Chemical waste gas adsorbent and preparation method thereof

An adsorbent and waste gas technology, applied in chemical instruments and methods, gas treatment, other chemical processes, etc., can solve the problems of poor treatment effect and achieve the effect of sufficient raw materials, large specific surface area and light specific gravity

Inactive Publication Date: 2016-10-12
ANQING FENGYUAN CHEM
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the treatment effect of solid particle adsorbents for domestic waste gas treatment is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A chemical waste gas adsorbent, made of the following raw materials in parts by weight: 30 parts of calcium carbonate fiber, 20 parts of tetrabutyl titanate, 10 parts of fruit shell activated carbon, 7 parts of alginic acid, 7 parts of pyrite slag, and 10 parts of bamboo charcoal powder 3 parts of silica sol, 20 parts of volcanic rock, 5 parts of nano-carbon dioxide, 3.5 parts of cellulose ether, 1 part of methyltriethoxysilane, 9 parts of hemp pulp, and appropriate amount of water.

[0015] The preparation method of the chemical waste gas adsorbent comprises the following preparation steps:

[0016] (1) Pulverize the calcium carbonate fiber through a 120-mesh sieve, add nano-titanium dioxide and methyltriethoxysilane, stir and grind for 1 hour, and dry at 150° C. to obtain modified nano-titanium dioxide;

[0017] (2) Take the volcanic rock and heat it at 600°C for 4 hours, cool and grind it into powder, put it into a high mixer, add modified nano-titanium dioxide, mix ...

Embodiment 2

[0020] A chemical waste gas adsorbent, made of the following raw materials in parts by weight: 32 parts of calcium carbonate fiber, 22 parts of tetrabutyl titanate, 6 parts of fruit shell activated carbon, 8 parts of seaweed, 8 parts of pyrite slag, and 12 parts of bamboo charcoal powder , 4 parts of silica sol, 25 parts of volcanic rock, 6 parts of nano-carbon dioxide, 2.6 parts of cellulose ether, 2 parts of methyltriethoxysilane, 10 parts of hemp pulp, and appropriate amount of water.

[0021] The preparation method of the chemical waste gas adsorbent comprises the following preparation steps:

[0022] (1) Pulverize the calcium carbonate fiber through a 150-mesh sieve, add nano-titanium dioxide and methyltriethoxysilane, stir and grind for 2 hours, and dry at 160° C. to obtain modified nano-titanium dioxide;

[0023] (2) Take the volcanic rock and calcine it at 650°C for 3 hours, cool and grind it into powder, put it into a high mixer, add modified nano-titanium dioxide, an...

Embodiment 3

[0026] A chemical waste gas adsorbent, made of the following raw materials in parts by weight: 35 parts of calcium carbonate fiber, 25 parts of tetrabutyl titanate, 10 parts of fruit shell activated carbon, 10 parts of alginic acid, 9 parts of pyrite slag, and 15 parts of bamboo charcoal powder 5 parts of silica sol, 30 parts of volcanic rock, 7 parts of nano-carbon dioxide, 3.5 parts of cellulose ether, 3 parts of methyltriethoxysilane, 12 parts of hemp pulp, and appropriate amount of water.

[0027] The preparation method of the chemical waste gas adsorbent comprises the following preparation steps:

[0028] (1) Pulverize the calcium carbonate fiber through a 180-mesh sieve, add nano-titanium dioxide and methyltriethoxysilane, stir and grind for 2 hours, and dry at 180° C. to obtain modified nano-titanium dioxide;

[0029] (2) Take the volcanic rock and calcine it at 700°C for 2 hours, cool and grind it into powder, put it into a high mixer, add modified nano-titanium dioxid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a chemical waste gas adsorbent and a preparation method thereof. The adsorbent is prepared from, by weight, 30-35 parts of calcium carbonate fiber, 20-25 parts of tetrabutyl titanate, 5-10 parts of shell activated carbon, 7-10 parts of alginic acid, 7-9 parts of pyrite cinder, 10-15 parts of bamboo charcoal powder, 3-5 parts of silica sol, 20-30 parts of volcanic rock, 5-7 parts of nano carbon dioxide, 2.1-3.5 parts of cellulose ether, 1-3 parts of methyl triethoxysilane, 9-12 parts of jute pulp and a proper amount of water. The chemical waste gas adsorbent is high in adsorption and can efficiently remove main pollutants such as volatile organic substances, inorganic matter, hydrogen sulfide, ammonia and mercaptan and various odors, the deodorizing efficiency can reach 98% or above, and the antibacterial and air purifying effects are achieved.

Description

technical field [0001] The invention relates to the technical field of chemical waste gas treatment, in particular to a chemical waste gas adsorbent and a preparation method thereof. Background technique [0002] Chemical waste gas refers to the poisonous and harmful gas discharged from chemical plants in chemical production. Chemical waste gas often contains many types of pollutants, complex physical and chemical properties, and different toxicity, which seriously pollutes the environment and affects human health. The composition of chemical waste gas produced by different chemical production industries varies greatly. For example, the waste gas produced by the chlor-alkali industry mainly contains chlorine, hydrogen chloride, vinyl chloride, mercury, acetylene, etc., and the waste gas produced by the nitrogen fertilizer industry mainly contains nitrogen oxides, urea dust, carbon monoxide, ammonia, sulfur dioxide, methane, etc. At present, the treatment effect of solid pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/24B01J20/30B01D53/02
CPCB01J20/24B01D53/02B01D2257/304B01D2257/306B01D2257/406B01D2257/708B01J20/0285B01J20/043B01J20/103B01J20/12B01J20/20B01J20/22
Inventor 黄帆
Owner ANQING FENGYUAN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap