Preparation method for graphene modified anticorrosive paint
A graphene modification and anti-corrosion coating technology, applied in anti-corrosion coatings, polyester coatings, epoxy resin coatings, etc., can solve the problems of low barrier property, short service life, poor weather resistance, etc., to overcome poor weather resistance and extend protection. Time, chemical resistance and strong corrosive effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0029] Example 1
[0030] A preparation method of graphene modified anticorrosive coating includes the following steps:
[0031] (1) Preparation of graphene-resin composite slurry
[0032] Add the resin to the solvent in proportion to dissolve. After uniformly dissolving, add stabilizer and graphene powder to the resin in proportion. The graphene powder should be pre-dispersed before adding. The specific treatment process is: another of the same category as the above Solvent and place the graphene powder in the solvent. The mass ratio of the graphene powder to the solvent is 1:250-300, and then ultrasonically disperse for 20-40 minutes. After the dispersion is completed, pass the vacuum with a filter cloth of more than 500 meshes. The solvent is removed by the suction filter to obtain wet graphene, and then the lubricating graphene is added to the resin, and then the stabilizer, graphene and resin are mixed uniformly by stirring. After the mixing is uniform, the dispersion process i...
Example Embodiment
[0040] Example 2
[0041] A preparation method of graphene modified anticorrosive coating includes the following steps:
[0042] (1) Preparation of graphene-resin composite slurry
[0043] The epoxy resin is added to the absolute ethanol in proportion, and the epoxy resin is uniformly dissolved by stirring to reduce the viscosity of the epoxy resin. The mass ratio of the epoxy resin to the absolute ethanol is 70:30, which is uniformly dissolved Then, first add polyvinylpyrrolidone to the epoxy resin in proportion and stir and mix uniformly. The mass ratio of epoxy resin to polyvinylpyrrolidone is 100:1, then add graphene powder in proportion and stir and mix uniformly. The mass ratio of the graphene powder is 98.8:1.2. After stirring and mixing uniformly, the shearing emulsification dispersion process is used for dispersion treatment for 0.5 h. After the treatment is completed, the graphene-resin composite slurry is obtained. Among them, the graphene powder should be pre-dispersed ...
Example Embodiment
[0052] Example 3
[0053] A preparation method of graphene modified anticorrosive coating includes the following steps:
[0054] (1) Preparation of graphene-resin composite slurry
[0055] The alkyd resin is added to xylene in proportion, and the alkyd resin is uniformly dissolved by stirring to reduce the viscosity of the alkyd resin. The mass ratio of alkyd resin to xylene is 65:35. After uniform dissolution, First add the silane coupling agent to the alkyd resin according to the proportion and stir and mix evenly. The mass ratio of the alkyd resin to the silane coupling agent is 100:1.5. Then add the graphene powder according to the proportion and stir and mix evenly. The mass ratio of graphene powder is 98:2. After stirring and mixing uniformly, a high-speed homogeneous stirring dispersion process is used for dispersion treatment for 1.5 hours. After the treatment is completed, a graphene-resin composite slurry is obtained. Among them, the graphene powder should be pre-disperse...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap