Processing technology of insulating thermosetting plastic material

A processing technology and plastic material technology, which is applied in the field of plastic material processing, can solve the problems that thermally conductive plastics cannot meet the requirements, and achieve the effects of improving insulation and corrosion resistance, good flame retardancy, and simple preparation process

Inactive Publication Date: 2016-06-22
FUYANG SIBO IND DESIGN
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, thermally conductive plastics often fail to meet the requirements in terms of other properties, such as flame retardancy, mechanical properties, and high temperature and corrosion resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing technology of insulating thermosetting plastic material
  • Processing technology of insulating thermosetting plastic material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A processing technique for an insulating plastic material, comprising the steps of:

[0018] Step 1) Crushing and grinding: Add dolomite, perlite and sepiolite to the crusher in a mass ratio of 2:1:1 for crushing, and then grind to obtain a powder with a particle size of 200 mesh, which is material A ;

[0019] Step 2) Preparation of modified resin: Add material A, alumina and serine into the mixing tank in sequence, and stir while heating. When heated to 90°C, add methacryloxypropyltrimethoxysilane to maintain Continue stirring at 90°C for 20 minutes; then cool down to 60°C, add polyethylene resin, and stir for 1 hour to obtain material B; wherein, the material A, alumina, serine, methacryloxypropyltrimethoxysilane and The mass ratio of polyethylene resin is 8:2:1:3:86;

[0020] Step 3) Preparation of modified graphite: Put the graphite into a crucible, place it in a muffle furnace for calcination, and under the protection of nitrogen, calcine at 700°C for 3 minutes,...

Embodiment 2

[0025] A processing technique for an insulating plastic material, comprising the steps of:

[0026] Step 1) Crushing and grinding: Add dolomite, perlite and sepiolite to the crusher in a mass ratio of 2:1:1 for crushing, and then grind to obtain a powder with a particle size of 200 mesh, which is material A ;

[0027] Step 2) Preparation of modified resin: Add material A, alumina and serine into the mixing tank in sequence, and stir while heating. When heated to 90°C, add methacryloxypropyltrimethoxysilane to maintain Continue stirring at 90°C for 20 minutes; then cool down to 60°C, add polyethylene resin, and stir for 1 hour to obtain material B; wherein, the material A, alumina, serine, methacryloxypropyltrimethoxysilane and The mass ratio of polyethylene resin is 8:2:1:3:86;

[0028] Step 3) Preparation of modified graphite: put the graphite into a crucible, place it in a muffle furnace for calcination, and under the protection of nitrogen, calcine at 700-800°C for 3 minu...

Embodiment 3

[0033] Plastic material performance test of the present invention:

[0034] The plastic material prepared in embodiment 1-2 is made standard test piece according to test standard, carries out following performance test, and the results are shown in Table 1:

[0035] Table 1

[0036]

[0037] 2. Corrosion resistance test: Take salt solution as an example, soak the test material in 10% sodium chloride solution for 240 hours, and measure the main performance parameters, see Table 2:

[0038] Table 2

[0039] group Flame retardant Thermal conductivity retention rate (%) Tensile strength retention (%) Elongation at break (%) Example 1 V0 99.3 97.2 98.5 Example 2 V0 99.1 96.9 98.8

[0040] 3. High temperature resistance performance test: The performance test of the plastic materials prepared in Examples 1 and 2 under high temperature conditions: the selected temperature is 90°C, and the cable material is placed at this temperature for 240 ho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of thermosetting plastic processing and discloses a processing technology of an insulating thermosetting plastic material. The processing technology comprises the following steps: 1, crushing and grinding raw materials; 2, preparing modified resin; 3, preparing modified graphite; 4, conducting banburying; 5, preparing the thermosetting plastic material. The processing technology is simple in process, great in operability and suitable for industrialized production.

Description

technical field [0001] The invention belongs to the technical field of plastic material processing and discloses a processing technology of insulating plastic material. Background technique [0002] Plastic is mainly composed of carbon, oxygen, hydrogen, nitrogen and other organic or inorganic elements. The finished product is solid, and it is a molten liquid during the manufacturing process. Therefore, it can be melted by machine heating, pressure can be applied to make it flow, and cooling can make it Solidified and formed into various shapes, this large and varied group of materials is called plastics. Plastic parts are widely used in every field of life today, such as household appliances, instruments, wires and cables, construction equipment, communication electronics, automobile industry, aerospace, daily hardware, etc. The main component of plastic raw materials is carbon-containing compounds, which are made of polymer synthetic resin (polymer) as the main component,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/00C08L29/04C08L23/06C08K13/06C08K9/00C08K3/04C08K3/34C08K9/06C08K3/26C08K7/14B29B9/06
CPCB29B9/06C08K2201/011C08K2201/014C08L23/00C08L2201/02C08L2201/08C08L2205/03C08L29/04C08L23/06C08K13/06C08K9/00C08K3/04C08K3/34C08K9/06C08K2003/265C08K2003/267C08K7/14
Inventor 凌泽波
Owner FUYANG SIBO IND DESIGN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com