A kind of carbon-iron-titanium-silicon-aluminum oxide compound and its preparation method and application

A silicon-alumina oxide and composite technology, which is applied in chemical instruments and methods, metal/metal oxide/metal hydroxide catalysts, separation methods, etc. The problems of high carbon yield and large particle size of iron particles have achieved a wide range of industrial application prospects, high-value utilization, and high activated carbon yield.

Active Publication Date: 2018-12-11
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the above-mentioned inventions, the dealkalization or other treatment processes of alkaline compounds in the red mud did not make good use of the iron oxide therein
And using red mud directly as a carbon fiber catalyst, because the raw material contains a large amount of alkaline substances and chlorine elements, and the iron particle size is large, it is difficult to have high activity and high carbon yield for carbon fiber preparation, so it does not have industrial application prospects
Combining the pollution of red mud and the current situation of comprehensive utilization, it is not difficult to find that there is no feasible technology at this stage to realize the high-value utilization methods and approaches of iron in red mud, and the high-value and large-scale application of red mud

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of carbon-iron-titanium-silicon-aluminum oxide compound and its preparation method and application
  • A kind of carbon-iron-titanium-silicon-aluminum oxide compound and its preparation method and application
  • A kind of carbon-iron-titanium-silicon-aluminum oxide compound and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A preparation method of an iron-titanium-silicon-aluminum oxide compound for depositing carbon fibers, comprising the steps of:

[0049] (1) After adding 1 kg of water to 1 kg of red mud, put it into a ball mill tank and mill it for 12 hours, so that the particle size is less than or equal to 100 nm, and obtain the first slurry, the solid content of the first slurry is 30%;

[0050] (2) After 1 kg of dilute nitric acid solution (10% concentration) was added dropwise in the first slurry, the pH value of the solution was about 2, and the system became slurry; the slurry red mud was added dropwise with ammonia water (10% concentration) during the ball milling process. Concentration) 0.5kg, the pH value of the solution is about 6, the silica-alumina sol precipitates again, the viscosity of the system becomes smaller, and the second slurry is obtained;

[0051] (3) After the second slurry is subjected to solid-liquid separation and washing, it is dried at 120°C, and then roa...

Embodiment 2

[0059] A preparation method of an iron-titanium-silicon-aluminum oxide compound for depositing carbon fibers, comprising the steps of:

[0060] (1) After adding 2 kg of water to 1 kg of red mud, put it into a ball mill tank and mill it for 10 hours, so that the particle size is less than or equal to 100 nm, to obtain the first slurry, the solid content of the first slurry is 20%;

[0061] (2) After dripping dilute hydrochloric acid solution (5%) 1kg successively in the first slurry, the solution pH value is about 4, and the system becomes slurry; Slurry red mud is dripped successively sodium hydroxide (10% in ball milling process) % concentration) after 0.5kg, the pH value of the solution is about 6, the silica-alumina sol precipitates again, the viscosity of the system becomes smaller, and the second slurry is obtained;

[0062] (3) After the second slurry is subjected to solid-liquid separation and washing, it is dried at 100° C., and then roasted at 600° C. for 5 hours to o...

Embodiment 3

[0070] A preparation method of an iron-titanium-silicon-aluminum oxide compound for depositing carbon fibers, comprising the steps of:

[0071] (1) After adding 1 kg of water to 1 kg of red mud, add it to a ball mill tank and mill for 24 hours, so that the particle size is less than or equal to 100 nm, and obtain the first slurry, the solid content of the first slurry is 50%;

[0072] (2) After dripping sulfuric acid solution (50%) 0.2kg successively in the first slurry, the pH value of the solution is about 3, and the system becomes slurry; slurry red mud is dripped with sodium carbonate aqueous solution (5 % concentration) after 1kg, the pH value of the solution was about 7, the silica-alumina sol precipitated again, the viscosity of the system became smaller, and the second slurry was obtained;

[0073] (3) After the second slurry is subjected to solid-liquid separation and washing, it is dried at 100°C, and then calcined at 800°C for 3 hours to obtain a solid substance, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
adsorption capacityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
Login to View More

Abstract

The invention provides a carbon-iron titanium silicon-aluminum oxide composite and its preparation method and application. The preparation method of the carbon-iron titanium silicon-aluminum oxide composite includes the following steps: adding water to red mud, and grinding to obtain the third A slurry; add acid to the first slurry to adjust the pH value to 2-4, add a surface dispersant, add alkaline substances under grinding to adjust the pH value to 5-10, and obtain a second slurry; add the second slurry Solid-liquid separation is performed, and the solid is roasted to obtain a coated iron-titanium-silica-aluminum oxide; the coated iron-titanium-silica-aluminum oxide is reduced in a reducing gas atmosphere, and then carbon fibers are generated in a hydrocarbon atmosphere and cooled. Finally, the carbon-iron-titanium-silicon-aluminum oxide composite is obtained. The invention can realize high-value utilization of red mud and has strong industrial application potential.

Description

technical field [0001] The invention belongs to the field of hazardous solid waste treatment and application, and relates to a carbon-iron-titanium-silicon-aluminum oxide compound and its preparation method and application. Background technique [0002] Red mud is the polluting strong alkaline waste slag discharged when the aluminum industry extracts alumina. Generally, for every ton of alumina produced, 1.0 to 2.0 tons of red mud are incidentally produced. A large amount of red mud cannot be fully and effectively utilized, and can only be stacked in a large area of ​​storage yard, which occupies a large amount of land and causes serious pollution to the environment. Most countries have listed red mud as a hazardous waste. The production of red mud has caused direct and indirect impacts on human production and life in many ways. Therefore, the output and hazards of red mud should be minimized to achieve multi-channel, Large quantities of resources are imminent. [0003] Be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/20B01J20/30C02F1/28B01D53/02B01J23/745C02F101/16C02F101/34
CPCB01D53/02B01J20/0211B01J20/0229B01J20/08B01J20/103B01J20/20C02F1/281B01J23/745C02F2101/345C02F2101/16B01D2253/1124B01D2253/102B01D2253/10B01D2253/106B01D2253/104B01D2257/60B01D2257/602B01D2258/0283B01J2220/4887B01J2220/42B01J35/23
Inventor 余剑李长明郭凤崔彦斌
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com