High-temperature resistant water-borne flashing coating used for photo frames

A high-temperature-resistant, water-based technology, applied in fire-resistant coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems such as the unsatisfactory high-temperature resistance of metallic flash coatings

Inactive Publication Date: 2016-11-09
蚌埠市禹会区贵宾装饰材料商行
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Then the high temperature resistance of the metal flash coating in the prior art cannot meet the needs of actual use, so it is urgent to design a metal flash coating with excellent high temperature resistance to meet the needs of actual use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A high-temperature-resistant water-based glitter coating for photo frames proposed by the present invention, its raw materials include by weight: 50 parts of water-based resin, 15 parts of hydroxyl-containing polyacrylate emulsion, 6 parts of cellulose acetate butyrate solution, low methyl etherification amino resin 2.5 parts, 3.5 parts of iron oxide red, 4.5 parts of iron oxide yellow, 5 parts of pearl powder, 3.5 parts of dodecyl mercaptan, 6 parts of dimethylethanolamine, 2.5 parts of triethylamine, 4 parts of triethanolamine, 2-amino -5.5 parts of 2-methyl propanol, 3.5 parts of ammonia water, 2.5 parts of glycidyl acrylic acid ether, 3.5 parts of ethylene glycol monobutyl ether, 4.5 parts of water-based aluminum powder, 2.5 parts of charcoal powder, 3.5 parts of talcum powder, 6 parts of sodium bicarbonate 3.5 parts of glass fiber, 3.5 parts of vermiculite powder, 6 parts of perlite powder, 4 parts of EVA wax, 4-8 parts of polyethylene wax, 2-5 parts of nano-titaniu...

Embodiment 2

[0021]A high-temperature-resistant water-based glitter coating for photo frames proposed by the present invention, its raw materials include by weight: 45 parts of water-based resin, 20 parts of hydroxyl-containing polyacrylate emulsion, 3 parts of cellulose acetate butyrate solution, 4 parts of butylated amino resin 2 parts, 2 parts of iron oxide red, 6 parts of iron oxide yellow, 4 parts of pearl powder, 5 parts of dodecyl mercaptan, 3 parts of dimethylethanolamine, 4 parts of triethylamine, 2 parts of triethanolamine, 2-amino- 8 parts of 2-methyl propanol, 2 parts of ammonia water, 4 parts of glycidyl acrylic acid ether, 2 parts of ethylene glycol monobutyl ether, 6 parts of water-based aluminum powder, 1 part of charcoal powder, 5 parts of talcum powder, 3 parts of sodium bicarbonate , 4 parts of glass fiber, 2 parts of vermiculite powder, 8 parts of perlite powder, 2 parts of EVA wax, 8 parts of polyethylene wax, 2 parts of nano-titanium dioxide, 4 parts of water-based pol...

Embodiment 3

[0024] A high-temperature-resistant water-based glitter coating for photo frames proposed by the present invention, its raw materials include by weight: 55 parts of water-based resin, 10 parts of hydroxyl-containing polyacrylate emulsion, 9 parts of cellulose acetate butyrate solution, completely methylated amino resin 1 part, 5 parts of iron oxide red, 3 parts of iron oxide yellow, 6 parts of pearl powder, 2 parts of dodecyl mercaptan, 9 parts of dimethylethanolamine, 1 part of triethylamine, 6 parts of triethanolamine, 2-amino - 3 parts of 2-methyl propanol, 5 parts of ammonia water, 1 part of glycidyl acrylic acid ether, 5 parts of ethylene glycol monobutyl ether, 3 parts of water-based aluminum powder, 4 parts of charcoal powder, 2 parts of talcum powder, 9 parts of sodium bicarbonate 1 part of glass fiber, 5 parts of vermiculite powder, 4 parts of perlite powder, 6 parts of EVA wax, 4 parts of polyethylene wax, 5 parts of nano titanium dioxide, 1 part of water-based polyis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

High-temperature resistant water-borne flashing coating used for photo frames is disclosed. Raw materials of the coating include water-borne resin, hydroxy-containing polyacrylate emulsion, a cellulose acetate butyrate solution, amino resin, iron oxide red, iron oxide yellow, pearl powder, lauryl mercaptan, dimethyl ethanolamine, triethylamine, triethanolamine, 2-amino-2-methyl-1-propanol, ammoniacal liquor, glycidyl acrylate, 2-butoxyethanol, aqueous aluminium powder, charcoal powder, talcum powder, sodium bicarbonate, glass fibers, vermiculite powder, perlite powder, EVA wax, polyethylene wax, nanometer titanium dioxide, a water-borne polyisocyanate curing agent, a wetting agent, a dispersant, a defoaming agent, a levelling agent and an anti-settling agent BYK-420. The flashing coating has excellent resistance to high temperatures.

Description

technical field [0001] The invention relates to the field of flash paint, in particular to a high-temperature-resistant water-based flash paint for photo frames. Background technique [0002] At present, the scaly aluminum powder in the metallic flash paint forms a multi-layer parallel arrangement in the coating film, which can effectively reflect ultraviolet rays, infrared rays and visible light, delay its aging damage to the coating film, and can also effectively prevent water, air, etc. And the penetration of ions, because of its unique decorative and anti-corrosion effects, it is more and more used in the surface coating of photo frames. [0003] However, the high temperature resistance of the metal glitter coatings in the prior art cannot meet the requirements of actual use, so there is an urgent need to design a metal glitter coating with excellent high temperature resistance to meet the needs of actual use. Contents of the invention [0004] In order to solve the t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D133/00C09D175/04C09D175/14C09D133/14C09D7/12
CPCC09D143/04C08L2201/08C08L2205/02C08L2205/035C09D5/18C09D7/61C09D7/63C09D7/70C08L33/00C08L75/04C08L75/14C08L33/14C08L1/14C08L61/32C08K13/04C08K2003/2272C08K5/37C08K5/17C08K3/34C08K7/14
Inventor 刘贵斌刘阳
Owner 蚌埠市禹会区贵宾装饰材料商行
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com