A technology of leather coatings and coatings, which is applied in the direction of fireproof coatings, leather surface treatment, antifouling/underwater coatings, etc. It can solve the problems of high surface energy, easy gaps at the interface, agglomeration, and poor dispersion, so as to improve water resistance, Good antibacterial properties, the effect of reducing water absorption

Inactive Publication Date: 2016-09-07
CHUZHOU VOCATIONAL & TECHN COLLEGE
View PDF2 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Nanomaterials have the characteristics of small size and high surface energy, so they are easy to agglomerate and have poor dispersion
In addition, in the preparation process of nanocomposite materials, the affinity between nanomaterials and polymer matrix with low surface energy is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] A flame-retardant and antibacterial leather coating, which is made up of the following raw materials in parts by weight:

[0025] Zinc borate hydrate 2, calcium linoleate soap 1, triterpene saponin 0.1, calcium naphthenate 0.7, polyvinylpyrrolidone 1.7, polyacrylamide 0.8, stannous chloride 1.6, triethanolamine 0.1, methyl methacrylate 190, Sodium lauryl sulfate 3, urotropine 0.1, ammonium persulfate 0.2, 20% formaldehyde solution 6, zinc acetate 16, silver nitrate 4, decabromodiphenyl ether 1, sodium lauryl sulfate 0.4.

[0026] A kind of preparation method of described flame-retardant antibacterial leather coating, comprises the following steps:

[0027] (1) Mix the above-mentioned zinc acetate and urotropine, add it to deionized water 60 times the weight of the mixture, and stir evenly to form liquid a;

[0028] (2) Take the above-mentioned sodium lauryl sulfate, add it to deionized water 17 times its weight, stir evenly, add zinc borate hydrate, raise the temperatu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-flaming antisepsis leather coating which is composed of, by weight, 2-3 parts of hydrous zinc borate, 1-1.5 parts of linoleic acid calcium soap, 0.1-0.2 part of triterpenoid saponin, 0.7-1 part of calcium naphthenate, 1.7-2 parts of polyvinylpyrrolidone, 0.8-1 part of polyacrylamide, 1.6-2 parts of stannous chloride, 0.1-0.13 part of triethanolamine, 190-200 parts of methyl methacrylate, 3-4 parts of lauryl sodium sulfate, 0.1-0.2 part of urotropine, 0.2-0.3 part of ammonium persulfate, 6-7 parts of a 20%-25% formaldehyde solution, 16-20 parts of zinc acetate, 4-7 parts of silver nitrate, 1-2 part of decabromodiphenyl ether and 0.4-1 part of sodium lauryl sulfate. The anti-flaming antisepsis leather coating has a good antibacterial property and excellent moisture permeability and water resistance. Leather coated with the obtained emulsion is good in antibacterial property and excellent in hygiene property.

Description

technical field [0001] The invention relates to the technical field of leather coatings, in particular to a flame-retardant and antibacterial leather coating and a preparation method thereof. Background technique [0002] Leather finishing agent / textile coating agent is a polymer compound that is evenly coated on the leather / textile surface. It forms one or more layers of film on the leather / fabric surface by adhesion. Therefore, the quality of the coating material not only directly affects the appearance and quality of the product, but also determines the performance of the product to a large extent. Polyacrylate emulsion has the characteristics of flexibility and elasticity in film formation, and the coating has the characteristics of light resistance, aging resistance, and excellent wet rub resistance. It is a kind of leather textile coating material widely used at present. However, due to the existence of some polar groups in traditional polyacrylate emulsions, and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/12C09D5/14C09D5/18C08F20/14C14C11/00
CPCC08F20/14C08K2201/011C08L2201/02C09D5/14C09D5/18C09D133/12C14C11/003C08L33/26C08K13/06C08K9/12C08K2003/0806C08K9/04C08K2003/2296C08K2003/387C08K5/06
Inventor 周玲玲肖陆飞梁建军曹秦
Owner CHUZHOU VOCATIONAL & TECHN COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap