Metal/graphene composite material and preparation method thereof

A composite material and graphene technology, applied in coatings and other directions, can solve problems such as environmental pollution, long production cycle, and interface impact, and achieve the effects of avoiding energy waste and environmental pollution, high production efficiency, and optimized performance

Active Publication Date: 2016-01-06
SHANDONG UNIV
View PDF10 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The technical solution provided by this patent includes multiple washing and drying steps and a reduction process under a special atmosphere. The production cycle is long, and a variety of reducing agents are mentioned in the solution, which will cause environmental pollution and the steps are cumbersome
In addition, the necessary steps of the patent’s technical solution include coating a layer of polymer film on

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal/graphene composite material and preparation method thereof
  • Metal/graphene composite material and preparation method thereof
  • Metal/graphene composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The present embodiment relates to the preparation method of graphene / aluminum composite material, and described method comprises the steps:

[0041] Step 1: preparing a graphene oxide solution: preparing a graphene oxide aqueous solution by an improved Hummers method, and adjusting the concentration of the graphene oxide aqueous solution to 0.2 mg / ml by adding deionized water.

[0042] Step 2: adjust the pH value of the graphene oxide aqueous solution: take 25ml of the graphene oxide solution described in step 1, and adjust the pH of the solution to 4 by adding 0.1mol / L dilute hydrochloric acid or 0.1mol / L NaOH solution.

[0043] Step 3: At room temperature, take 1 g of aluminum powder with a particle size of 20 μm and add it to the graphene oxide aqueous solution with a pH of 4 as described in step 2. The aluminum particles and graphene oxide are fully mixed and reacted by magnetic stirring. The reaction time is 24 hours A uniformly dispersed graphene / aluminum particle...

Embodiment 2

[0047] The present embodiment relates to the preparation method of graphene / iron composite material, and described method comprises the steps:

[0048] Step 1: preparing a graphene oxide solution: prepare a graphene oxide aqueous solution by an improved Hummers method, and adjust the concentration of the graphene oxide aqueous solution to 0.5 mg / ml by adding deionized water.

[0049] Step 2: adjust the pH value of the graphene oxide aqueous solution: take 50 ml of the graphene oxide solution described in step 1, and adjust the pH of the solution to 5 by adding 0.1 mol / L dilute hydrochloric acid.

[0050] Step 3: At room temperature, take 1 g of iron powder with a particle size of 15 μm and add it to the graphene oxide aqueous solution with a pH of 5 as described in step 2. The iron particles and graphene oxide are fully mixed and reacted by magnetic stirring, and the reaction time is 0.5 h, A uniformly dispersed graphene / iron particle mixture obtained by in-situ reduction of g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a metal/graphene composite material and a preparation method thereof. The metal/graphene composite material comprises metal particles and graphene; the metal particles are uniformly clad with the graphene; the mass ratio of the metal to the graphene is 1:(0.005-0.1); and the graphene is reduced graphene oxide which has an atom-laminated structure and is obtained through in-situ reduction of graphene oxide on the surfaces of the metal particles. Compared with a traditional preparation method, the preparation method disclosed by the invention has the advantages that the processes of metal melting, activating and the like are not performed, so that the preparation procedure of the composite material is greatly simplified; energy waste and environment pollution are avoided; and the metal/graphene composite material which is higher in dispersity and better in property is obtained.

Description

technical field [0001] The invention relates to the field of composite materials, in particular to a metal / graphene material and a preparation method thereof. Background technique [0002] Graphene is made of sp 2 The two-dimensional honeycomb crystal composed of hybrid carbon atoms is simply a single-layer graphite sheet, which is only one carbon atom thick. The basic structural unit is a benzene six-membered ring, and the carbon-carbon bond length is about 0.142nm. The structure of graphene is very stable, and the connection between carbon atoms is very flexible. When the carbon atom plane is subjected to external force, it can bend and deform to ensure the stability of its own structure. Graphene is the thinnest two-dimensional material found so far, with a thickness of only 0.34nm. The unique structure of graphene makes it have many excellent characteristics, such as: mechanical, optical, electrical, thermal and other physical and chemical properties, and also has a hu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F1/02B22F3/02
Inventor 慈立杰侯广梅翟伟艾青
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap