Activated rust layer rust converting agent for electric transmission and transformation equipment and preparation method and application of rust converting agent

A technology for power transmission and transformation equipment and rust transfer agent, which is applied in the direction of metal material coating process, etc., can solve the problems of difficult to meet requirements, large damage to iron substrates, harsh use conditions, etc., to improve the quality of surface treatment and reduce surface treatment. Difficulty, the effect of improving the anti-corrosion life

Active Publication Date: 2016-05-04
STATE GRID CORP OF CHINA +2
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there are also some surface treatment reagents on the market, such as rust remover, phosphating solution, passivation solution, etc., the product function is single, the use conditions are harsh, and it is difficult to meet the requirements on site
For example, the existing rust remover is mainly based on strong acid solution, which has a fast rust removal effect, but it does great damage to the iron matrix and is prone to over-corrosion; phosphating solution and passivation solution have higher requirements for surface treatment and are suitable for It is used after large-area sandblasting, which has high requirements on the site and is difficult to apply on site
Moreover, there are many components and complex shapes of power transmission and transformation equipment. New equipment may adopt hot-dip galvanizing, cold-dip galvanizing, electro-galvanizing, and zinc-aluminum alloy coating for anti-corrosion. Allow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Activated rust layer rust converting agent for electric transmission and transformation equipment and preparation method and application of rust converting agent
  • Activated rust layer rust converting agent for electric transmission and transformation equipment and preparation method and application of rust converting agent
  • Activated rust layer rust converting agent for electric transmission and transformation equipment and preparation method and application of rust converting agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] 1. Prepare the materials according to the following mass ratio, and the chemical reagents are analytically pure:

[0057]

[0058] 2. Product preparation:

[0059] Step 1. Mix 12 parts of phosphoric acid with 12 parts of deionized water, wait for cooling, and set aside.

[0060] Step 2. Put 62 parts of deionized water into the beaker first, stir with SWFS-400 laboratory high-speed disperser, set the stirring speed at 600r / min, and mix zinc dihydrogen phosphate and zinc oxide in proportion under stirring , potassium chlorate, sodium molybdate, sodium fluoride, sodium benzoate, citric acid, oxalic acid, thiourea, triethanolamine, and OP-10 were added in sequence, stirred for 30 minutes, then added phosphoric acid prepared in step 1, and continued to stir for 30 minutes. The solution is transparent and free of impurities to obtain the product.

[0061] 3. Performance test:

[0062] The product that makes is carried out performance test, and data is as following table...

Embodiment 2

[0074] Phosphoric acid: 15 parts

[0075] Deionized water: 71 parts

[0076] Others are the same as embodiment one.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an activated rust layer rust converting agent for electric transmission and transformation equipment and a preparation method and application of the rust converting agent and belongs to the technical field of corrosion prevention of special materials. The rust converting agent disclosed by the invention is prepared from the following components in parts by mass: 8-15 parts of phosphoric acid, 1-3 parts of citric acid, 0.5-3 parts of oxalic acid, 0.1-0.5 parts of thiourea, 0.1-0.5 parts of triethanolamine, 1-2 parts of zinc oxide, 5-8 parts of zinc dihydrogen phosphate, 0.1-1 parts of molybdate, 0.1-1 parts of hydrochloride, 0.5-1 parts of emulsifier, 0.5-1 parts of hydrofluoride, 0.5-1 parts of sodium benzoate, and 70-80 parts of deionized water. The components are added to a container according to proportion and mechanically stirred to be uniform, a product can be obtained after the reaction is completed and the solution is transparent and has not impurities, and in use, the rust converting agent can be brushed before a paint is coated. The rust converting agent is reasonable in component design and simple in preparation process, and the obtained rust converting agent has excellent performances, is wide in application scope and is convenient for large-scale production and application.

Description

technical field [0001] The invention relates to an active rust layer rust converter for power transmission and transformation equipment, a preparation method and application thereof, and belongs to the technical field of anticorrosion of special materials. Background technique [0002] Power transmission and transformation equipment is mostly distributed in outdoor environments, and corrosion is very common. Corrosion causes equipment to fail early, causing huge economic losses and waste of resources and energy, and will bring potential safety hazards. Regular inspections of power transmission and transformation equipment in service Anti-corrosion coating to prolong service life. However, the operating environment of anti-corrosion coatings for power transmission and transformation equipment is very harsh. Most of them work in the open air or at high altitudes, surrounded by high-voltage electrical appliances, and the application of electrical and power tools is limited. Hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C22/47C23G1/08
CPCC23C22/47C23G1/088
Inventor 李明陈军君王军刘纯胡波涛欧阳克俭谢亿
Owner STATE GRID CORP OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products