A kind of polybutylene succinate 3D printing wire material and preparation method thereof

A technology of printing wire and formula, applied in the field of 3D printing wire and its preparation, can solve the problems of operator burns, incompatibility, phase separation, etc., and achieve the effects of reducing burns, good biocompatibility, and increasing crystallization temperature

Active Publication Date: 2017-12-29
FUJIAN NORMAL UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese Patent Application Publication No. CN103665802A discloses a method for modifying PLA materials that can be used for 3D printing. The method utilizes inorganic nanomaterials as toughening agents to toughen and modify PLA. Although this method can improve the toughness of PLA, it does not The heat resistance of PLA did not improve significantly
Chinese Patent Application Publication No. CN104530669A discloses a modified polylactic acid PLA material that can be used for 3D printing and its preparation method. The method utilizes polybutylene succinate as a toughening agent to toughen and modify PLA. Although the method can improve the toughness of PLA, since the modified wire is a two-phase system of PLA and PBS, the tensile strength of the modified PLA is not high, and it is easy to cause phase separation during the printing process, making the printing effect poor.
[0005] In addition, when PLA is used for 3D printing, the temperature of the nozzle is generally around 230°C, and the energy consumption is high, which may easily cause burns to the operator, and is not suitable for 3D printers for children.
Chinese Patent Application Publication No. CN103980682A discloses a 3D printing polycaprolactone material and its preparation method. The method uses carbon nanotubes and graphene as dimension reinforcement materials to prepare modified polycaprolactone 3D with high strength. Printing materials, although polycaprolactone has a melting point of 63°C, it can be used as a wire for children's 3D printers, but its heat resistance is poor, and its application range is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polybutylene succinate 3D printing wire material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A PBS 3D printing filament:

[0044] (1) Formula by mass ratio:

[0045] PBS 100

[0046] Talc powder 0.5

[0047] Tea polyphenols 0.6

[0048] UV531 0.5

[0049] stearic acid 1

[0050] (2) Its preparation method:

[0051] A. Dry the PBS in a vacuum oven at 80°C for 12 hours;

[0052] B. According to the formula by weight, take the dried PBS, talcum powder, tea polyphenols, UV531 and stearic acid;

[0053] C. Place the weighed components in a high-speed kneader, keep the speed at 2000 rpm / min, and stir at high speed for 7 minutes;

[0054] D. PBS, talcum powder, tea polyphenols, UV531 and stearic acid that will be mixed uniformly are added to the single-screw extruder feed port of the extrusion platform of Hapu torque rheometer, and the single-screw extruder parameter is : Zone 1 is 75°C, Zone 2 is 110°C, Zone 3 is 120°C, Zone 4 is 115°C, and the rotation speed is 10rpm / min;

[0055] E. Cool the PBS wire rod extruded from the die of the extruder through the firs...

Embodiment 2

[0060] A PBS 3D printing filament:

[0061] (1) Formula by mass ratio:

[0062] PBS 100

[0063] Calcium carbonate 0.7

[0064] 1010 0.5

[0065] UV531 0.5

[0066] EBS 1.5

[0067] (2) Its preparation method:

[0068] A. Dry the PBS in a vacuum oven at 80°C for 12 hours;

[0069] B. According to the formula by weight, weigh the dried PBS, calcium carbonate, 1010, UV531 and EBS;

[0070] C. Place the weighed components in a high-speed kneader, keep the speed at 3500 rpm / min, and stir at high speed for 15 minutes;

[0071] D. Add uniformly mixed PBS, calcium carbonate, 1010, UV531 and EBS to the feeding port of the single-screw extruder of the extrusion platform of the Harp Torque Rheometer. The parameters of the single-screw extruder are: 85°C in the first zone , the second zone is 120°C, the third zone is 130°C, the fourth zone is 125°C, and the rotation speed is 30rpm / min;

[0072] E. Cool the PBS wire rod extruded from the die of the extruder through the first wate...

Embodiment 3

[0077] A kind of PBS 3D printing wire rod and preparation method thereof

[0078] (1) Formula by mass ratio:

[0079] PBS 100

[0080] Calcium sulfate whiskers 0.3

[0081] 168 0.5

[0082] UV327 0.5

[0083] Oxidized polyethylene wax 1

[0084] (2) Its preparation method:

[0085] A. Dry the PBS in a vacuum oven at 80°C for 12 hours;

[0086] B. According to the formula by weight, take the dried PBS, calcium sulfate whiskers, 168, UV327 and oxidized polyethylene wax;

[0087] C. Place the weighed components in a high-speed kneader, keep the speed at 5000 rpm / min, and stir at high speed for 10 minutes;

[0088] D. Add uniformly mixed PBS, calcium sulfate whiskers, 168, UV327 and oxidized polyethylene wax to the feed port of the single-screw extruder of the extrusion platform of the Harp Torque Rheometer, and the parameters of the single-screw extruder are : The first zone is 80°C, the second zone is 125°C, the third zone is 140°C, the fourth zone is 135°C, and the spee...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polybutylene succinate 3D printing wire and a preparation method thereof, which relates to a printing material. The purpose of the present invention is to provide a 3D printing polymer material that can be printed at a lower temperature and has better toughness. The technical scheme of the present invention is as follows: 1. According to the mass part ratio, the formula is PBS100, nucleating agent 0.05-2, antioxidant 0.02-2, anti-ultraviolet agent 0.03-2, lubricant 1-2. 2. The preparation method is: (1) Drying; (2) Weighing; (3) High-speed kneading; (4) Melting extrusion; (5) Cooling traction; (6) Coiling. The present invention uses PBS, which is the same complete biodegradable resin as polylactic acid (PLA), as the wire material, which not only has good biodegradability and biocompatibility, but also can be printed at a lower temperature, and the product has good flexibility. sex.

Description

technical field [0001] The invention belongs to the invention and relates to a 3D printing wire and a preparation method thereof. Background technique [0002] 3D printing technology, that is, additive manufacturing technology, together with robotics and artificial intelligence technology, is known as the key technology to promote the third industrial revolution. 3D printing technology is a rapid additive manufacturing technology that generates three-dimensional entities by adding materials layer by layer. Compared with traditional subtractive manufacturing technology, it has the characteristics of low loss, intelligent, precise and efficient product manufacturing. Especially in the field of high-end manufacturing involving complex shapes, 3D printing technology has shown great advantages. [0003] According to the principle of printing technology and the different materials used, 3D printing technology can be divided into laser cladding forming technology (LCF), fusion dep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L29/14C08K13/02C08K3/34C08K3/26C08K13/04C08K7/08C08K3/36C08K3/22C08K5/098C08K3/32B29C47/92B29C47/88B29C47/34B29B13/06B29C48/06B29C48/355B29C48/92
CPCB29C48/06B29C48/919
Inventor 夏新曙陈庆华张颂羔林鸿裕黄宝铨杨松伟
Owner FUJIAN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com