Solar heat absorption coating

A technology of solar heat absorption and coatings, which is applied in the direction of radiation-absorbing coatings, anti-corrosion coatings, fire-resistant coatings, etc., can solve the problems of complex process flow, high cost, and high requirements, and achieve increased pleochroism, reduced preparation costs, and heat resistance. The effect of performance improvement

Inactive Publication Date: 2016-04-13
GUANGXI CHAOXING SOLAR ENERGY TECH
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The current solar heat-absorbing coatings are full of researches specifically aimed at the weather resistance and water resistance of solar energy coatings. Nowadays, nano-materials are used as raw materials for heat-absorbing materials, which can improve the weather resistance and heat-absorbing efficiency of coatings. For example, Chinese patent CN102286243A , but the cost is extremely high; there are also changes in the formulation of pigments to improve the weather resistance of the prepared coatings, such as Chinese patent CN102134428B, but its preparation process is complicated and requires high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solar heat absorption coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of solar heat absorbing paint, raw material is:

[0034] Film-forming agent: modified casein-gelatin 50kg;

[0035] Film-forming aids: ethylene glycol butyl ether 7kg, propylene glycol phenyl ether 3kg;

[0036] Light absorbing agent: 8kg of cobalt blue powder, 12kg of cobalt manganese copper oxide, and 15kg of enamel black are blended into black;

[0037] Solvent: acetic acid 6kg, anhydrous butyl acetate 8kg, glycerol 6kg;

[0038] Auxiliaries are plasticizers, coupling agents, leveling agents, wetting agents and defoamers, wherein,

[0039] Plasticizer: dibutyl phthalate 2kg;

[0040] Coupling agent: silane coupling agent 1kg, titanate coupling agent 2kg;

[0041] Leveling agent: EFKA35702kg, EFKA35801kg for uniform mixing;

[0042] Wetting agent: polysiloxane 2kg;

[0043] Defoamer: polyoxyethylene oxypropylene glycerin 1kg.

[0044] The steps of preparing the solar heat absorbing coating according to the above-mentioned raw materials are as follows:

[...

Embodiment 2

[0048] A kind of solar heat absorbing paint, raw material is:

[0049] Film-forming agent: modified casein-gelatin 100kg;

[0050] Film-forming aids: 8kg ethylene glycol butyl ether, 9kg propylene glycol phenyl ether, 13kg dodecyl alcohol ester;

[0051] Light absorbing agent: 10kg of cobalt blue powder, 20kg of cobalt manganese copper oxide, and 25kg of enamel black are blended into black;

[0052] Solvent: 15kg of glycerol, 15kg of tetrahydrofuran-oxypropylene copolymerized glycol and 25kg of polyurethane polyether polyol;

[0053] Auxiliaries are plasticizers, coupling agents, leveling agents, wetting agents and defoamers, wherein,

[0054] Plasticizer: dibutyl phthalate 3kg;

[0055] Coupling agent: aluminate coupling agent 2kg;

[0056] Leveling agent: YCK-13605kg;

[0057] Wetting agent: polyether modified polydimethylpolysiloxane 2kg;

[0058] Defoamer: polyoxyethylene polyoxypropylene pentaerythritol ether 3kg;

[0059] The steps of preparing the solar heat abso...

Embodiment 3

[0063] A kind of solar heat absorbing paint, raw material is:

[0064] Film-forming agent: modified casein-gelatin 80kg;

[0065] Film-forming aids: propylene glycol phenyl ether 6kg, dodecyl alcohol ester 9kg and dibutyl phthalate 10kg;

[0066] Light absorbing agent: Use 18kg of chromium oxide green powder, 12kg of selenium cadmium sulfide powder, and 20kg of iron oxide red powder to make red;

[0067] Solvent: acetic acid 20kg, and polyurethane polyether polyol 20kg;

[0068] Auxiliaries are plasticizers, coupling agents, leveling agents, wetting agents and defoamers, wherein,

[0069] Plasticizer: dibutyl phthalate 2kg;

[0070] Coupling agent: a mixture of 2 kg of phosphate coupling agent and 2 kg of borate coupling agent;

[0071] Leveling agent: mix BYK-3332kg and TEGOGlide1002kg;

[0072] Wetting agent: polyester modified polydimethylsiloxane 3kg;

[0073] Defoamer: Polyoxypropylene 2kg.

[0074] The steps of preparing the solar heat absorbing coating according ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a coating, in particular to a solar heat absorption coating. The solar heat absorption coating is prepared from, by weight, 50-100 parts of film forming agent, 35-55 parts of light absorption agent, 10-30 parts of film forming assistant, 20-50 parts of solvent and 10-30 parts of assistant. The film forming agent is modified casein-gelatin. The solar heat absorption coating is characterized in that after the light absorption agent, the film forming agent, the solvent and the assistant are evenly dispersed through ball milling, the film forming assistant is added and evenly mixed, and then the solar heat absorption coating can be obtained. The film forming agent can be modified to serve as an important raw material for preparing the coating, the prepared coating has good weather fastness and waterproofness under the outdoor condition, the preparation process is simple and easy to understand, the heat absorption efficiency of the heat absorption coating can be guaranteed, and high promotional value is achieved.

Description

technical field [0001] The invention relates to heat-absorbing materials, in particular to a solar heat-absorbing paint. Background technique [0002] Energy utilization plays a pivotal role in the development of human society, but the excessive development of resources and inefficient resource utilization make human beings face a severe test. As we all know, solar energy is the most abundant and widely available renewable energy, which plays a major role in solving energy crisis and environmental problems. , making it a hot research topic in various countries. Our country is rich in solar energy resources and has broad prospects for solar energy utilization. At present, it is the first user and producer of solar water heaters in the world. [0003] Solar thermal application is one of the simplest, most direct, and most effective ways for human beings to utilize solar energy. However, due to the small and discontinuous energy density of solar energy after reaching the eart...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D151/08C09D5/32C09D5/18C09D5/08C09D7/12C09D7/00C08F289/00C08F220/18
CPCC08F289/00C08L2201/02C08L2201/08C08L2205/03C09D5/08C09D5/18C09D5/32C09D7/20C09D7/61C09D7/63C09D7/65C09D151/08C08L83/04C08L71/02C08K13/02C08K2003/2289C08K5/12C08L83/12C08L83/10C08K2003/2251C08K2003/3027C08K2003/2272C08K2003/3009C08F220/1804
Inventor 陆俊行李正良马昭键陆美玲丘秋燕甘伟平韦福达
Owner GUANGXI CHAOXING SOLAR ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap