Heat insulation waterproof paint of butadiene styrene rubber modified by nanometer SiO2 and preparation method thereof

A technology of styrene-butadiene rubber and waterproof coating, applied in the field of coatings, can solve the problems of low wall bonding strength and decorative properties, limit the use range of coatings, and be unsuitable for waterproof coatings, etc., achieve good application prospects, low cost, and improve heat insulation performance effect

Inactive Publication Date: 2016-11-16
ANHUI LENCAQI BUILDING MATERIAL
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Now this kind of coating is undergoing a transformation from industrial heat insulation to building heat insulation. Low and decorative properties need to be further improved, etc., which limit the scope of application of this type of coating
[0004] Patent No. 201510887384.8 discloses a waterproof rubber material, which is prepared from the following raw materials in parts by weight: polyethylene terephthalate 7-8, trioctyl citrate 3-4, rosin 1-2, polypropylene Nitrile 24-27, sodium diacetate 1-2, graphite 12-13, fly ash microbeads 3-4, sod

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The nano-SiO of this embodiment 2 Modified styrene-butadiene rubber heat-insulating waterproof coating, which is prepared from the following raw materials in parts by weight: 100 parts of styrene-butadiene rubber emulsion, 8 parts of neoprene rubber emulsion, 20 parts of hydroxyethyl methacrylate, alkyl m-benzene 10 parts of diphenol formaldehyde resin, 2 parts of hexamethoxymethyl melamine, 3 parts of titanium dioxide, 3 parts of talcum powder, 2 parts of sodium tripolyphosphate, 2 parts of tributyl phosphate, 2 parts of alcohol ester twelve, 1,2 - 0.5 parts of benzisothiazolin-3-one, 2 parts of hydroxymethyl cellulose, 8 parts of hollow glass microspheres, 4 parts of 25% ammonia water, 40 parts of absolute ethanol, 4 parts of tetraethyl orthosilicate, hydroxyl 8 parts of silicone oil, 2 parts of white carbon black, 0.5 part of dibutyltin dilaurate, appropriate amount of deionized water.

[0018] The nano-SiO of this embodiment 2 The heat-insulating waterproof coatin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to heat insulation waterproof paint of butadiene styrene rubber modified by nanometer SiO2. The paint is prepared from the following raw materials in parts by weight: 100 parts of butadiene styrene rubber emulsion, 8 to 10 parts of chloroprene rubber emulsion, 15 to 20 parts of hydroxyethyl methylacrylate, 8 to 10 parts of alkyl resorcinol formaldehyde resin, 1 to 2 parts of hexakis methoxymethyl melamine, 3 to 5 parts of titanium dioxide, 3 to 5 parts of talcum powder, 1 to 2 parts of sodium tripolyphosphate, 2 to 3 parts of tributyl phosphate, 1 to 2 parts of texanol, 0.5 to 1 part of 1,2-benzoisothiazolinone-3-ketone, 1 to 2 parts of hydroxymethyl cellulose, 8 to 10 parts of hollow glass micro beads, 3 to 4 parts of 25-percent ammonium hydroxide, 40 to 50 parts of absolute ethyl alcohol, 3 to 5 parts of ethyl orthosilicate, 5 to 8 parts of hydroxyl silicone oil, 1 to 2 parts of white carbon black, 0.5 to 1 part of dibutyltin dilaurate and a proper amount of deionized water. The paint has the advantages that the manufacturing price is low; good heat insulation effects and lighting degrees are realized; the construction is simple and convenient; the application prospects are good.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a nano-SiO 2 A modified styrene-butadiene rubber heat-insulating waterproof coating and a preparation method thereof. technical background [0002] Due to the sunlight, the temperature inside the building rises, which will increase the energy consumption of the air conditioner. In addition, industrial plants, prefabricated houses or temporary buildings mostly use metal steel plate roofs. In the sun, the indoor temperature will rise rapidly. In many cases, the effect of using air conditioning to cool down the indoor temperature is not good. Lowering indoor temperatures by lowering the roof surface temperature is usually the most practical way. The way to prevent the indoor temperature from rising is to make the outdoor heat (mainly the heat generated by sunlight) pass into the room as little as possible, and the indoor heat be dissipated as much as possible. [0003] The therm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D109/08C09D115/02C09D161/12C09D101/28C09D7/12C08C19/28
CPCC08C19/28C08L2205/035C09D7/61C09D7/62C09D7/63C09D7/65C09D109/08C08L15/02C08L61/12C08L1/284C08K13/06C08K9/04C08K9/02C08K7/28C08K2003/2241C08K3/34C08K3/36
Inventor 乔启信金自海
Owner ANHUI LENCAQI BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products