Glass fiber compound surface skin and production method

A composite surface, glass fiber technology, applied in the field of glass fiber composite surface skin and production, can solve the problems of single raw material density, insufficient hardness, etc., and achieve the effect of not easy to be old, high density, easy to process and form

Inactive Publication Date: 2016-06-08
四川省中鑫威格节能科技股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although glass fiber and spunlace non-woven fabrics are relatively mature in construction, they are rarely used in construction skins at present, and even if they are used, they have defects such as density and insufficient hardness due to their relatively simple raw materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass fiber compound surface skin and production method
  • Glass fiber compound surface skin and production method
  • Glass fiber compound surface skin and production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Produce glass fiber composite dough according to the following steps:

[0026] (1) According to the thickness of the carbon fiber composite skin to be produced, prepare one or more pieces of glass fiber cloth, spunlace non-woven fabric made of glass fiber and an appropriate amount of random copolymerized polypropylene and binder, among which, the bonding The mass ratio of agent to random copolymerized polypropylene is 1:6 and the binder includes the following raw materials in parts by mass: 10 parts of phenolic resin, 7 parts of quartz sand, 2 parts of dicyandiamide, 2 parts of dimethylformamide, 1.5 parts of polyacrylate, 3 parts of dipropylene glycol methyl ether, 4 parts of simethicone, 4 parts of fumaric acid, 1.5 parts of fumaric anhydride, 4 parts of trimesic acid, 1.5 parts of trimesic anhydride and anionic surfactant 1.5 parts, the anionic surfactant is the anionic surfactant containing the hydrophobic group shown in the following formula:

[0027]

[0028] ...

Embodiment 2

[0036] Produce glass fiber composite dough according to the following steps:

[0037] (1) According to the thickness of the carbon fiber composite skin to be produced, prepare one or more pieces of glass fiber cloth, spunlace non-woven fabric made of glass fiber and an appropriate amount of random copolymerized polypropylene and binder, among which, the bonding The mass ratio of agent to random copolymerized polypropylene is 1:5 and the binder includes the following raw materials in parts by mass: 10 parts of furan resin, 6 parts of quartz sand, 1 part of dicyandiamide, 1 part of dimethylformamide, 1 part of polyacrylate, 2 parts of dipropylene glycol methyl ether, 3 parts of simethicone, 3 parts of fumaric acid, 1 part of fumaric anhydride, 3 parts of trimesic acid, 1 part of trimesic anhydride and anionic surfactant 1 part, the anionic surfactant is an anionic surfactant containing a hydrophobic group shown in the following formula:

[0038]

[0039] Among them, R 1 is ...

Embodiment 3

[0047] Produce glass fiber composite dough according to the following steps:

[0048](1) According to the thickness of the carbon fiber composite skin to be produced, prepare one or more pieces of glass fiber cloth, spunlace non-woven fabric made of glass fiber and an appropriate amount of random copolymerized polypropylene and binder, among which, the bonding The mass ratio of agent to random copolymerized polypropylene is 1:8 and the binder includes the following raw materials in parts by mass: 10 parts of imide resin, 8 parts of quartz sand, 3 parts of dicyandiamide, 3 parts of dimethylformamide 2 parts, polyacrylate 2 parts, dipropylene glycol methyl ether 4 parts, simethicone 5 parts, fumaric acid 5 parts, fumaric anhydride 2 parts, trimellitic acid 5 parts, trimellitic anhydride 2 parts and anionic surface 2 parts of activator, anionic surfactant is the anionic surfactant containing the hydrophobic group shown in the following formula:

[0049]

[0050] Among them, R...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass fiber compound surface skin which is prepared from glass fabric, spunlace nonwoven fabric, polypropylene randon copolymer and a binding agent. The binding agent is prepared from liquid resin, quartz sand, dicyandiamide, dimethyl formamide, polyacrylic ester, dipropylene glycol monomethyl ether, dimethicone, fumaric acid, fumaric acid anhydride, trimesic acid, trimesic acid anhydride and a negative ion surface active agent. The invention further discloses a production method of the glass fiber compound surface skin. The method includes the following steps of preparing the raw materials, preparing solidification liquid, conducting rolling and thermocuring, conducting quick cooling to form a semi-solidified plate, cutting the semi-solidified plate, and conducting natural cooling to the normal temperature to obtain the glass fiber compound surface skin. The glass fabric and the spunlace nonwoven fabric are used as base materials, polypropylene random copolymer and the binding agent are added, and the produced glass fiber compound surface skin has excellent performance on the aspects of appearance, high compactness, high strength, abrasion resistance, high temperature resistance, corrosion resistance, acid and base resistance and low expansion.

Description

technical field [0001] The invention relates to a building dough and a production method, in particular to a glass fiber composite dough and a production method. Background technique [0002] The building skin is a kind of surface building material pasted on the surface of the concrete structure. Its purpose is to make the concrete surface more beautiful, and it can also bear part of the external load acting on it. [0003] Traditional building skins are mostly made of wood skins, plastic skins, metal skins or composite skins made of these skins. Although they play a corresponding role in aesthetics and load-bearing, traditional skins are wear-resistant, high-temperature resistant, corrosion-resistant, The acid and alkali resistance and low expansion performance are poor, resulting in the single function of the dough and the defects that it is easy to be old and damaged in the later stage. [0004] Glass fiber (original name in English: glassfiber or fiberglass) is an inorg...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/14C08L61/04C08L61/00C08L79/08C08L83/04C08L33/04C08K13/04C08K7/14C08K3/36C08K5/315C08J5/04
CPCC08L23/14C08J5/043C08J2323/14C08L2201/08C08L2205/035C08L61/04C08L83/04C08L33/04C08K13/04C08K7/14C08K3/36C08K5/315C08L61/00C08L79/08
Inventor 刘伟
Owner 四川省中鑫威格节能科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products