-keeping lightness type fibers and preparation method thereof
  • Bright warm-keeping lightness type fibers and preparation method thereof
  • Bright warm-keeping lightness type fibers and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] A method for preparing bright, warm and lightweight fibers. Firstly, an oiling oil is prepared. The specific preparation steps are as follows: blend the initiator butanol and strong alkali potassium hydroxide, then raise the temperature to 105°C, and then add and mix evenly The amount of ethylene oxide, [(1,1,2,2-tetrafluoroethoxy) methyl] ethylene oxide and propylene oxide, the amount of butanol is ethylene oxide, [(1,1, 2,2-tetrafluoroethoxy) methyl] 1‰ of the total mass of ethylene oxide and propylene oxide, the amount of strong base potassium hydroxide is ethylene oxide, [(1,1,2,2- 1‰ of the total mass of tetrafluoroethoxy)methyl]oxirane and propylene oxide, ethylene oxide, [(1,1,2,2-tetrafluoroethoxy)methyl]oxirane The molar ratio of alkanes and propylene oxide is 10:1:20, the polymerization reaction is carried out under the protective atmosphere of nitrogen atmosphere, the reaction pressure is 0.4MPa, and after the relative molecular weight is 1000, the fluorine-c...

Embodiment 2

[0066] A method for preparing bright, warm and lightweight fibers. Firstly, an oiling oil is prepared. The specific steps are: blend the initiator butanol and strong alkali sodium hydroxide, then raise the temperature to 125°C, and then add the evenly mixed ring Ethylene oxide, [(1,1,2,2-tetrafluoroethoxy)methyl]oxirane and propylene oxide, the amount of butanol is ethylene oxide, [(1,1,2, 2-tetrafluoroethoxy) methyl] 5‰ of the total mass of ethylene oxide and propylene oxide, the amount of strong alkali sodium hydroxide is ethylene oxide, [(1,1,2,2-tetrafluoro 5‰ of the total mass of ethoxy)methyl]oxirane and propylene oxide, ethylene oxide, [(1,1,2,2-tetrafluoroethoxy)methyl]oxirane and The amount of propylene oxide is 20:3:30 in molar ratio, the polymerization reaction is carried out under the protective atmosphere of inert gas atmosphere, the reaction pressure is 0.5MPa, and after the relative molecular weight is 4000, neutralization, adsorption, vacuum dehydration and dry...

Embodiment 3

[0080] A method for preparing bright, warm and lightweight fibers. Firstly, an oiling oil is prepared. The specific steps are as follows: blend the initiator butanol and strong alkali sodium hydroxide, then raise the temperature to 115°C, and then add evenly mixed ring Ethylene oxide, [(1,1,2,2-tetrafluoroethoxy)methyl]oxirane and propylene oxide, the amount of butanol is ethylene oxide, [(1,1,2, 2-tetrafluoroethoxy) methyl] 2‰ of the total mass of ethylene oxide and propylene oxide, the amount of strong alkali sodium hydroxide is ethylene oxide, [(1,1,2,2-tetrafluoro Ethoxy) methyl] 1.5‰ of the total mass of ethylene oxide and propylene oxide, ethylene oxide, [(1,1,2,2-tetrafluoroethoxy) methyl] oxirane and The amount of propylene oxide is 12:1:30 by molar ratio, the polymerization reaction is carried out under the protective atmosphere of an inert gas atmosphere, the reaction pressure is 0.8MPa, and after reaching a relative molecular weight of 3000, neutralization, adsorpti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Breaking strengthaaaaaaaaaa
Monofilament denieraaaaaaaaaa
Breaking strengthaaaaaaaaaa
Login to View More

Abstract

The present invention relates to bright warm-keeping lightness type fibers and a preparation method thereof, wherein mainly a polyester is subjected to special-shaped spinning hole melt spinning, oil agent feeding and winding so as to prepare the bright warm-keeping lightness type fibers, wherein the oil agent at least comprises a fluorine-containing polyether, the mass of the fluorine-containing polyether is more than or equal to 45% of the mass of the oil agent, the fluorine-containing polyether is a random copolymer of ethylene oxide, [(1,1,2,2-tetrafluoroethoxy)methyl]ethylene oxide and propylene oxide, and the structure formula is defined in the specification. The preparation method comprises: metering a polyester, extruding, cooling, oiling, stretching, carrying out thermal shaping, and winding so as to prepare the bright warm-keeping lightness type fibers. According to the bright warm-keeping lightness type fibers of the present invention, the fiber cross section shape is changed by the spinning while the fibers have the hollowness, the air permeability and the thermal insulation property are increased, and with the special cross section shape of the fibers, the bright surface light refraction effect is provided so as to make the fabric bright and gorgeous; and the fibers further have characteristics of lightness, light weight, and soft touch feeling.

Description

technical field [0001] The invention relates to a bright, warm and light fiber and a preparation method thereof. Background technique [0002] Since its appearance, polyethylene terephthalate (PET) fiber has developed rapidly because of its excellent performance, and its output has become the crown of synthetic fibers in the world. Polyester fiber has a series of excellent properties such as high breaking strength and elastic modulus, moderate resilience, excellent heat setting, good heat resistance and light resistance, acid resistance, alkali resistance and corrosion resistance, and the fabric has the advantages of wrinkle resistance and good stiffness, so , Polyester fibers are widely used in clothing, home textiles and other fields. [0003] A bright, warm and light fiber, which is a bright special-shaped yarn, changes the cross-sectional shape of the fiber through spinning, and at the same time makes the fiber hollow to increase air permeability and thermal insulation....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F11/08D01D5/096D01D5/253D01D5/088C08G65/28
Inventor 韦开顺柴森光王峰
Owner JIANGSU HENGKE ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com