Preparation method of modified phenolic resin base activated carbon and supercapacitor

A technology of phenolic resin and resole phenolic resin, which is applied in the preparation method of graphene-modified phenolic resin-based activated carbon and the field of supercapacitors, can solve the problems of low mesoporosity, small specific surface area, and low conductivity, and achieve high porosity rate, high conductivity, and the effect of reducing internal resistance

Active Publication Date: 2016-11-09
SHANDONG OBO NEW MATERIAL CO LTD
View PDF3 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In the existing literature, the use of phenolic resin to prepare porous activated carbon (phenolic resin-based activated carbon) has been reported, but there are still problems such as small specific surface area, low mesoporosity and low conductivity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of modified phenolic resin base activated carbon and supercapacitor
  • Preparation method of modified phenolic resin base activated carbon and supercapacitor
  • Preparation method of modified phenolic resin base activated carbon and supercapacitor

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The invention provides a kind of preparation method of modified phenolic resin-based activated carbon, comprising the following steps:

[0043] A) after the resole phenolic resin is mixed with the graphene oxide solution, a mixture is obtained;

[0044] B) after foaming the mixture obtained by the above steps, curing accelerator, blowing agent and surfactant, a composite phenolic resin foam is obtained;

[0045] C) under the condition of inert gas and / or nitrogen, after the composite phenolic resin foam that above-mentioned step is obtained is carbonized, obtain carbonized material;

[0046] D) After the carbonized material obtained in the above steps is mixed with alkali, after activation under the conditions of inert gas and / or nitrogen, the primary product of activated carbon is obtained;

[0047]E) The activated carbon primary product obtained in the above steps is subjected to heat treatment under the protection of a reducing gas to obtain a modified phenolic resi...

Embodiment 1

[0073] Get 100g the resole phenolic resin (F / P=1.3) that is prepared by phenol and paraformaldehyde, add the ethanol solution 100mL (graphene oxide monolayer ratio >95%) that contains 2g fully exfoliated graphene oxide wherein, Stir at high speed under ultrasonic to disperse for 60min. Then the obtained solution was distilled off under reduced pressure to remove the ethanol solvent to obtain a resole phenolic resin in which graphene oxide was fully dispersed.

[0074] Then add 0.5g of surfactant Tween-80, 10mL of foaming agent petroleum ether, 0.5mL of curing accelerator mixed acid solution (p-toluenesulfonic acid:phosphoric acid=2:1), and foam at 70°C for 45min to obtain Phenolic foam.

[0075] Then put the phenolic foam into a muffle furnace protected by inert gas, and carbonize at 800°C for 2 hours to obtain a pre-carbonized product. Grind the pre-carbonized product into 50-100μm particles, add 100g of potassium hydroxide powder and mix well, add it into a pure nickel cru...

Embodiment 2

[0082] Get 100g of resole phenolic resin (F / P=1.5) prepared by resorcinol and formaldehyde aqueous solution, add the ethanol solution 100mL (graphene oxide monolayer ratio >95% that contains 1g fully exfoliated graphene oxide) wherein ), high-speed stirring and dispersing under ultrasonic for 60min. Then the obtained solution was distilled off under reduced pressure to remove the ethanol solvent to obtain a resole phenolic resin in which graphene oxide was fully dispersed.

[0083] Then add 1 g of surfactant polyoxypropylene ether, 10 mL of blowing agent n-pentane, and 1 g of curing agent oxalic acid, and foam at 80° C. for 60 minutes to obtain phenolic foam.

[0084] Then add the phenolic foam into a muffle furnace protected by inert gas, and carbonize it at 800°C for 2 hours to obtain a carbonized product; grind the pre-carbonized product into particles of 50-100 μm, add 200g of potassium hydroxide powder and mix well, add Place in a pure nickel crucible in a tube furnace, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
electrical resistivityaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of modified phenolic resin base activated carbon. Oxidized graphene is added into phenolic resin to be uniformly dispersed, and the oxidized graphene is reduced into graphene in the follow-up activation and reduction treatment process, so that the activated carbon has the high conductivity, and a carbon material internal resistor is lowered; due to the phenolic resin foaming technology, the carbon material has the high porosity and can be easily mixed with base to be uniform, the application amount of the base is effectively lowered, and meanwhile the obtained activated carbon has the superhigh specific surface area; the phenolic resin is attached to an oxidized graphene sheet layer in the foaming curing process, generation of a mesoporous is promoted due to obstruction of oxidized graphene, and therefore the rate of the mesoporous of activated carbon is increased; the preparation method is simple, mild and suitable for large-scale industrial production.

Description

technical field [0001] The invention belongs to the technical field of resin materials, and relates to a preparation method of modified phenolic resin-based activated carbon and a supercapacitor, in particular to a preparation method of graphene-modified phenolic resin-based activated carbon and a supercapacitor. Background technique [0002] Phenolic resin is a polymer produced by polycondensation reaction of phenolic compounds and aldehyde compounds under the catalysis of acid or alkali catalysts. The most common one is the resin obtained by condensation of phenol or its homologues (such as cresol, xylenol, etc.) and formaldehyde. According to the type and ratio of raw materials used and the type of catalyst, it can be divided into two types of thermoplastic and thermosetting resins. Thermoplastic phenolic resin is a linear resin that only melts when heated, but cannot become insoluble or infusible. However, it can be transformed into thermosetting after adding a curing a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B31/12H01G11/44H01G11/24
CPCY02E60/13H01G11/44C01P2004/01C01P2006/12C01P2006/17C01P2006/40H01G11/24
Inventor 程金杰张在忠姜彤彤胡兴华
Owner SHANDONG OBO NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap