Titanate alloy steel anticorrosive coating and preparation method thereof

An anti-corrosion coating, alloy steel technology, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problem of poor dispersion, reduce the anti-corrosion performance of polyaniline, and the physical anti-penetration ability of polyaniline cannot meet the requirements of harsh use conditions, etc. problems, to achieve the effect of improving solubility, improving the ability to passivate metals, and enhancing the ability to inhibit anodic reactions

Inactive Publication Date: 2016-11-23
TIANCHANG YINHU PAINT
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The poor dispersion and poor adhesion of polyaniline in polyaniline / resin coatings also greatly reduce the anti-corrosion performance of polyaniline. At the same time, the physical anti-penetration ability of polyaniline is far from meeting the requirements of harsh service conditions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] A kind of titanate alloy steel anticorrosion paint, it is made up of the raw material of following weight part;

[0023] Tetrabutyl titanate 4, polysorbate 800.8, aniline 50, pyrrole 30, sulfosalicylic acid 7, epoxy resin E513, ammonium persulfate 1.3, molybdic acid 4, polyamide resin 3, n-butanol 160, ethyl alcohol Glycol butyl ether 20, polyethylene adipate glycol 3, ammonium zirconium carbonate 0.7, tin methyl mercaptide 1, kt101 titanate coupling agent 0.6, glyceryl caprylate 0.2, aluminum tripolyphosphate 1.6.

[0024] A preparation method of the described titanate alloy steel anticorrosion coating comprises the following steps:

[0025] (1) Add ammonium persulfate to 21 times its weight in deionized water, and stir evenly to obtain an initiator solution;

[0026] (2) Add the above-mentioned tetrabutyl titanate to deionized water 20 times its weight, stir evenly, add ammonium zirconium carbonate, add 90% hydrochloric acid dropwise, adjust the pH to 2, raise the te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Impact strengthaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a titanate alloy steel anticorrosive coating. The titanate alloy steel anticorrosive coating consists of the following raw materials in parts by weight: tetrabutyl titanate 4-6 parts, polysorbate 80 0.8-1 part, aniline 50-60 parts, pyrroles 30-40 parts, sulfosalicylic acid 7-9 parts, epoxy resin E51 3-4 parts, ammonium persulfate 1.3-2 parts, molybdic acid 4-6 parts, polyamide resin 3-5 parts, n-butyl alcohol 160-170 parts, butyl glycol ether 20-30 parts, polyadipate ethylene glycol 3-5 parts, zirconium ammonium carbonate 0.7-1 part, methyl stannum mercaptide 1-2 parts, kt101 titanate coupling agent 0.6-1 part, octyl and decyl glycerate 0.2-0.4 part, and aluminium triphosphate 1.6-2 parts. The titanate alloy steel anticorrosive coating is modified by the titanate coupling agent, and therefore, the surface hydrophobicity and the weather fastness of the finished coating are improved effectively.

Description

technical field [0001] The invention relates to the technical field of anti-corrosion coatings, in particular to a titanate alloy steel anti-corrosion coating and a preparation method thereof. Background technique [0002] In recent years, polyaniline, as a new type of conductive polymer material, has attracted more and more attention. Its synthesis process is simple, no pollution to the environment, low cost, and has stable thermodynamic and chemical properties, so that it has a wide range of applications in various fields. In particular, its excellent anti-corrosion performance makes it widely used in the field of anti-corrosion. However, its weak adhesion and poor solubility of the paint film have greatly restricted its application. If the excellent chemical corrosion resistance of polyaniline is combined with the excellent adhesion and mechanical properties of epoxy resin to prepare blended coatings, this will greatly improve the anti-corrosion ability of epoxy resin c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D179/02C09D179/04C09D163/00C09D5/08C09D7/12C08G73/02C08G73/06
CPCC08G73/0266C08G73/0611C08L2205/02C08L2205/035C09D5/08C09D7/63C09D7/67C09D179/02C08L79/04C08L63/00C08K13/02C08K5/42C08K3/24C08K5/10
Inventor 祝盆鑫祝秀凤汪鹏程孙巨福戴宇钧
Owner TIANCHANG YINHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products